• Textile Coloration and Finishing
• /
• v.29 no.2
• /
• pp.97-103
• /
• 2017

Polyketone fiber, a newly developed high strength fiber, has a tenacity and modulus similar to the p-aramid fiber, and can be used for reinforcing mechanical rubber goods(MRG), such as tires, hoses, and technical textiles. It will be expected for replacement of super fiber such as aramids and increasing the technical textile market share. This paper surveys the mechanical properties of polyketone fiber for technical textiles. For this purpose, dyed polyketone fabric is prepared, mechanical properties of coated and uncoated polyketone fabrics such as tensile strength, elongation and tear strength were examined before and after weather resistance test(temperature $63{\pm}3^{\circ}C$, humidity 60%, amount of power $0.35w/m^2$). The differences of mechanical properties between uncoated and coated fabrics for high functional technical textiles and composite materials are estimated through this study. The UV-stability of polyketone fabric showed obvious improvement after coating. After 168h(7day) of UV exposure, the coated fabric showed less deterioration in mechanical properties with the retained tensile strength and elongation at break greater than 22 and 17% of the uncoated polyketone fabrics values, respectively.

• Journal of dental hygiene science
• /
• v.10 no.6
• /
• pp.445-450
• /
• 2010

The aim of this study was to evaluate the effect according to the fiber type and combination on the reinforcement of heat-polymerized denture base resin. The heat-polymerized resin(Vertex RS, Dentimax, Netherlands) was used in this study. Glass fiber(GL; ER 270FW, Hankuk Fiber Glass, Korea), polyaromatic polyamide fiber(PA; aramid; Kevlar-49, Dupont, U.S.A.) and ultra high molecular weight polyethylene fiber(PE, polyethylene; P.E, Dong Yang Rope, Korea) were used to reinforce the denture base resin specimens. The final size of test specimen was $64mm{\times}10mm{\times}3.3mm$. The specimens of each group were stored in distilled water at $37^{\circ}C$ for 50 hours before measurement. The flexural strength and flexural modulus were measured by an universal testing machine(Z020, Zwick, Germany) at a crosshead speed of 5 mm/min in a three-point bending mode. In this study, all fibers showed reinforcing effects on denture base resin(p<0.05). In terms of flexural strength and flexural modulus, glass fiber 5.3 vol.% showed most effective reinforcing effect on heat polymerized denture base resin. For flexural modulus, PA/GL was the highest in denture base resin specimen for hybrid FRC using two combination (p<0.05). Glass fiber 5.3 vol.% and PA/GL are considered to be applied effectively in reinforcing the heat polymerized denture base resin.