• Journal of Korea Foundry Society
• /
• v.15 no.3
• /
• pp.291-297
• /
• 1995

The mechanical properties and fracture toughness of permanent mold cast austempered gray cast iron(AGI) were compared to those of sand cast AGI. The iron was melted to eutectic composition in order to get better castability especially in permanent mold casting. Specimens prepared for tensile, impact and fracture toughness test were austenitized at $900^{\circ}C$ and austempered at $270^{\circ}C$ and $370^{\circ}C$ for 1 hour. The strength, impact and fracture toughness of permanent mold cast AGI were found to be superior to those of sand cast AGI. The maximum value of 836 MPA in tensile strength, was obtained at the austempering temperature of $270^{\circ}C$. But ductility of AGI was not improved by permanent mold casting.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.04a
• /
• pp.77-82
• /
• 1998

The Part of slot on rotary compressor which plays an important part of the reliability and performance is studied on machinability and the wear characteristics for the specimen made by sand mold and permanent mold. The experiment are used the face cutter of milling machine which make the processing surface like broaching process and rollblock wear test machine. Permanent-mold casting iron is not affected by variation of RPM of milling machine, but sand-mold cast-iron is improved to increasing RPM. Also sand-mold casting iron shows superior wear characteristic to permanent-mold casting iron. This results from harder matrix of pearlite structure and self-lubrication characteristics of graphite. And wear particles in tested oil show shape and size similar to severe wear particles of oil taken from rotary compressor. The material and surface condition of slot play important part of the reliability and performance.

• Journal of Korea Foundry Society
• /
• v.11 no.1
• /
• pp.44-53
• /
• 1991

The proper feeding conditions for thin Al-Alloy (AA336, JIS AC8A) castings in permanent mold were investigated to eliminate microshrinkage porosity. 5mm-thick plates (200mm long, 60mm wide) were cast with increasing padding taper from 0 to 5% under different conditions : (1) constant mold temperature of $350^{\circ}C$, (2) continuous production with uniform mold thickness (10mm), (3) continuous production with a negative taper of 2.5% in mold thickness (thickness decreasing in direction to riser). The test casting were machined off to the midplane and the shrinkage porosity was examined visually. The critical padding taper which can just eliminate the shrinkage porosity was determined for each condition, i.e. : (1) 4.5% at the constant mold temperature, (2) 3.5% for continuous production with the uniform mold thickness (3) 1.5% for continuous production with the taper in mold thickness. A computer simulation by a finite difference analysis program was applied to the test casting. The liquid fraction gradient (LFG) and the temperature gradient divided by the square root of the cooling rate (G /SR) were calculated at the end of solidification and compared with the shrinkage porosity area in the castings. For the case of constant mold temperature, LFG is a better parameter to predict shrinkage porosity than G /SR and its critical value is around 11%/cm. But for the case of continuous production, neither LFG nor G /SR could be a reliable parameter. The experimental results about the critical padding taper are of practical interest for designing permanent molds and castings. The computer simulation results stimulate further research to be directed on the prediction of centerline microshrinkage porosity in continuous production.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.1047-1052
• /
• 2003

The purpose of this study is to improve the productivity and constructability of permanent forms. The permanent forms will cut down the cost of production and make easier to install in the field; hence increase the use of forms in the today's market. The permanent form is produced in the factory and built in field. So this study is in two parts. The one is the productivity in factory, the other is constructability in the field. This study is the designing a new mold system as a solution to existing mold system's problems.

• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.135-139
• /
• 2007

To produce higher quality of titanium casting at a lower cost, the new titanium casting technology by using a permanent metal mold was developed and applied to fabricate hip joint for biomedical application. The present study was carried out to investigate the reactivity and fluidity of the Ti-6.0 wt%Al-4.0 wt%V alloy with metal mold by applying various ceramic powders coating on the mold surface. The molten titanium for manufacturing hip joint was poured into steel mold. No reaction layer was formed on the surface of specimens fabricated steel mold coated with $Y_2O_3$ powder.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.751-756
• /
• 2001

