• Journal of the Korean Wood Science and Technology
• /
• v.39 no.4
• /
• pp.359-369
• /
• 2011

The study was carried out to investigate the quality characteristics of pellets manufactured with adding soybean oil, waste soybean oil, ozonized soybean oil and ozonized waste soybean oil to Larix kaemferi Carr sawdust. The characteristics of pellet included moisture contents, heating value, ash contents, apparent densities, durabilities, absorption ratio and elementary analysis. Moisture contents were shown 7.66~9.48% which satisfied the first grade (less than 10%) of quality standard of wood pellets announced by Korea Forest Research Institute. The heating value of the manufactured wood pellets in this study exceeded the first grade of quality standard (more than 4,300 kcal/kg) and it appeared that the pellets manufactured with adding oils and ozonized oils had more heating value than the control pellets. Ash contents 0.34~0.42% also passed the first grade (less than 0.7%) of quality standard and apparent densities were adequate for the first grade (640 kg/$m^3$) on the quality standard. Durabilities of the pellets manufactured with adding soybean oil and ozonized waste soybean oil were shown over the first grade (97.5 kg/$m^3$) of quality standard. In the general results of durabilities, the pellets manufactured with additives had better values than the control pellets. After 24 hours absorption ratio experiment, absorption ratio of pellets manufactured with additives also appeared much lower moisture absorption than the control pellets and they still had the same results after 5days absorption ratio experiment. Elementary analysis of the sulfur content was satisfied the first grade (less than 0.05%) of quality standard of wood pellets and the nitrogen content was also adequate for the first grade (less than 0.3%) of quality standard of wood pellets.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.6
• /
• pp.498-504
• /
• 2011

The purpose of this study was to investigate and develop an eco-frendly wood adhesive based on vegetable oil (especially soybean oil), the renewable and sustainable natural resources, using ozonification technology for the chemical structure modification. The waste soybean oil (WSBO) was reacted with $O_3$ at the rate of $450m{\ell}$(acetone) : $50m{\ell}$ (WSBO) for different times, 1, 2, 3 hrs. The investigation of the modified chemical strecture of the ozonied WSBOs were conducted using FT-IR. As ozonification time increased, the peak of the unsaturated double bonds was disappeared especially ozonized-3hrs and aldehyde or carboxyl peak appeared because ozonification broke the oil into small molecules. The plywood were made at $150^{\circ}C$ with 4 minutes hot-press time using the different ozonized 3 hrs WSBO/pMDI adhesives and were tested for the dry, wet, cyclic boil test according to the Korea Industrial Standard F3101 Ordinary plywood. The bond strengths gradually increased until 1 : 0.5~1 : 3, but it decreased 1 : 4, as the contents of pMDI increased. The results of the dry, wet and cyclic bond strengths the equivalent ratio was formed approximately between 1 : 2~1 : 3. And the 1 : 1~1 : 4 strengths met constantly the standard requirement of 7.0kgf/$cm^2$ (KS F3101). From the comprehensive view on the results of above experiment, it could be confirmed that ozonized WSBO/pMDI has characteristics of effective reactivity and wet stability showed as an excellent candidate of wood adhesive applications.