• Journal of Ceramic Processing Research
• /
• v.20 no.6
• /
• pp.655-659
• /
• 2019

Calcium phosphates such as HA (hydroxyapatite), β-TCP (tricalcium phosphate) and biphasic HA/β-TCP, were synthesized by wet chemical precipitation in aqueous solution combined with ball milling process. Nanosize powders of the calcium phosphates were synthesized using Ca(OH)2 and H3PO4. The effects of initial precursor Ca/P ratio (1.30, 1.50 and 1.67), ball milling process and post heat-treatment on the phase evolution behavior of the powders were investigated. The phase of resulting powder was controllable by adjusting the initial Ca/P ratio. HA was the only phase for as-prepared powders in both cases of Ca/P ratios of 1.50 and 1.67. The single HA phase without any noticeable second phase was obtained for the initial Ca/P ratio of 1.67 in the overall heat-treatment range. Pure β-TCP and biphasic calcium phosphate (HA/β-TCP) were synthesized from precursor solutions having Ca/P molar ratios of 1.30 and 1.50, respectively, after having been heat-treated above 700 ℃. The β-TCP phase has appeared on the pre-existing DCPD (dicalcium phosphate dihydrate) and/or HA phase. Dense ceramics having translucency were obtained at a considerably lower sintering temperature. The modified process offered a fast, convenient and economical route for the synthesis of calcium phosphates.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.24 no.3
• /
• pp.311-316
• /
• 2008

Calcium phosphate cement (CPC) has been used as bone substitute successfully due to good biocompatibility and osteoconductivity. One of the important mechanical characteristics of CPC is flowablility, which can be evaluated by measuring rheological parameters. However, there have been few studies that measured rheological properties of CPC. The purpose of this study was to evaluate the rheological properties of CPC paste mixed with 2 kinds of setting solutions, 2% hydroxyprophyl methylcellulose (HPMC) and 35% polyacrylic acid (PAA). The CPC used was dicalcium phosphate dihydrate (DCPD). Rheological properties of CPC paste were measured using rheometer. The statistical analysis was carried out with Mann-whitney test with Bonferronis collection. CPC with both setting solutions showed shear thinning behavior. CPC with 2% HPMC showed signigicantly higher complex viscosity than CPC with 35% PAA(p<0.05).

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.39.1-39.1
• /
• 2011

가압경수로의 압력경계기기는 약 $300^{\circ}C$, 150기압의 고온고압수환경에서 가동되고 있다. 특히 가압기 밀림관은 고온수와, 저온수가 교차하는 부분으로 열성층 형성으로 열적, 기계적 피로 및 수화학환경이 더해진 부식피로 등에 의하여 손상을 받는다. PWR 원전에서 수화학환경은 대표적으로 용존산소(DO) 5ppb, pH 6~8, 용존수소(DH) <30 cc/kg, 온도 $316^{\circ}C$의 환경을 유지하게 된다. 가압기 밀림관에는 오스테나이트계 스테인리스강이 사용되는데, 오스테나이트계 스테인리스강은 고온 수화학환경에 민감한 것으로 알려져 있다. 따라서 오스테나이트계 스테인리강을 공기중에서의 기계적특성 및 피로특성을 향상시키기 위하여 질소를 첨가한 스테인리스강을 제조하여 PWR 원전환경에서의 피로균열성장특성을 평가하였다. 실험에 사용된 재료는 PWR 원전 가압기 밀림관 소재인 Type 347 스테인리스강에 0.0005 wt%가 첨가된 상용재와 0.11 wt% 질소가 첨가된 재료이다. 사용된 시편형상은 두께 5 mm, 폭 25.4 mm의 CT 시편이다. 수화학환경은 150기압, 온도 $316^{\circ}C$, 용존산소(DO) 5ppb, 용존수소(DH) 30 cc/Kg, pH는 약 7로 유지 하였으며, 응력비 0.1, 하중 반복속도 10Hz의 기계적 조건에서 하중제어로 시험을 진행하였다. 균열길이는 직류전위차법(Direct Current Potential Drop: DCPD)을 이용하여 측정하였다. 질소함량이 증가할수록 동일 사이클에서 균열길이가 늦게 성장하였고, 피로균열성장속도도 약간 늦어지는 것으로 나타났다. 각 스테인리스강의 피로파면 관찰결과 상용재는 약 1 ${\mu}m$의 산화물들이 생성되는 반면 질소첨가 스테인리스강은 약 0.1 ${\mu}m$정도 산화물이 생성되었다. 산화막의 두께도 질소가 첨가됨으로써 상용재에 비해 얇게 생성되었다. 따라서 질소가 첨가됨으로써 부식환경에서 내산화성이 향상되었으며, 이는 피로균열성장특성에 영향을 미치는 것으로 판단된다.