• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2000.10a
• /
• pp.326-331
• /
• 2000

This paper describes the statistical analysis techniques for the surface roughness assessment of polished surfaces. In experiments, the polishing process of the sample surfaces which are manufactured by ball end mill is consist of two steps; the cusp removal process and the surface finishing process. For the cusp removal process, the criterion of cusp removal was established from the power spectrum analysis to assess the change of the cusp removal rate. For the finishing process, the surface was polished by the rotational CBN tool and vibration wood tool. And the surface quality of polished surface was assessed using the functional parameters based on the statistical values of surface profiles. Consequently, the surface finish performance of the polished surface using the vibration wood tool was improved.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.697-702
• /
• 1995

The rough growth surfaces of diamond films fabricated by the hot filament CVD were polished using thermomechanical polishing method. And then, its application to the optical windows was discussed through the measurement of transmittance in the range of infrared radiation and analysis of surfaces structure. The results were compaerd with those of the films polished with conventional mechanicla polishing. The transmittance of the mechanically polished film reached 57~66% over the whole range from 500 to 4000 cm-1. But the transmittance of the film polished with thermomechanical polishing method was reduced below 35%. This decrease in transmittance was due to both the graphitization of diamond on the polished surface and the growth of $\beta$-SiC at diamond/Si interface during polishing. The residual Fe in hte thermomechanically polished surface was confirmed by SIMS analysis. This Fe played the role of the graphitization of near surface region of the diamond film.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.6
• /
• pp.472-478
• /
• 2016

PURPOSE. The aim of this study was to analyze the shapes of lingual polished surfaces in lower complete dentures formed by polished surface impressions and to provide reference data for use when manufacturing edentulous trays and lower complete dentures. MATERIALS AND METHODS. Twenty-six patients with mandibular edentulism were studied. After lower wax dentures were fabricated, wax was removed from the lingual side of the wax denture and a lingual polished surface impression was obtained with tissue conditioner. The definitive denture was scanned with a three-dimensional scanner, and scanned images were obtained. At the cross-sections of the lingual frenum, lateral incisors, first premolars, first molars, and anterior border of the retromolar pads, three points were marked and eight measurements were taken. The Kruskal-Wallis test and a post hoc analysis with the Mann-Whitney test were performed. RESULTS. Each patient showed similar values for the same areas on the left and right sides without a statistically significant difference. The height of the contour of the lingual polished surface at the lingual frenum was halfway between the occlusal plane and lingual border, it moved gradually in a downward direction. The angle from the occlusal plane to the height of the contour of the lingual polished surface was increased as it progressed from the lingual frenum towards the retromolar pads. CONCLUSION. The shape of the mandibular lingual polished surface was convex at the lingual frenum, lateral incisors and gradually flattened towards the first molars and retromolar pads.

• Korean Journal of Materials Research
• /
• v.24 no.12
• /
• pp.682-688
• /
• 2014

Physical and chemical changes in a polished wafer and in $2.5{\mu}m$ & $4{\mu}m$ epitaxially grown Si layer wafers (Epilayer wafer) after surface treatment were investigated. We characterized the influence of surface treatment on wafer properties such as surface roughness and the chemical composition and bonds. After each surface treatment, the physical change of the wafer surface was evaluated by atomic force microscopy to confirm the surface morphology and roughness. In addition, chemical changes in the wafer surface were studied by X-ray photoemission spectroscopy measurement. Changes in the chemical composition were confirmed before and after the surface treatment. By combined analysis of the physical and chemical changes, we found that diluted hydrofluoric acid treatment is more effective than buffered oxide etching for $SiO_2$ removal in both polished and Epi-Layer wafers; however, the etch rate and the surface roughness in the given treatment are different among the polished $2.5{\mu}m$ and $4{\mu}m$ Epi-layer wafers in spite of the identical bulk structural properties of these wafers. This study therefore suggests that independent surface treatment optimization is required for each wafer type, $2.5{\mu}m$ and $4{\mu}m$, due to the meaningful differences in the initial surface chemical and physical properties.

• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.2
• /
• pp.363-372
• /
• 1996

A common site of fracture in maxillary complete denture is on the anteroposterior midline that coincides with the notch for relief of the labial frenum. Various approaches to reduce the incidence of this type of fracture have been suggested. The most widely used technique is the reinforcement of acrylic resin denture base with several solid metal forms. But few comparative studies on the efficacy of metal reinforcements have been reported. This study was conducted to compare reinforcing effects of commonly available metal reinforcements, which include wire, metal mesh embedded in the denture base and metal plate affixed to the impression surface of denture base by silicoating technique. This was load on the posterior. The strain gauges were oriented perpendicular to the anteroposterior midline of maxillary polished denture surface at one labial and the four palatal sites Non-renforced denture was used as control. The results were as follows : 1. In the non-reinforced denture group, only tensile strains on the palatal polished surface were observed. The tensile strains decreased in the order of incisive papilla, posterior denture border area, mid palatal area and rugae area. Compressive strain was observed on the labial polished surface. 2. As compared with the non-reinforced denture group, the metal plate or the metal mesh reinforced denture groups showed reduced palatal tensile strains,and the metal mesh reinforcement had a better reinforcing effect than the metal plate. But both reinforced denture groups showed no difference in the amount of compressive strain on the labial polished surface when compared to the non-reinforced denture group. 3. The metal wire positioned just above the labial notch decreased the compressive strain on the labial polished surface. But the presence of metal wires in the palatal polished surface caused increase in tensile strains in the area.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.2 s.95
• /
• pp.145-152
• /
• 1999