Permanent-Form is one of system forms for reducing human labor, work costs, oscillation, noise, construction wastes and so on. Permanent-Form is made from precast method in facilities. and carried in construction site to assemble with no demolding. The biggest expense to produce Permanent-Form is about manufacturing mold. To satisfy various size of building member, the same number of manufacturing mold is needed. In this paper, studied about manufacturing mold module for acquiring economic merit and construction member safety. Permanent-Form is member stress and structural analyzed if temporary equipment were used. The result of this study is below. (1) Column sizes of Permanent-Form are 47 kinds of prototype that based on Modular coordination's basic module. 4 pieces or 6 pieces are composed basically. (2) For beam size modular coordination, standard height and width of beam are 150mm and 100mm. It brings 24 kinds of prototype. 4 pieces or 5 pieces are composed basically. (3) Structural analysis value of modular member is like this Column member shows 9.4 to 85kgf/$cm^{2}$ stress distribution and beam member shows 6.3 to 95kgf/$cm^{2}$ stress distribution. Constructing permanent form could have structural safety with use of temporary equipment

• Journal of Korea Foundry Society
• /
• v.13 no.3
• /
• pp.259-267
• /
• 1993

The effects of casting processes-direct and indirect squeeze casting, permanent mold casting and die casting on the microstructure and mechanical properties were studied for the hypereutectic B390 aluminium alloy. The effects of T5 and T6 heat treatment were also examined. The direct and indirect squeeze casting showed no casting defects such as porosity and shrinkage were observed in permanent mold castings and die castings. The primary silicon phase was refined and homogeneously distributed in the order of indirect squeeze casting, diecasting, direct squeeze casting and permanent mold casting. Depletion of primary silicon phase in die casting surface was disappeared in indirect squeeze casting. Tensile strength of cast and heat treated specimens were increased in the order of direct squeeze casting, permanent mold casting, indirect squeeze casting and die casting. Hardness of indirect squeeze castings was larger than that of other castings. As indirect squeeze casting of B390 aluminium alloy, the time of T6 heat treatment to achieve high strength can be reduced.

• Journal of Korea Foundry Society
• /
• v.20 no.1
• /
• pp.3-12
• /
• 2000

The lead content of drinking water has been restricted to less than 15 ppb by Environmental Protection Agency (EPA) in USA. This has led to extensive research and development work at the Materials Technology Laboratory (MTL) of CANMET, a Canadian Government research laboratory, on the development of low-lead and lead-free copper alloys for plumbing applications. Attentionhas also been focused on the environmentally friendly and energy efficient permanent mold casting process to minimize the disposal of foundry sand contaminated by lead due to the use of leaded alloys in the non-ferrous foundries. A new series of alloys called SeBiLOY contaning Bi and Se been introduced to replace lead in the leaded alloys. This paper addresses some important casting characteristics such as fluidity, hot tear resistance, mechanical properties and microstructure of lead-free alloys such as SeBiLOY III and low-lead alloys such as silicon brass, silicon bronze and yellow brass in gravity permanent mold casting.

• Journal of Korea Foundry Society
• /
• v.35 no.2
• /
• pp.36-43
• /
• 2015

In this study, the influences of aluminum and tin additions (individual and combined) on corrosion behavior of magnesium alloy have been determined. The studied alloys were fabricated by permanent mold casting method to measure the corrosion properties, a potentiodynamic test, hydrogen evolution test and immersion test were carried out in a 3.5% NaCl solution at pH 7.2. From the results of microstructure analysis, the Mg-9Al-1Zn alloy was found to be composed of ${\alpha}$-Mg and rod-like $Mg_{17}Al_{12}$ phase and the Mg-5Sn-5Al-1Zn alloy was found to be composed of ${\alpha}$-Mg, rod-like $Mg_{17}Al_{12}$ and $Mg_2Sn$ phases. In the case of the Mg-9Sn-1Zn alloy, the microstructure was composed of ${\alpha}$-Mg and eutectic $Mg_2Sn$ phase. With Sn addition (individual and combined), the corrosion resistance of the Mg alloys improved.

• Journal of Korea Foundry Society
• /
• v.36 no.2
• /
• pp.60-66
• /
• 2016

In this study, comparison of corrosion properties of the Mg-1.5Ge-1Zn (GZ21) alloy and Mg-9Al-1Zn (AZ91) alloy were investigated. The studied alloys were fabricated by permanent mold casting method. And the potentiodynamic test, hydrogen evolution test, immersion test and A.C Impedance test were carried out in a 3.5% NaCl solution with pH7.2 at room temperature to measure the corrosion properties. The microstructure of GZ21 alloy was composed of ${\alpha}-Mg$ and $Mg_2Ge$ phases and AZ91 alloy was composed of ${\alpha}-Mg$ and $Mg_{17}Al_{12}$ phases. From the test results, the corrosion property was improved by adding Ge. It seemed that the corrosion mechanism was changed from galvanic corrosion (AZ91) to filiform corrosion (GZ21).