• 대한치과보철학회지
• /
• 제43권5호
• /
• pp.684-693
• /
• 2005

Statement of problem: Ti-6Al-7Nb alloy is used instead of Ti-6Al-4V alloy that was known to have toxicity. Purpose: This study was performed to investigate the effect of electrolyte concentration on the surface characteristics of anodized and hydrothermally-treated Ti-6Al-7Nb alloy Materials and methods: Discs of Ti-6Al-7Nb alloy of 20 mm in diameter and 2 mm in thickness were polished sequentially from #300 to 1,000 SiC paper ultrasonically washed with acetone and distilled water for 5 min, and dried in an oven at $50^{\circ}C$ for 24 hours. Anodizing was performed at current density $30mA/cm^2$ up to 300 V in electrolyte solutions containing $\beta-glycerophosphate$ disodium salt hydrate $(\beta-GP)$ and calcium acetate (CA). Hydrothermal treatment was conducted by high pressure steam at $300^{\circ}C$ for 2 hours using a autoclave. All samples were soaked in the Hanks' solution with pH 7.4 at $36.5^{\circ}C$ for 30 days. Results and conclusion: The results obtained were summarized as follows: 1. After hydrothermal treatment, the precipitated HA crystals showed the dense fine needle shape. However, with increasing the concentration of electrolyte they showed the shape of thick and short rod. 2. When the dense fine needle shape crystals was appeared after hydrothermal treatment, the precipitation of HA crystals in Hanks' solution was highly accelerated. 3. The crystal structures of $TiO_2$ in anodic oxide film were composed of strong anatase peak and weak rutile peak as analyzed with thin-film X-ray diffractometery. 4. The Ca/P ratio of the precipitated HA layer was equivalent to that of HA crystal in Hanks' solution.

• 대한수의학회지
• /
• 제30권1호
• /
• pp.15-27
• /
• 1990

Effects of oral administration of electrolyte solutions were studied in experimentally dehydrated adult sheep. By the latin square method five ruminal fistulated sheep were examined and dehydrated by deprivation of feed and water for 72 hours. Tap water, physiological saline, 0.45% NaCl+120 mM/L glucose and 0.9% NaCl+1% propylene glycol solution were orally administrated after dehydration, respectively. Rehydration effect and modification of the rumen function were compared. 1. After 72 hours of deprivation of feed and water, sheep were hypertonic dehydrated and blood acid-base parameters were not significantly changed. And there was marked increase in ruminal pH and decrease in ruminal total volatile fatty acid(VFA) concentration. 2. After the fluids administration the changes in blood acid-base parameters were not significant in all groups. 3. Although glucose fermentation in the rumen was observed, 0.45% NaCl+120 mM/L glucose was more effective in rehydration than physiological saline and tap water. But it was difficult to know the rehydration effect of 0.9% NaCl+1% propylene glycol solution exactly because of excessive increase in plasma osmolality. 4. After refeeding, total concentration and proportions of ruminal volatile fatty acid(VFA) were not significantly different among groups and recovered to normal concentration but not in proportions after 2 days in all groups. 5. In vitro cultured ruminal protozoa were susceptible to the decrease of the pH and osmolality.

• 한국재료학회지
• /
• 제14권9호
• /
• pp.607-613
• /
• 2004

This study was to investigate the surface properties of electrochemically oxidized Ti-6Al-7Nb alloy by anodic spark discharge technique. Anodizing was performed at current density 30 $mA/cm^2$ up to 300 V in electrolyte solutions containing $DL-{\alpha}$-glycerophosphate disodium salt hydrate($DL-{\alpha}$-GP) and calcium acetate (CA). Hydrothermal treatment was done at $300^{\circ}C$ for 2 hrs to produce a thin outermost layer of hydroxyapatite (HA). The bioactivity was evaluated from HA formation on the surfaces in a Hanks' solution with pH 7.4 at $36.5^{\circ}C$ for 30 days. The size of micropores and the thickness of oxide film increased and complicated multilayer by increasing the spark forming voltage. Needle-like HA crystals were observed on anodic oxide film after the hydrothermal treatment at $300^{\circ}C$ for 2 hrs. When increasing $DL-{\alpha}$-GP in electrolyte composition, the precipitated HA crystals showed the shape of thick and shorter rod. However, when increasing CA, the more fine needle shape HA crystals were appeared. The bioactivity in Hanks' solution was accelerated when the oxide films composed with strong anatase peak with presence of rutile peak. The increase of amount of Ca and P was observed in groups having bioactivity in Hanks' solution. The Ca/P ratio of the precipitated HA layer was equivalent to that of HA crystal and it was closer to 1.67 as increasing the immersion time in Hanks' solution.