• 대한가정학회지
• /
• 제5권1호
• /
• pp.815-825
• /
• 1966

Many synthetic antioxidants are now used to prevent the oxidation of oils and fats. Among the synthetic and tioxidants, it was known that those of HQ(Hydroquinone), BHA(Butyl hydroxyanisole), IG(isoamyl gallate), and NDGA(Nordihydro guaiaretic acid) are most efficient as the antioxidizing agent. In this work, Degree of antioxidation was investigated on the some such antioxidans BHA, CI(citric acid), AA(Ascoric acid) for several kinds of oils and fats which are most available in Korea by determining Acid value and Iodine Value. The results of experiments were as follows 1. The decreasing order of antioxidizing action by acid value is BHA, AA, CA. 2. The order of antioxidizing action by Iodine value is almost same as the case of Acid Value. 3. It is effective to add the antioxidants to kep oils and fat. 4. Oxidation is accelerated by standing oils and fats after boiling in the from fry pan. 5. Sesame oil is little oxidized without antioxidant.

• 폴리머
• /
• 제24권1호
• /
• pp.97-104
• /
• 2000

산화처리 된 평직형태의 탄소섬유와 resole 형태의 페놀수지를 7:3 중량비로 혼합하여 성형공정에 따라 탄소섬유/페놀수지 복합재료를 제조하였으며, 이를 다시 불활성 분위기에서의 탄화(100$0^{\circ}C$) 및 $CO_2$ 분위기에서 활성화(700, 800,, 900 및 100$0^{\circ}C$)시켜 PAN계 활성탄소섬유/페놀수지 복합재료를 제조하였다. 본 연구에서는, 이렇게 제조된 복합재료에 활성화 온도가 미치는 영향을 중화 적정법에 따른 pH, 표면 산도 및 표면 염기도 등의 표면성질과 BET 방법에 따른 비표면적, 기공구조 등의 흡착특성을 측정하여 고찰하였다. 또한, ASTM에 따라 시편에 걸리는 압력 손실을 측정하였다. 결과적으로, 활성화 온도는 그 표면 성질의 변화에 영향을 주어, 90$0^{\circ}C$ 이상의 온도에서 시료의 표면은 점차 염기성이 커지는 것을 확인할 수 있었다. 또한, 비표면적, 총 기공 부피 및 기공 크기 분포도 등의 발달은 활성화 온도의 증가에 따라 점차 증가함을 쉽게 확인할 수 있으며, 그 중 활성화 온도가 90$0^{\circ}C$인 경우 가장 발달한 것으로 나타났다. 마찬가지로, 활성화 온도의 증가에 따라 시편 양 단면에 걸리는 압력손실은 점차 감소하였으며, 이것은 열처리 온도에 의한 활성탄소섬유 복합재료의 질량손실에 의한 것으로 사료된다.

• Journal of Korean Society for Atmospheric Environment
• /
• 제10권E호
• /
• pp.311-324
• /
• 1994

The quantitative knowledge of N $O_{\gamma}$ (＝N $O_{x}$ ＋HN $O_3$＋/PAN＋N $O_3$ ＋$N_2$ $O_{5}$ ＋HN $O_2$＋N $O_3$$^{-10}$ ＋organic nitrates＋......)distribution is essential in tropospheric chemistry, especially, especially that related to understanding the processes leading to ozone production. Ambient concentrations of NO, N $O_2$, HN $O_3$ and PAN as well as total N $O_{\gamma}$ were measured during June and early July 1992 at a rural site(Candor, NC), in the central Piedmont region of NC. The measurements of N $O_{\gamma}$ species were made in an effort to provide a comprehensive understanding of nitrogen chemistry and to investigate the total nitrogen budget at the site. N $O_{\gamma}$, N $O_2$, and NO showed diurnal variations with maxima in the morning. The maximum N $O_{\gamma}$ concentration reached was 14.5 ppbv, and the maximum concentrations of NO and N $O_2$ were 5.4 and 7.8 PPbv, respectively. The mean N $O_{\gamma}$ concentration as found to be 2.88$\pm$1.58 ppbv(n=743). The mean concentrations of NO and N $O_2$, were found to be 0.15 $\pm$ 0.29 ppbv(n＝785) and 1.31 $\pm$ 0.99 ppbv(n＝769). Products of photochemical oxidants, (N <$O_{\gamma}$-N $O_{x}$ ), such as HN $O_3$ and PAN, as well as ozone showed diurnal variation with maxima in the afternoon and minima at night The fractions of individual reactive nitrogen species to total N $O_{\gamma}$ were investigated and contrasted to the results from remote marine site and rural continental sites. N $O_{x}$ was the major species to total N $O_{\gamma}$(45%). NO concentrations appeared to be nearly constant whether the Prevailing winds were from continental areas or from oceanic areas. Linear regression of $O_3$ with (N $O_{\gamma}$- N $O_{x}$ )/N $O_{\gamma}$ (i.e. percent N $O_{x}$ converted to the photochemical products of N $O_{\gamma}$) yielded ( $O_3$) ＝25.8 〔 N $O_{\gamma}$-N $O_{x}$ 〕/(N $O_{\gamma}$) ＋27, ( $r^{2}$＝0.58). The regression intercept is interpreted as the ozone back ground (intercept=27ppbv) and the slope suggests that 8.6 molecules of ozone are formed per molecule of N $O_{x}$ oxidized products (when the average N $O_{\gamma}$ concentration, about 3 ppbv at the site, is used). The N $O_{x}$ N $O_{\gamma}$ ratio was used as an indicator of the chemical age of airmasses and the ratio showed strong positive correlations with HN $O_3$( $r^{2}$=0.58), PAN ( $r^{2}$=0.46) and $O_3$( $r^{2}$=0.62). Larger N $O_{\gamma}$ and N $O_{x}$ N $O_{\gamma}$ ratio were found when winds came from continental sides. It may suggest that synoptic meteorological conditions and transport of N $O_{x}$ are important in the distribution of N $O_{\gamma}$ and its relationship with photochemical oxidants at the site.

• 한국재료학회지
• /
• 제4권7호
• /
• pp.733-740
• /
• 1994

페놀수지 결합재에 보강섬유의 종류에 따라서 내염섬유 보강 복합재(OFRP), 탄소섬유 보강 복합재(CFRP), 유리섬유 보강 복합재(GFRP), 아라미드 섬유 보강 복합재(AFRP)를 제조하였다. 각 보강섬유의 분율을 달리함에 따라 마찰계수 및 마모율을 측정하여 각 보강섬유의 특성이 미치는 영향을 관찰하였다. 아라미드의 섬유량이 45tw%일 때 평균 마찰계수가 0.353-0.383으로 가장 높게 나타난 반면에 핏치계 탄소섬유를 45wt% 보강한 경우 0.164-0.190으로 가장 낮게 나타났다. AFRP와 CFRP의 마모율은 낮게 나타내었으며, GFRP와 OFRP는 섬유분율이 증가함에 따라 급격히 증가하는 양상을 보였다. OFRP는 마모 diagram이 불안정하였으며 CFRP와 AFRP는 대체적으로 안정한 형태를 나타내었다. GFRp는 상당히 불안정한 마모diagram을 나타낸 것으로 보아 마찰 안정성이 가장 떨어짐을 알 수 있었다.