• Journal of the Korean Ceramic Society
• /
• v.52 no.4
• /
• pp.290-293
• /
• 2015

The properties of the IZTO thin films on the glass were studied with a variation of the $SiO_2$ buffer layer thickness. $SiO_2$ buffer layers were deposited by plasma-enhanced chemical vapor deposition (PECVD) on the glass, and the In-Zn-Tin-Oxide (IZTO) thin films were deposited on the buffer layer by RF magnetron sputtering. All the IZTO thin films with the $SiO_2$ buffer layer are shown to be amorphous. Optimum $SiO_2$ buffer layer thickness was obtained through analyzing the structural, morphological, electrical, and optical properties of the IZTO thin films. As a result, the IZTO surface roughness is 0.273 nm with a sheet resistance of $25.32{\Omega}/sq$ and the average transmittance is 82.51% in the visible region, at a $SiO_2$ buffer layer thickness of 40 nm. The result indicates that the uniformity of surface and the properties of the IZTO thin film on the glass were improved by employing the $SiO_2$ buffer layer and the IZTO thin film can be applied well to the transparent conductive oxide for display devices.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.12
• /
• pp.601-605
• /
• 2004

In this paper, we investigated ionic impurities and physical properties by change of carbon black content, which is asemiconductive material for underground power transmission. Specimens were made into sheet form with three existing resins and nine specimens for measurement. The ionic impurities of the specimens were measured using anICP-AES (Inductively Coupled Plasma Atomic Emission Spectrometer), and the density of specimens was measured by a density meter. Specific heat (Cp) was then measured using aDSC (Differential Scanning Calorimetry). The ranges of measurement temperature were from 0[$^{\circ}C$] to 200[$^{\circ}C$], and heating temperature was 4[$^{\circ}C$/min]. Ionic impurities were measured to be high according to increases in the content of carbon black from this experimental result and density was also increased according to these properties. In particular, the impurity content values of A1 and A2, and existing resins, were measured at more than 4000[ppm]. Specific heat from the DSC results was lowered according to augmentation in the content of carbon black. The ionic impurities of carbon black containing Fe, Co, Mn, Al and Zn are forms of rapidly passed kinetic energy that increase the number of times breaking occurs during unit time with the near particles according to an increase in the vibration of particles by the applied heat energy.

• Journal of Chest Surgery
• /
• v.15 no.2
• /
• pp.259-265
• /
• 1982

We have designed a new type of bubble oxygenator (KOREA-KIM VENOTHERM OXYGENATOR) made of PVC sheet and deforming mesh incorporated in the heat exchanger, and evaluated in experimental animal for the analysis of it`s efficiency. The Oxygenator has low priming volume with high flow rate up to 6 L/rain, and efficiency of heat exchanger was excellent as 1-$1.5^{\circ}C.$ using total cardiopulmonary bypass method under moderate to deep hypothermia. Average priming volume of 1317 ml with 30% hemodilution method was perfused with an average of 1.1-3.0 L/min.$M^2$of arterial blood and pure oxygen at a rate of 2-3.4 L/min for 49.6 minutes continuously in average. During total cardiopulmonary bypass, average $PaO_2$ was $159.8{\pm}60$mmHg, $PaCO_2$ $41.0{\pm}3$mmHg respectively under $SaO_2$ over 96% with systolic arterial pressure of 70 mmHg and CVP of 5-10 cm$H_2O$. Plasma free Hemoglobin was $7.0{\pm}4$ mg/dl with 25% drop of hemoglobin and hematocrit at the end of cardiopulmonary bypass. This KKV Oxygenator was observed to have excellent capabillty of oxygen and carbon dioxide gas transfer with small amount of blood trauma, and the efficiency of heat exchanger was satisfactory during cooling and rewarming of the bubbled blood. Disadvantages have included the somewhat poor deforming effect due to loose PVC fiber mesh, the extracompact character of Teflon filters, and the rough inner surface of the heat exchanger copper pipes.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.22 no.2
• /
• pp.90-96
• /
• 1985

The properties of plasma-enhanced CVD phosphorous silicate glass (PECVD PSG) for passivation layer are studied . Phosphorous contentration was analyzed with X-ray fluores-cence. As a result, PECVD PSG has a limiting phosphors concentration of about 8 mole%. Curves relating to etcll rate, infrared absorption ratio, and sheet resistivity were adapted to monitor phosphorous concentration indirectly Dielectric properties, step coverage, crack resistance, and gettering effect are discussed in both of atmospheric pressure CVD (APCVO) and PECVD oxide. PECVD SiO2 film have density of about 2.4 g/㎤ at deposition rate of 450$\AA$/min, refractive index of about 1.53, and breakdown at fields of II-13 MV/cm. Crack resistance of PECVD oxide is greater than APCVD oxide. PECVD PSG films contained with 2 mole % phosphorous show good step coverage and gettering ability. The obtained results show more advantages in PECVD PSG than in APCVD PSG for device passivation.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.823-827
• /
• 2005

