• Textile Coloration and Finishing
• /
• v.21 no.4
• /
• pp.46-56
• /
• 2009

In order to establish the standard manufacturing condition of PET flame retardant sheets, physicochetnical properties of the samples made by the conventional flame-retardant finishing were systematically investigated, including compatibility among flame retardant agent and finishing auxiliaries, surface property, and wicking property. From this results, the addition of washing and renapping process after the shearing process was required for the more effective in producing PET flame-retardant sheet by the standard finishing. The effect of the modification of the regular flame retardant finishing process was studied by FTIR, TGA, and flame retardancy test.

• Elastomers and Composites
• /
• v.37 no.4
• /
• pp.224-233
• /
• 2002

This study has investigated the flame retardant properties of EPDM rubber with the addition of various flame retardants. Carbon black, stearic acid, zinc oxide cross-linking agent were mixed with EPDM rubber to produce the base rubber E0 without the addition of flame retardants. Phosphorus flame retardant Tricrecyl phosphate(TCP) was added to E0 in 0.5, 1, 1.5, 2 phr to make E1~E4 samples and red phosphorus was added in 3, 6, 9, 12 phr to make E5~E8 samples. A flame retardant of the bromine family Decabromodiphenyloxide(DBDPO), and a chlorinated paraffin retardant of the chlorine family was added to E0 in 3, 6, 9, 12 phr to make E9~E12 and E13~E16 samples, repectively. Basic physical properties such as tensile strength, tear strength and hardness were measured for all the rubber samples with various flame retardant additions. There was no substantial differences. On the other hand, Oxygen index and UL94 were measured to study flame retardant properties. From oxygen index measurements E0 sample showed a value of 23.5%, indicating the improvement of flame retardant properties. Also from UL94 measurements, it was found that addition of red phosphorus resulted in maximum flame retardant effect. It was found that increasing the amount of addition resulted in decreasing combustion rate and improving flame retardant effect regardless of the kind of flame retardant.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1678-1686
• /
• 2021

In this study, we prepared phosphorous flame-retarding coating solutions by mixing triphosphate (3 phosphonate), phytic acid (6 phosphonate), or ammonium polyphosphate (10 phosphonate) with boric acid as a crosslinking agent and acryl resin binder. Prepared phosphorous flame-retarding coating solutions were coated onto non-woven fabrics, respectively, to obtain high flame-retarding effects. These prepared flame-retardant non-woven fabrics were evaluated using smoke density standard test (ASTM E662), limit oxygen index standard test (ISO E622), and vertical burning standard test (UL 94). Their flame-retarding effects were affected by the number of phosphonate groups. Regardless of natural or synthetic binder resins, their effects showed the following order: ammonium polyphosphate > phytic acid > triphosphate. Natural hydrocarbon compounds were also examined to determine the possible retardancy of binder resins. Results showed that natural hydrocarbon binder resins could be used for preparing fire-retardant nonwoven fabrics.

• Journal of the Korean Applied Science and Technology
• /
• v.29 no.2
• /
• pp.224-230
• /
• 2012

In this paper, flame-resisting PMMA(polymethyl methacrylate) sheet was manufactured and its characteristics were tested. PMMA was synthesized by bulk polymerization of a monomer methyl methacrylate with addition of phosphorous flame retardant, triethyl phosphate and ethylene glycol dimethacrylate as a cross linking agent. PMMA sheet was manufactured by using the cell molding method, which does not alter or affect the existing property of PMMA. Then the characteristics of PMMA sheet were tested for the TEP content, the content and curing time of EGDMA. As TEP content increases, the length of carbonization lessens and the amount of char production increases. As a result, it strengthened the effect of flame retardants. But the hardness of the sheet decreased as TEP content increased. However, hardness increased when EGDMA was added up to 3 wt% while curing time was decreased from 3 hours to 2 hours. There was no change of hardness when more than 3 wt% of EGDMA was used.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.4
• /
• pp.349-355
• /
• 2019

A fire, be it caused intentionally or unintentionally, leads to economic loss and physical damage, and requires digestion. The number of fires is increasing yearly, and electrical fires account for more than 30% among the main causes of fires. Electric wires that catch fire typically employ silicone coatings; silicone has organic as well as inorganic properties. Silicon is a natural, nonexistent, synthetic product with numerous applications. In this study, a silicon rubber for application in wires was prepared by high-temperature vulcanization (HTV) with a Shore A hardness of 70. We report results for the flame retardancy test and the fire safety characteristics via inorganic analysis. For this, a quartz inorganic material was added to the wire specimen, and 18% powdered extinguishing agent ammonium phosphate and expanded vermiculite respectively. Thus, expanded vermiculite showed the best flame retardancy and fire safety characteristics.