• Journal of Powder Materials
• /
• v.25 no.5
• /
• pp.390-394
• /
• 2018

Metallic tantalum powder is manufactured by reducing tantalum oxide ($Ta_2O_5$) with magnesium gas at 1,073-1,223 K in a reactor under argon gas. The high thermodynamic stability of magnesium oxide makes the reduction reaction from tantalum oxide into tantalum powder possible. The microstructure after the reduction reaction has the form of a mixture of tantalum and magnesium oxide, and the latter could be entirely eliminated by dissolving in weak hydrochloric acid. The powder size in SEM microstructure for the tantalum powder increases after acid leaching in the range of 50-300 nm, and its internal crystallite sizes are observed to be 11.5 to 24.7 nm with increasing reduction temperatures. Moreover, the optimized reduction temperature is found to be 1,173 K as the minimum oxygen concentration is approximately 1.3 wt.%.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.290.1-290.1
• /
• 2016

Grapehen, a single atomic layer of graphite, has been in the spotlight and researched in vaious fields, because its fine mechanical, electrical properties, flexibility and transparence. Synthesis methods for large-area graphene such as chemical vaper deposition (CVD) and mechanical, chemical exfoliation have been reported. In particular, chemical exfoliation method receive attention due to low cost process. Chemical exfoliation method require reduction of graphene oxide in the process of exfoliation such as chemical reduction by strong reductant, thermal reduction on high temperature, and optical reduction via ultraviolet light exposure. Among these reduction methods, optical reduction is free from damage by strong reductant and high temperature. However, optical reduction is economically infeasible because the high cost of short-wavelength ultraviolet light sorce. In this paper, we make graphene-oxide and lanthanoid ion mixture aqueous solution which has highly optical absorbency in selective wevelength region. Sequentially, we synthesize reduced graphene oxide (RGO) using the solution and visible laser beam. Concretely, graphene oxide is made by modified hummer's method and mix with 1 ml each ultraviolet ray absorbent Gd3+ ion, Green laser absorbent Tb3+ ion, Red laser absorbent Eu3+ ion. After that, we revivify graphene oxide by laser exposure of 300 ~ 800 nm layser 1mW/cm2 +. We demonstrate reproducibility and repeatability of RGO through FT-IR, UV-VIS, Low temperature PL, SEM, XPS and electrical measurement.

• Korean Journal of Materials Research
• /
• v.27 no.2
• /
• pp.63-68
• /
• 2017

A black nickel oxide powder, one of the commercial nickel oxide ores, was reduced by hydrogen gas in a batch-type fluidized-bed reactor in a temperature range of 350 to $500^{\circ}C$ and in a residence time range of 5 to 120 min. The hydrogen reduction behavior of the black nickel oxide was found to be somewhat different from that of green nickel oxide ore. For the black nickel oxide, the maximum temperature (below which nickel oxide particles can be reduced without any agglomeration) was significantly lower than that observed for the green nickel oxide. In addition, the best curve fittings of the Avrami model were obtained at higher values of the overall rate constant "k" and at lower values of the exponent "m", compared to those values for the green nickel oxide. It may be inferred from these results that the hydrogen reduction rate of the black nickel oxide is faster than that of the green nickel oxide in the early stages, but the situation reverses in the later stages. For the black nickel oxide ore, in spite of the low temperature sintering, it was possible to achieve a high degree fluidized-bed reduction at lower temperatures and at lower gas consumption rates than was possible for the green nickel oxide. In this regard, the use of black nickel oxide is expected to yield a benefit if its ore price is sufficiently lower than that of the green nickel oxide.

• Journal of Powder Materials
• /
• v.12 no.5 s.52
• /
• pp.336-344
• /
• 2005

In the present study, the focus is on the effect of cobalt oxide powder in the carbothermal reduction of the titanium-cobalt-oxygen based oxide powder by solid carbon for the optimizing synthesis process of ultra fine TiC/Co composite powder. The titanium-cobalt-oxygen based oxide powder was prepared by the combination of the spray drying and desalting processes using the titanium dioxide powder and cobalt nitrate as the raw materials. The titanium-cobalt-oxygen based oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under flowing argon atmosphere. Changes in the phase structure and thermal gravity of the mixture during carbothermal reduction were analysed using XRD and TGA. Titanium-cobalt-oxygen based oxide powder desalted at $600^{\circ}C$ had a mixture of $TiO_2\;and\;Co_{3}O_4$. And the one desalted at $800^{\circ}C$ had a mixture of $TiO_2\;and\;CoTiO_3$. In the case of the former powder, the reduction of cobalt oxide powder in the titanium-cobalt-oxygen based oxide powder occurred at lower temperature than the latter one. However, the carbothermal reduction of titanium dioxide powder in the titanium-cobalt-oxygen based oxide powder with a mixture of $TiO_2\;and\;Co_{3}O_4$ occurred at higher temperature than the one with a mixture of $TiO_2\;and\;CoTiO_3$. And also, the former powder showed a lower TiC formation ability than the latter one.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11b
• /
• pp.86-91
• /
• 2005

A metal product obtained from an electrolytic reduction process, possesses less volume and radioactivity than those of the unprocessed spent oxide fuels. The chemical composition of the metal product varies according to the process condition. In this work, a basic study was performed to evaluate the chemical forms of the spent oxide fuel components in an electrolytic reduction process with the operation conditions. One of the most important operation conditions is the cell potential applied for the reduction cell. It is expected that $PU_{2}O_3$ is difficult to reduce even though the cell potential is negative enough to reduce the lithium oxide when the activity of $Li_{2}O$ exceeds 0.003. The reduction of actinide oxides via the reduction of $Li_{2}O$ is assumed to have a greater reduction yield than a direct reduction of the actinide oxides.