Barrier ribs in the plasma display panel (PDP) function to maintain the discharge space between the glass plates as well as to prevent optical crosstalk. Patterning of barrier ribs is one of unique processes for making PDP. Barrier ribs could be formed by screen-printing, sand blasting, etching, and photolithographic process. In this work photosensitive barrier rib pastes were prepared by incorporating binder polymer, solvent, functional monomers photoinitiator, and barrier rib powder of which surface was treated with fumed silica particles. Studies on the function of materials for the barrier rib paste were undertaken. After optimization of paste formulation and photolithographic process, it was applied to the photosensitive barrier rib green sheet and was found that photolithographic patterning of barrier ribs could be formed with good resolution up to $110{\mu}m$ height and $60{\mu}m$ width after sintering.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.12
• /
• pp.1326-1331
• /
• 2004

In this paper, we have investigated thermal properties and Impurities content of specimens showing by changing the content of carbon black that is semiconductive materials for underground power transmission. Specimens were made of sheet form with the three of existing resins and the nine of specimens for measurement. Impurities content of specimens was measured by ICPAES(Inductively Coupled Plasma Atomic Emission Spectrometer). Heat capacity(ΔH) and melting temperature(Tm) were measured by DSC(Differential Scanning Calorimetry). The ranges of measurement temperature were from $0^{\circ}C$ to 20$0^{\circ}C$, and heating temperature was 4$^{\circ}C$/min. And then thermal diffusivity was measured by LFA 447. The measurement temperature was $25^{\circ}C$. Impurities content was highly measured according to increasing the content of carbon black from ICPAES results. And heat capacity and melting temperature from the DSC results were simultaneously decreased according to increasing the content of carbon black, while thermal diffusivity was increased according to increasing the content of carbon black. Because ionic impurities of carbon black containg Fe, Co, Mn, Al, and Zn were rapidly increasing kinetic energy by vibration of ionic impurities through the applied heat energy.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.4
• /
• pp.219-224
• /
• 2006

Silver paste with low sintered temperature has been developed in order to apply electronic parts, such as bus electrode, address electrode in PDP (Plasma Display Panel) with large screen area. In this study, nano-sized silver particles with 10-30 nm were synthesized from silver nitrate ($AgNO_3$) solution by chemical reduction method and silver paste with low sintered temperature was prepared by mixing silver nanoparticles, conventional silver powder with the particle size 1.6 um and Pb-free frit. Conductive thick film from silver paste was fabricated by screen printing on alumina substrate. After firing at $540^{\circ}C$, the cross section and surface morphology of the thick films were analyzed by FE-SEM. Also, the sheet resistivity of the fired thick films was measured using the four-point technique.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.5
• /
• pp.636-644
• /
• 2006

Recently, there were some successful examples that the laser welding was introduced into production line. However, the spread of laser welding is not sufficient in many industries. There are several reasons why it is difficult to penetrate the laser welding into production lines. Because it is different from reflection, absorption and permeation of laser beam according to material and surface condition. Moreover, there are significant problems in processing such as absorption and scattering of beam by the induced plasma or plume. Therefore, understanding of mechanism on formation of weld defect in laser welding of the laminated core for motor is very important. In this paper, it was analyzed in terms of materials which was source of defect in laser welding and conventional arc welding. As a results of analysis, insulation coating film of the laminated core was judged to main factor of weld defect. it could be well aware as tracing carbon volume, and it was deduced that weld defect by insulation coating film was caused by difference of mechanism between the two heat sources.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.248.1-248.1
• /
• 2014

We present results from an experimental study of conductivity change of poly (3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) film according to the surface structuring. We demonstrate that the patterned structure was enhanced with approximately five times conductivity in comparison with non structure of PEDOT:PSS film. In order to patterning, we have fabricated polystyrene (PS) colloidal monolayer as a template with sphere diameter of 780nm and 1.8um. Structure has honeycomb shape and it provide shorter path way to flowing of electron. Pattern size was controlled by PS diameter and varied by Transformer Coupled Plasma (TCP) etching system. Conductivity was converted from sheet resistance which measured by 4-point prove. Film thickness was derived using Field Emission Scanning Electron Microscopy (FE-SEM) images.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.9
• /
• pp.455-458
• /
• 2004

In this paper, we investigated impurities content and physical properties showing by changing the content of carbon black that is semiconductive materials for underground power transmission. Specimens were made of sheet form with the three of existing resins and the nine of specimens for measurement. Impurities content of specimens was measured by ICP-AES (Inductively Coupled Plasma Atomic Emission Spectrometer), and density of specimens were measured by density meter And then specific heat (Cp) was measured by DSC (Differential Scanning Calorimetry). A ranges of measurement temperature were from $0^{\circ}[C]$ to $200^{\circ}[C]$, and heating temperature was $4^{\circ}[C/min]$. Impurities content was highly measured according to increasing the content of carbon black from this experimental result, also density was increased according to these properties. Especially impurities content values of the Al and A2 of existing resins were measured more than 4000［ppm］. Specific heat from the DSC results was decreased according to increasing the content of carbon black. Because ionic impurities of carbon black having Fe, Co, Mn, Al and Zn are rapidly passed kinetic energy increasing the number of times breaking during the unit time with the near particles according to increasing vibration of particles by the applied heat energy.