• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 춘계학술발표대회
• /
• pp.33.2-33.2
• /
• 2009

Dielectric and piezoelectric properties of Lead-free $(1-x)(Bi_{0.5}K_{0.5})TiO_3-xBiFeO_3$ceramics prepared by a conventional solid state reaction method were investigated in the range of x = 0~10 mol%. Piezoelectric coefficient was increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% then decreased with increasing x. Electromechanical coupling factor ($K_p$) was increased up to 0.18 at x = 10 mol%. On the other hand, mechanical quality factor ($Q_m$) was decreased. Grain size was not much changed with various x and a single perovskite with tetragonal symmetry was maintained at all compositions forming a solid solution between $(Bi_{0.5}K_{0.5})TiO_3$ and $BiFeO_3$. Depolarization temperature ($T_d$) was gradually decreased with increasing x from $302^{\circ}C$ at x = 0 to $245^{\circ}C$ at x = 10 mol%.

• 한국결정성장학회지
• /
• 제9권5호
• /
• pp.510-515
• /
• 1999

일정농도의 $TiO_2$ 수용액과 일정농도의 KOH 수용액을 반응시켜 $TiO_2$의 가수분해에 의한 Titanium Oxide의 생성 및 생성물의 열처리 조건에 따른 거동을 연구하였다. 열처리 조건은 300~1000$1000^{\circ}C$에서 각각 1시간으로 하였고 각 조건에서 얻어진 생성물의 분석은 XRD, DTA 및 FT-IR에 의하여 연구 검토되었으며 그 결과 다음과 같은 결론을 얻을 수 있었다. \circled1 $90^{\circ}C$의 온도조건에서 초기 가수분해 반응 생성물은 Anatase형 TiO2의 주 peak가 회절각도의 폭이 넓고 강도가 약하게 나타나 준결정질 물질임을 나타내고 있다. \circled2 결정질이 좋지 못한 준정질 산화티탄은 $300^{\circ}C$까지는 Anatase 결정성이 온도와 더불어 좋아지며 $700^{\circ}C$에서 rutile형 TiO2로 상전이 한다. \circled3 alkali pH 영역에서 생성된 K-O-Ti 결합을 형성한 비 결정성 물질은 potasium titanate계의 물질로써 결정화 온도는 630~$640^{\circ}C$ 부근이다. \circled4 비 결정성 K-O-Ti 결합이 공존하는 준결정성 산화티탄은 K-O-Ti 결합물질의 함량이 증가됨에 따라 Anatase로의 결정화 온도가 $300^{\circ}C$에서 50$0^{\circ}C$로 높아지며 또한 rutile형 $TiO_2$로의 상이전도 $700^{\circ}C$에서 $900^{\circ}C$로 높아진다. \circled5 $TiO_4$와 KOH를 사용한 습식법에 의한 Anatase형 $TiO_2$합성조건은 pH 3~pH 5가 가장 바람직하며 열처리 온도는 $300^{\circ}C$에서 가능하다.

• 한국결정성장학회지
• /
• 제5권3호
• /
• pp.261-268
• /
• 1995

소성서냉법으로$K_2Ti_4O_9$ 중간상 휘스커를 제조한 다음, 비등수 및 산처리에 의하여$K_2Ti_6O_{13}$ 휘스커로 상전이 시키는데 있어서, 비등수 및 산처리 시간과 농도가 상전이 및 휘스커의 표면과 해섬(scattering a bundle of whisker)에 미치는 영향을 알아보았다. 그 결과 휘스커의 표면상태가 개선되었으며, 아울러 휘스커 간에 해섬을 유도하여 직경이 작으면서도 aspect ratio가 큰 양질의 휘스커를 얻을 수 있었다. 비등수 및 산처리는 휘스커의$K_2Ti_4O_9 {\leftrightarro} K_2Ti_6O_{13}$상전이를 유도하였는데 이러한 상전이는 $K^+$ 이온의 용출에 의해 진행되었다.

• Environmental Engineering Research
• /
• 제23권3호
• /
• pp.330-338
• /
• 2018

This study investigated the possibility of using potassium titanate oxide ($K_2Ti_4O_9$) and acrylic acid-grafted polypropylene fabric (PP-g-AA) as adsorbents capable of removing strontium from aqueous solutions. $K_2Ti_4O_9$ showed the highest rate of strontium removal in the weak alkaline range, while the PP-g-AA increased strontium removal in the neutral range. Moreover, the adsorption capacity of the $K_2Ti_4O_9$ was not affected by the coexistence of K and Na ions, while the adsorption capacity decreased when Ca and Mg ions were present at the same concentration as that of strontium. When coexisted at the same concentration as strontium, Na, K, Ca, and Mg ions strongly reduced the adsorption capacity of the PP-g-AA. The results also indicated that the adsorption of strontium on $K_2Ti_4O_9$ was consistent with both the Langmuir and Freundlich adsorption isotherms. In contrast, the adsorption of strontium on the PP-g-AA was more consistent with the Langmuir isotherm model. Moreover, the adsorption equilibrium time of $K_2Ti_4O_9$ was generally 12 h, while that of the PP-g-AA was 5 h, indicating that the adsorption rates were consistent with the pseudo-second order kinetics model. $K_2Ti_4O_9$ and the PP-g-AA could be regenerated by simple washing with 0.5 N HCl.