• Fibers and Polymers
• /
• v.1 no.2
• /
• pp.92-96
• /
• 2000

A high molecular weight polyhydroxyamide (PHA) solution in N, N-dimethyl acetamide (DMAc) was prepared from 3, 3'-dihydroxybenzidine and isophthalic chloride (IPC), which was used for spinning PHA fiber. Before spinning, the diffusion property of DMAc into various coagulants was examined. The fiber was well formed in coagulants such as water/ethanol with a composition of 5/5, ethanol, and ethanol/isopropanol with a composition of 7/3 and 5/5. However, the PHA fiber spun in the water/ethanol mixture contained voids. After the fiber spun in ethanol was annealed at over $350^{\circ}C$, the ultimate stress and initial modulus of the fiber increased from 75.5 MPa and 3.22 GPa to 369 MPa and 29.5 GPa, respectively. These properties of the PHA fiber spun by the dry spinning method were also enhanced, attaining 154 MPa and 5.56 Gpa, respectivel.

• Proceedings of the Korean Fiber Society Conference
• /
• 2001.10a
• /
• pp.359-360
• /
• 2001

헤테로고리 방향족 polybenzoxazole(PBO)은 대표적인 내열성 고분자로서, 고온에서의 열적안정성 및 내화학성, 기계적 물성, 방염성 등에서 우수한 성질을 나타낸다. 그러나 황산과 같은 강산에만 용해되기 때문에 가공성 면에서 단점을 가지고 있어 사용하는데 있어 제약이 따른단 현재 이러한 단점을 보완하기 위해 polyhydroxyamide(PHA)와 같은 전구체 고분자에 대한 연구가 많은 연구자들에 의해 진행되고 있다. (중략)

• Elastomers and Composites
• /
• v.55 no.3
• /
• pp.205-214
• /
• 2020

A series of wholly aromatic polyhyroxyamide (PHA) copolymers were prepared by direct polycondensation reaction of isophthalic acid and diacids containing bulky units with 3,3'-dihydroxybenzidine. The inherent viscosities of the PHAs measured at 35℃ in DMAc solution were in the range of 0.31-0.56 dL/g. The solubility study revealed that the PHAs were readily soluble in aprotic solvents such as, dimethylacetamide (DMAc), dimethyl sulfoxide (DMSO), and N-methyl-2-pyrrolidone (NMP) at room temperature and in less polar solvent such as pyridine. However, the polybenzoxazole (PBO) copoymers were quite insoluble in all organic solvents except partially soluble in concentrated sulfuric acid and partially soluble in NMP containing LiCl. The PBO copolymers showed maximum weight loss temperature in the range of 593-632℃ and high char yields in the range of 65.0-71.2% at 900℃ in a nitrogen atmosphere.

• Elastomers and Composites
• /
• v.46 no.4
• /
• pp.295-303
• /
• 2011

A series of new aromatic polyhydroxyamides (PHAs) containing imide ring were prepared by direct polycondensation reaction of imide-diacids and two types of bis(o-aminophenol)s including 3,3'-dihydroxybenzidine and 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane. The polymers were characterized by FT-IR, FT-NMR, DSC and TGA. The inherent viscosities of the PHAs measured at $35^{\circ}C$ in DMAC solution were in the range of 0.49-1.13 dL/g. PHA 2 and 3, except PHA 1, were soluble in polar solvents such as DMAc, DMF and NMP. PHA 4, 5, and 6 containing 6F group showed a higher solubility in less polar solvents. But the polybenzoxazoles (PBOs,) were insoluble in a variety of solvents except partially soluble in sulfuric acid. The PBO 1, 2 and 3 showed maximum weight loss temperature in the range of $650-656^{\circ}C$ and relatively high char yields in the range of 57.4-61.9 % under a nitrogen atmosphere. These results suggested that the introduction of imide or diimide ring in the main chain was effective in improving the thermal stability of PHAs and PBOs.