• 한국막학회:학술대회논문집
• /
• 한국막학회 2002년도 춘계 총회 및 학술발표회
• /
• pp.106-109
• /
• 2002

No Abstract, See Full-text

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.164-165
• /
• 2006

Carbon nanotube(CNT)-reinforced poly(ethylene-co-ethyl acrylate)(EEA) nanocomposites were prepared by melt mixing with a Haake internal mixer. The CNT loading was vaned from 0 to 20 wt%. The changes m CNT dispersion and shape were investigated with FE-SEM observation with and without the Tensile strain of 40%. The CNT was protruded over the fracture surface upon Tensile strain, which is a very interesting behavior.

• 공업화학
• /
• 제19권2호
• /
• pp.161-167
• /
• 2008

다층카본나노튜브(MWCNT)가 강화된 폴리에틸렌에틸아크릴레이트(EEA) 나노복합체를 용융혼합법과 용액혼합법으로 제조하였다. 카본나노튜브의 형태 및 함량변화에 따른 기계적, 열적, 전기적 특성을 조사하였다. MWCNT의 함량이 증가함에 따라 인장강도, 모듈러스는 증가하였고, 파단신장률은 감소하였다. 할로우 형태의 MWCNT가 일반적인 MWCNT에 비해 우수한 인장강도 및 파단신장률을 나타내었다. MWCNT 함량이 증가함에 따라 약 $40^{\circ}C$의 열분해온도의 향상을 보였다. 전기적 특성은 용융혼합법의 경우가 가장 높은 전기저항 특성을 나타내었고, 용액혼합법의 경우 일반형 MWCNT가 할로우 MWCNT보다 낮은 체적저항을 보였다. MWCNT의 함량이 증가할수록 파단면 위로 돌출되는 CNT 수가 증가하였고, 인장변형을 가하면 표면 위로 돌출되는 CNT 수와 길이가 크게 증가하였다. 용융혼합된 시편이 용액혼합에 비해 돌출된 CNT의 수와 길이가 현격히 낮았다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.270-273
• /
• 2009

A comb-like copolymer consisting of a poly(vinylidene fluoride-co-chlorotrifluoro-ethylene) backbone and poly(hydroxy ethyl acrylate) side chains, i.e. P(VDF-co-CTFE)-g-PHEA, was synthesized through atom transfer radical polymerization (ATRP) using CTFE units as a macroinitiator. Successful synthesis and a microphase-separated structure of the copolymer were confirmed by proton nuclear magnetic resonance (1H-NMR), FT-IR spectroscopy, and transmission electron microscopy (TEM). This comb-like polymer was crosslinked with 4,5-imidazole dicarboxylic acid (IDA) via the esterification of the -OH groups of PHEA and the -COOH groups of IDA. Upon doping with phosphoric acid ($H_3PO_4$) to form imidazole-$H_3PO_4$ complexes, the proton conductivity of the membranes continuously increased with increasing $H_3PO_4$ content. A maximum proton conductivity of 0.015 S/cm was achieved at $120^{\circ}C$ under anhydrous conditions. In addition, these P(VDF-co-CTFE)-g-PHEA/IDA/$H_3PO_4$ membranes exhibited good mechanical properties (765 MPa of Young's modulus), and high thermal stability up to $250^{\circ}C$, as determined by a universal testing machine (UTM) and thermal gravimetric analysis (TGA), respectively.