• 한국염색가공학회지
• /
• 제25권1호
• /
• pp.37-46
• /
• 2013

This paper surveys the ESD characteristics of the PANI added PU/MWNT film according to the manufacturing conditions such as variation of the loading contents of PANI and the mixture ratio of 2 dispersion solutions. For this purpose, PANI added PU/MWNT ground films were made with IPA/MWNT 3wt% dispersion solution and PANI/DMF dispersion solutions(5, 10, 15, 20, 25, and 30wt% contents of the PANI) by the mixture ratio of dispersion solution(10/50, 20/40, 30/30, 40/20, and 50/10part) in the PU (972DF) 100g, which was treated with 500rpm for 30min in the stirrer with condition of the dry temperature $120^{\circ}C$ for 2min. Totally, 36 kinds of PANI added PU/MWNT film specimens were prepared. The physical properties of the PANI added PU/MWNT films such as electrical resistivity, absorbancy by UV-Vis spectrometer, and triboelectricity were measured and discussed with surface characteristics of the PANI added PU/MWNT films by SEM. The dispersion property of PANI to the DMF showed best dispersion at the 25% of PANI content. The surface electrical resistivity of the PANI added PU/MWNT films was decreased with increasing the weight content of PANI/DMF dispersion solution, and it showed the lowest value $10^6{\Omega}$ at the mixing condition of PANI/DMF 20part and MWNT/IPA 40part with 30% PANI. Furthermore, it was shown that the electrical and physical properties of the PANI added PU/MWNT film such as electrical resistivity, and triboelectricity were better than those of PU/MWNT film prepared with no PANI, which was result obtained in previous paper.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2011년도 제42회 하계학술대회
• /
• pp.1714-1715
• /
• 2011

In this work, highly conductive organic solvent-based polyaniline(PANI) was used as an anode in organic photovoltaic cells (OPV) based on poly - (3-hexylthiophene) and [6,6] - phenyl - C60 - butyricacid methyl ester (P3HT : PCBM). The transmittance of the used PANI film were 87.67% and 86.57% at 550nm, and its sheet resistance were 454 ${\Omega}/{\Box}$ and 298 ${\Omega}/{\Box}$. We fabricated ITO-free OPV cells using PANI as an anode, which exhibited an external power conversion efficiency of 2.28% with a result of Jsc of 6.922mA/cm2, Voc of 0.6093V, and FF of 54.10% under an illumination of air mass(AM) 1.5G (100mW/$cm^2$). We used ink-jet printing to deposit buffer layer and active layer on a glass substrate.

• Composites Research
• /
• 제24권6호
• /
• pp.1-6
• /
• 2011

본 연구에서는 탄소나노튜브를 물상에서 균일하게 분산시키기 위하여 물에 녹으면서 분자 내에서 자체 도핑이 가능한 새로운 종류의 그래프트 공중합체(PSSA-g-PANI, poly(styrenesulfonic acid-graft-aniline))를 합성하였고, 그 분산 능력을 실험해 보았다. PANI 고분자는 벤조이드와 퀴노이드 구조가 반복되어 존재하는 판상구조로 탄소나노튜브와 같은 탄소나노 소재의 벽에 강하게 결합할 수 있고, 따라서 짧은 시간의 sonication 처리 만으로 나노튜브를 분산시킬 수 있었고 그 분산 용액의 장시간 안정성은 다른 상용화된 분산제보다 뛰어났다. 또한 PSSA-g-PANI 그래프트 고분자/탄소나노튜브 복합 필름은 대략 1.5-2.5 S/cm의 전도도를 기록하였다.