• Elastomers and Composites
• /
• 제52권2호
• /
• pp.105-113
• /
• 2017

The curing behavior, mechanical properties, hot-air aging resistance, abrasion properties,thermal properties, etc., of EVM/EPM/APP (ammonium polyphosphate)/DPER (dipentaerythritol)/EG (expandable graphite) and EVM/EPM/ATH (aluminium trihydroxide) flame retarding systems in ethylene vinyl acetate rubber (EVM) blends with EPM (ethylene propylene rubber) were sequentially examined. For both flame retarding systems, the torque values increased with the content of EPM rubber and with the vulcanization time. As the content of EPM rubber increased, the scorch time became shorter, whereas the optimum cure time followed an increasing trend. For the EVM/EPM/APP/DPER/EG flameretarding system, as the content of EPM rubber increased, the hardness did not change,whereas the tensile strength and elongation at break decreased. A hot-air aging resistance test at $150^{\circ}C$ showed that the heat resistance decreased with the EPM content regardless of the kinds and contents of flame retardants. As the EPM content increased, the abrasion rate became higher and the abrasion resistance of the EVM/EPM/APP/DPER/EG flame retarding systems exceeded that of the EVM/EPM/ATH flame retarding counterparts. In comparison with the EVM/EPM/ATH flame retarding systems, the thermal stability of the EVM/EPM/APP/DPER/EG flame retarding system showed an increasing tendency.

• 폴리머
• /
• 제25권2호
• /
• pp.233-239
• /
• 2001

Mechanical mixing법으로 ethylene propylene diene terpolymer (EPDM)과 ethylene propylene diene terpolymer (EPDM)과 acrylonitrile butadiene rubber (NBR) 블렌드 혼련물을 제조하여, 이들의 무늬 점도, 가교 거동, 영구 압축 줄음율 및 동적 기계적 성질 등을 검토하였다. Rheovibron에 의한 동적 특성 측정의 결과로부터 EPDM/NBR 블렌드는 -43$^{\circ}C$ 및 -4$^{\circ}C$ 부근에서 두 개의 전이를 보였으며 이를 각각 NBR 고무 및 EPDM 고무의 T$_{g}$로 해석하였다. tan${\delta}$ 피크의 위치는 NBR 고무의 함량이 증가함에 따라 고온 쪽으로 이동함을 확인할 수 있었다. 또한 NBR 고무량이 증가할수록 최적 가황시간이 단축되는 경향을 보였다.

• Elastomers and Composites
• /
• 제47권3호
• /
• pp.254-258
• /
• 2012

자동차 엔진 개스킷용 아크릴 고무(ACM)의 재료 특성과 수명 예측에 관하여 연구하였다. 클로린 가교사이트를 포함하는 ACM (Chlorine Cure-Site ACM)과 카르복실기 가교사이트를 포함하는 ACM (Carboxyl Cure-Site ACM)을 이용하여 최적상태의 배합물을 제작하여 특성을 살펴보았다. 엔진용 개스킷의 주요한 특성인 열과, 엔진오일에서의 압축영구줄음율을 시험 평가한 결과 Carboxyl Cure-Site ACM 배합물이 상대적으로 더 우수한 것으로 나타났다. Carboxyl Cure-Site ACM 고무 재료에 대한 수명을 예측하기 위해 가속열노화시험을 수행하여 시간-온도 환산식인 아레니우스(Arrhenius) 관계식을 구하였다.

• Elastomers and Composites
• /
• 제53권3호
• /
• pp.168-174
• /
• 2018

Natural rubber (NR) and bromo-isobutylene-isoprene rubber (BIIR) were compounded with other formulation chemicals through polymer blending via a mechanical mixing method. After rubber vulcanization by hot-press compression molding, the cure characteristics, mechanical properties, and ozone resistance of the NR/BIIR blends were measured. As the BIIR content increased, the maximum torque of the blends decreased, while the optimum cure time and scorch time tended to increase. Furthermore, the hardness of the blends increased with increasing BIIR content, reaching the maximum value at 75 wt% BIIR, and decreased with a further increase in the BIIR loading. The tensile strength and elongation at break decreased with an increase in the BIIR content, reaching the minimum value at 75 wt% BIIR, and increased with a further increase in the BIIR content. In the ozone resistance test, cracks were not generated when the BIIR content was more than 75 wt%.

• 한국의류학회지
• /
• 제28권11호
• /
• pp.1507-1515
• /
• 2004

Washable wool was developed using environmental-friendly spray UV-cure technique. Photocrosslinkable polymer, dextran-methacrylate, was synthesized starting from natural biopolymer, dextran. The aqueous solution of dextran-methacrylate was applied to wool fabric with various concentrations to find out the optimum condition in minimizing felting shrinkage. The wool fabric subsequently cured by 365 nm UV, The effects of UV-cure time and photoinitiator concentration on felting behavior of wool were examined. As the concentration of dextran-methacrylate increased, the felting shrinkage decreased gradually. At concentration 0.5g/ml, the felting shrinkage of wool was negligible. Other properties such as air permeability, moisture content, wrinkle recovery, thickness and wettability were also evaluated. The surface coating of dextran polymer onto wool fiber was identified by SEM.