• Journal of Powder Materials
• /
• v.11 no.1
• /
• pp.28-33
• /
• 2004

In the present study, the focus is on the analysis of carbothermal reduction of the titanium-cobalt-oxygen based oxide powder by solid carbon for the optimizing synthesis process of ultra fined TiC/Co composite powder. The titanium-cobalt-oxygen based oxide powder was prepared by the combination of the spray drying and desalting processes using the titanium dioxide powder and cobalt nitrate as the raw materials. The titanium-cobalt-oxygen based oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and thermal gravity of the mixture during carbothermal reduction were analysed using XRD and TGA. The synthesized titanium-cobalt-oxygen based oxide powder has a mixture of $TiO_2$ and $CoTiO_3$. This oxide powder was transformed to a mixed state of titanium car-bide and cobalt by solid carbon through four steps of carbothermal reduction steps with increasing temperature; reduction of $CoTiO_3$ to $TiO_2$ and Co, reduction of $TiO_2$, to the magneli phase($Ti_nO_{2n-1}$, n>3), reduction of the mag-neli phase($Ti_nO_{2n-1}$, n>3) to the $Ti_nO_{2n-1}$(2$\leq$n$\leq$3) phases, and reduction and carburization of the $Ti_nO_{2n-1}$(2$\leq$n$\leq$3) phases to titanium carbide.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.8 no.1
• /
• pp.77-84
• /
• 2010

Reduction of oxides has been investigated for the volume reduction and recycling of the spent oxide fuel from commercial nuclear power plants. Various oxide reduction methods were proposed and KAERI (Korea Atomic Energy Research Institute) is currently developing an electrochemical reduction process using a LiCl-$Li_2O$ molten salt as a reaction medium. The electrochemical reduction process, the front end of the pyroprocessing, can connect the PWR (Pressurized Water Reactor) oxide fuel cycle to a metal fuel cycle of the sodium cooled fast reactor. This paper summarizes KAERI efforts on the development, improvement, and scale-up of the oxide reduction process.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11b
• /
• pp.39-50
• /
• 2005

Electrolytic reduction of uranium oxide to uranium metal was studied in a $LiCl-Li_{2}O$ molten salt system. The reduction mechanism of the uranium oxide to a uranium metal has been studied by means of a cyclic voltammetry. Effects of the layer thickness of the uranium oxide and the thickness of the MgO on the overpotential of the cathode and the anode were investigated by means of a chronopotentiometry. From the cyclic voltamograms, the decomposition potentials of the metal oxides are the determining factors for the mechanism of the reduction of the uranium oxide in a $LiCl-3\;wt{\%} Li_{2}O$ molten salt and the two mechanisms of the electrolytic reduction were considered with regards to the applied cathode potential. In the chronopotentiograms, the exchange current and the transfer coefficient based on the Tafel behavior were obtained with regard to the layer thickness of the uranium oxide which is loaded into the porous MgO membrane and the thickness of the porous MgO membrane. The maximum allowable currents for the changes of the layer thickness of the uranium oxide and the thickness of the MgO membrane were also obtained from the limiting potential which is the decomposition potential of LiCl.

• Carbon letters
• /
• v.24
• /
• pp.1-9
• /
• 2017

We studied the basic properties and fabrication of reduced graphene oxide (rGO) prepared using eco-friendly reduction agents in the graphene solution process. Hydrazine is generally used to reduce graphene oxide (GO), which results in polluting emissions as well as fixed nitrogen functional groups on different defects in the graphene sheets. To replace hydrazine, we developed eco-friendly reduction agents with similar or better reducing properties, and selected of them for further analysis. In this study, GO layers were produced from graphite flakes using a modified Hummer's method, and rGO layers were reduced using hydrazine hydrate, L-ascorbic acid, and gluconic acid. We measured the particle sizes and the dispersion stabilities in the rGO dispersed solvents for the three agents and analyzed the structural, electrical, and optical properties of the rGO films. The results showed that the degree of reduction was in the order L-ascorbic acid ${\geq}$ hydrazine > glucose. GO reduced using L-ascorbic acid had a sheet resistance of $121k{\Omega}/sq$, while that reduced using gluconic acid showed worse electrical properties than the other two reduction agents. Therefore, L-ascorbic acid is the most suitable eco-friendly reduction agent that can be substituted for hydrazine.

• Carbon letters
• /
• v.16 no.1
• /
• pp.41-44
• /
• 2015

We report the preparation of sulfonated reduced graphene oxide (SRGO) by the sulfonation of graphene oxide followed by radiation-induced chemical reduction. Graphene oxide prepared by the well-known modified Hummer's method was sulfonated with the aryl diazonium salt of sulfanilic acid. Sulfonated graphene oxide (SGO) dispersed in ethanol was subsequently reduced by ${\gamma}$-ray irradiation at various absorbed doses to produce SRGO. The results of optical, chemical, and thermal analyses revealed that SRGO was successfully prepared by ${\gamma}$-ray irradiation-induced chemical reduction of the SGO suspension. Moreover, the electrical conductivity of SRGO was increased up to 2.94 S/cm with an increase of the absorbed dose.