This paper presents the principle and experimental results of a non-contact surface roughness measurement by means of screen projected pattern of lase beam reflected from a polished surface. In the reflected laser beam pattern especially from a fine surface like ground or polished one, light intensity varies from the center fo the image to its boundary as the Gaussian distribution. The standard deviation of a light intensity distribution is assumed to be a good non-contact estimator for measuring the surface roughnes, because the light reflectivity is known to be well related with the surface roughness. This method doesn't need to discriminate between the specularly reflected light and the diffusely reflected one, whereas the scattered laser intensity method must do. Nor it needs to adjust the change of light intensity caused by environmental lights or specimen materials. Reflected laser beam pattern narrowly spreads out in the vertical direction to tiny scratches on the polished surface due to abrasives. The deeper the scratch the more the dispersion, which means the rougher surface. The standard deviation of the pattern is nearly in proportion to the surface roughness. Measurement errors by this method are shown to be below 10 percent compared with those obtained by a common contact method. The inclination of measuring unit from the normal axis causes the measurement errors up to 10 percent for an angle of 4 degree. Therefore the proposed method can be used as an on-the-machine quick roughness estimator within 10 percent measurement error.

• Proceedings of the Optical Society of Korea Conference
• /
• 1999.08a
• /
• pp.178-179
• /
• 1999

• Journal of Power System Engineering
• /
• v.12 no.3
• /
• pp.50-54
• /
• 2008

Various Sialon ceramics were fabricated by hot-pressing mixtures of $Si_3N_4$ with additive $Y_2O_3$ and $Al_2O_3$. The polished specimen of SiAlON $I{\sim}III$ went on increasing in strength by heat treatment, heat treated non-polished specimen were similar or up to polished specimen in strength. The polished specimen of both SiAlON IV and V showed a very high strength, but were not Increasing of strength by heat treatment. All specimens were fractured on the surface and at the inner flaws. Surface fractures were initiated from the polished surface flaw and corner flaw. Inner fractures were initiated from an internal defect.

• Restorative Dentistry and Endodontics
• /
• v.5 no.1
• /
• pp.13-18
• /
• 1979

The purpose of this study was to measure the roughness on the acid -etching surface. The etching agents of three-kinds composite resins were used to etch the tooth surface. Newly extracted I5-anterior teeth were invested with self-curing acrylic resin, and the labial surface was exposed. The exposed labial side was polished with abrasive papers and finally polished on polishing machine with zinc oxide powder. After the teeth were polished, the specimens were washed by water and dried by air. Surface roughness tester, Taylor-Habson's Taly Surf-10, (Fig-1) was used to measure roughness of this unetched tooth surface. And that, the specimens were divided into three groups. The first group was etched with Restodent etchant, the second group was etched with Nuva-system etchant, and Hi-pol etching agent was used in the third group. And the surface roughness tester was used to measure roughness of the etching teeth surface. The results obtained were as follows. 1. The roughness of acid-etched enamel were increased $2{\mu}m$ to $6{\mu}m$. 2. Hi-pol etchant produced the smoothest surface($2.3{\mu}m$). 3. Restodent etchant($3.8{\mu}m$) and Nuva-system etchant($3.7{\mu}m$) produced rougher surface than Hi-pol.

• Restorative Dentistry and Endodontics
• /
• v.16 no.2
• /
• pp.197-212
• /
• 1991

The purpose of this study was to roughness on the polished surface of visible light composite resins and was to observe the polished surfaces under Scanning Electrom Microscope(ISI DS 130 AKASHI Co. JAPAN). The surface roughness tester(Surfcom 700A Seimtsu profilometer Tokyo, Japan) was used to measure roughness of polished surfaces. In this study, 5 brands of visible of composite resins were examined, Pyrofile light bond Anterior Lite fil anterior Photo clearfil anterior & posterior Palfique light Anterior and posterior Silux Anterior. White point, Silicure point, Super snap Sof-Lex medium disk as cutting instrument, and celluloid matrix were used. The results obtained were as follows. 1. The Celluloid matrix produced the smoothest surfaces. 2. The surfaces made by Soflex medium disk was smoother than the surfaces made by any other polishing instruments. 3. The values of surface roughness made by White point, Silicon point and Super snap were similer. 4. Palfique light (AP) visible light composite resin showed the smoothest surface after polishing with Silicone point, Super snap disk and Soflex mediuem disk in all tested materials.