• Elastomers and Composites
• /
• 제45권1호
• /
• pp.44-50
• /
• 2010

기계적 혼련법으로 butadiene rubber(BR)과 대표적인 결정성고무인 chloroprene rubber(CR) 블렌드 혼련물을 제조하여, 이들의 가교 거동, 기계적 성질, 내오존성 및 동적 기계적 성질 등을 검토하였다. 내오존시험에 있어서 50 wt% CR 고무의 첨가에 의하여 크게 개선됨을 확인할 수 있었다. Rheovibron에 의한 동적 계적 특성 측정의 결과로부터 BR/CR 블렌드는 두 개의 전이를 보였으며 $tan{\delta}$ 피이크의 위치는 CR 고무의 함량이 증가함에 따라 고온 쪽으로 이동함을 확인할 수 있었다. 한편 CR 고무량이 증가할수록 최적 가황시간이 증가하는 경향을 보였다.

• Elastomers and Composites
• /
• 제50권2호
• /
• pp.87-91
• /
• 2015

Cure characteristics of non-oil-extended solution SBR (S-SBR_NO) and oil-extended solution SBR (S-SBR_ EO) compounds reinforced with silica/carbon black were investigated. Minimum and maximum torques of S-SBR_ EO compounds were much smaller than those of S-SBR_NO ones. Delta torques of S-SBR_NO compounds were greater than those of S-SBR_EO ones, and that of S-SBR_NO compound increased with increase in the 1,2-unit content. Optimum cure time ($t_{90}$) of S-SBR compound decreased with increase in the 1,4-unit content, whereas it increased with increase in the 1,2-unit content. Cure rate index of S-SBR compound increased with increase in the 1,4-unit content, whereas it decreased with increase in the 1,2-unit content. Comparing cure characteristics of S-SBR_NO and S-SBR_EO compounds with the same 1,2-unit content, $t_{90}$s of S-SBR_EO compounds were longer than those of S-SBR_NO ones and cure rate indices of S-SBR_EO compounds were smaller than those of S-SBR_NO ones.

• Elastomers and Composites
• /
• 제31권1호
• /
• pp.33-42
• /
• 1996

NR, NBR, and CR rubber were prepared by mixing filler in various ratios. Their vulcanization characteristics and thermal properties were studied. Vulcanization characteristics were investigated using cure curve that had been obtained from oscillating disk rheometer study. The Arrhenius law is known to describe the relationship between cure time and temperature of most elastomers. Curing could be done by the addition of sulfur, peroxides, and proper acceleratores. The optimum cure time that affects desirable values of modulus and tensile strength of the vulcanizate is taken as t90 as measured by a rheometer. Rubbers were cured in the rheometer at temperatures ranging from $130^{\circ}C\;to\;180^{\circ}C$ in order to check the validity of the curing system used. A linear relationship between ln(ts2) and ln(t90) was found for all elastomers. The term sensitivity has been used to describe the relationship between a change of ts2 to the corresponding change of t90 due to an increment of temperature. This is related to the formula of the compound.

• Elastomers and Composites
• /
• 제43권2호
• /
• pp.104-112
• /
• 2008

통상적인 고무블렌드 방법에 따라 개방식 2-롤밀을 사용하여 ethylene propylene diene terpolymer (EPDM)과 styrene butadiene rubber (SBR) 블렌드 배합물을 제조하여, 이들의 경화 특성, 기계적 성질 및 내오존성 등을 검토하였다. SBR함량이 증가할수록 가황곡선의 토크가 증가하였다. 최대 토크는 SBR 25wt% 일 때 가장 낮았으며 그 이상의 SBR 량에서는 직선적으로 증가하였다. 스코치시간 및 최적경화시간은 SBR고무 함량이 증가함에 따라 감소하였다. 경도는 SBR 함량이 50wt% 일 때 최고값을 보였으며 그 전후에서는 감소하는 경향을 보였다. 내오존시험에 있어서 소량의 EPDM 고무의 첨가에 의하여 내오존성이 크게 개선됨을 확인할 수 있었다.

• 공업화학
• /
• 제10권3호
• /
• pp.419-426
• /
• 1999

가황고무의 가황반응에 대하여 가황시스템 및 온도, 보강성충전제 첨가량 변화에 의한 반응속도상수 및 활성화에너지, 가교밀도 및 탄성상수, 가황특성 ($t_5,\;t_{90}$), 고무보강성 및 내마모성을 고찰하였다. 반응속도상수는 보강성충전제 첨가량, 가황시스템 및 가황반응온도에 대한 의존성이 크게 나타났으며, 반응온도에 따라 지수적으로 증가하였다. 활성화에너지는 가황시스템중 촉진제에 대한 황 비율이 높은 가황시스템에서 가장 작게 나타났으며, 보강성충전제 첨가량이 적을수록 작게 나타났다. 카본블랙 첨가량 변화는 고무보강성 및 내마모성에 직접적으로 영향을 미치고 있으나, 가황시스템 변화는 각기 다른 영향이 나타났다. 카본블랙 첨가량이 증가하면 모듈러스가 증가하고, 내마모성이 향상되며, 스코치시간이 짧아졌으나, 가교밀도 및 탄생상수는 감소하였다. 높은 가교밀도 및 탄성상수는 카본블랙 첨가량에 관계없이 촉진제에 대한 황 비율 0.73 (${\fallingdotseq}1$)에서 나타났으며, 스코치시간 ($t_5$)은 촉진제에 대한 황 비율 변화에 거의 영향을 받지 않는 것으로 나타났다. 빠른 최적가황시간 ($t_{90}$) 역시 촉진재에 대한 황 비율이 1에 가까운 조건 (=0.73)에서 나타났다. 가황조건별 배합고무의 등가 가황곡선계수는 카본블랙 첨가량에 관계없이 CC 시스템에 대해서는 0.96, SEC 및 EC 시스템에 대해서는 0.74로 나타났다. 한편 가황고무의 마모된 부피는 부과된 하중이 증가함에 따라 지수적으로 증가하였다.