• The korean journal of orthodontics
• /
• v.28 no.5 s.70
• /
• pp.877-891
• /
• 1998

This study was designed to observe the effects of various concentration of polyacrylic acid containing different concentration of sulfate ion on the crystal formation on the enamel surface. Experimental crystal growth solutions were made of $10\%,\;20\%,\;30\%\;and\;40\%$ polyacrylic acid(molecular weight,5,000) solutions which containing 0.1M, 0.2M, 0.3M, 0.5M, and 1.0M sulfate ion respectively. The extracted human first bicuspid enamel surface was contacted for n seconds with these solutions, washed for 15 seconds, dried, and then the crystal topography on the enamel surface was observed under the scanning electron microscope. The crystal topography were evaluated on the SEM photographs by degree of crystal coverage, crystal length, and consistency of crystal morphology, and conclusions were as the follows. 1. Polyacrylic acid solution etched slightly the enamel surface, and the difference of etching effect by its concentration was not observed. 2. The effect of concentration of polyacrylic acid on the crystal formation was less, especially that of $20\%\~40\%$ polyacrylic acid was almost not different. 3. Concentration of the sulfate ion was a determinant factor in precipitating crystals on the enamel. The experimental crystal growth solutions containing 0.1 M sulfate ion did not make crystal formation but those containing over 0.2 M sulfate ion did. 4. The degree of crystal coverage showed a tendency to increase and then decrease according to the concentration of sulfate ion in the $20\%-40\%$ polyacrylic acid. The experimental solutions containing 0.5 M sulfate ion showed the peak of degree of crystal coverage. 5. The crystal length showed a tendency to decrease by increment of sulfate ion in the polyacrylic acid solution. 6. There was a tendency to increase the frequency of random arragement of short crystals when increasing the concentration of sulfate ion in the polyacrylic acid solution. The lower concentration of sulfate ion in the polyacrylic acid solutions tended to make spherulitic arrangement of crystals, the higher concentration of sulfate ion, the more random arrangement of crystals. The experimental solutions containing 0.5M sulfate ion showed more spherulitic arrangement than random arrangement of crystals. 7. The best one of these experimental crystal growth solutions was $30\%$ polyacrylic acid solution containing 0.5M sulfate ion.

• Korean Chemical Engineering Research
• /
• v.52 no.3
• /
• pp.382-387
• /
• 2014

The PC/ABS blends were manufactured with high shear rate processing. Changes of the blend morphology were analyzed according to the screw speed and processing time. To find optimal conditions of the high shear rate processing of the PC/ABS blend, blend morphology and size of the dispersed phase, ABS, were observed with a SEM. Also, tensile properties of the PC/ABS blends were measured to investigate the effect of the high shear rate process with the screw speed of 500 rpm to 3000 rpm for processing times of 10s to 40s. Especially, to observe the dispersed phase of the PC/ABS blend clearly, fracture surfaces of the PC/ABS blend were etched with chromic acid solution. As screw speed and processing time increase, dispersed phase size of the PC/ABS blend decreases and mechanical properties of the blend decrease as well. Especially, at screw speed over than 1000 rpm of high shear rate processing, mechanical properties of the PC/ABS blends decrease drastically due to the degradation of the blend during the high shear rate processing. Consequently, the optimal condition of screw speed of the high shear processing of the PC/ABS blend is set at 1000rpm, in this study. Under optimal condition, the PC/ABS blend has relatively high mechanical properties with the relatively stable micro-structure having nanometer scale dispersed phase.