• Tribology and Lubricants
• /
• v.35 no.2
• /
• pp.139-147
• /
• 2019

This study investigates the effects of corrosion resistance characteristics of opponent materials in relative motion on the sliding wear behavior of mild carbon steel. Pin specimens made of mild carbon steel are tested at several sliding speeds against mating discs made of two types of alloyed steels, such as type D2 tool steel (STD11) and type 420 stainless steel (STS420J2), with different corrosion resistance characteristics in a pin-on-disc type sliding wear test machine. The results clearly show that the sliding wear behavior of mild carbon steel is influenced by the corrosion resistance characteristics of the mating disc materials at low sliding speeds. However, the sliding wear behavior at high sliding speeds is irrelevant to the characteristics because of the rising temperature. During the steady state wear period, the sliding wear rate of mild carbon steel against the type 420 stainless steel at a sliding speed of 0.5 m/s increases considerably unlike against the type D2 tool steel. This may be because the better corrosion resistance characteristics achieve a worse tribochemical reactivity. However, during the running-in wear period at low sliding speeds, the wear behavior of mild carbon steel is influenced by the microstructure after heat treatment of the mating disc materials rather than by their corrosion resistance characteristics.

• Journal of Korean Ophthalmic Optics Society
• /
• v.4 no.2
• /
• pp.65-71
• /
• 1999

The optical absorption spectrum was measured of the tinted powder, tinted solution and tinted lens in the visible regions. The tinted powder was very different with color of tinted lens that the optical absorptions was so higher, composed of the thick-gray color. The optical absorptions of tinted solution were just a little appeared by the energy split of a transition metal ion, so constructed with each color space. The optical absorptions of the tinted lens were appeared with the energy split peaks to a transition metal ion, so its were affected by the color constructions. The optical absorption peaks of each lens were depend on the tinted time. Blue color lens had a lot of absorption in the short wavelength regions than 500nm, and had a little appeared in the high wavelength regions than 500nm. In case of a yellow color, the optical absorptions were appeared quite contrary to the blue color, so these colors had the opponent-colors each other. In case of green color, the optical absorptions had a high in the both edges, had a low in the middle regions. In the pink color, by the optical absorptions form of quite contrary to the green color it, these colors had the opponent-colors each other. In the brown color, the optical absorptions had a maximum values in the short wavelength regions, and it gradually decreased goes by the long wavelength regions.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.10
• /
• pp.1117-1123
• /
• 2014

This study sintered $Si_3N_4$ with different amounts of $SiO_2$ nano-colloid. The surface of a mirror-polished specimen was coated with $SiO_2$ nano-colloid, and cracks were healed when the specimen was treated at a temperature of 1273 K for 1 h in air. Wear specimen experiments were conducted after heat treatments for 10 min at 1073, 1273, and 1573 K. The heat-treated surface that was coated with the $SiO_2$ nano-colloid was slightly rougher than the noncoated surface. The oxidation state of the surface according to the heat treatment temperature showed no correlation with the surface roughness. Moreover, the friction coefficient, wear loss, and bending strength were not related to the surface roughness. $Si_3N_4$ exhibited an abrasive wear behavior when SKD11 was used as an opponent material. The friction coefficient was proportional to the wear loss, and the bending strength was inversely proportional to the friction coefficient and wear loss. The friction coefficient and wear loss increased with increasing amounts of the $SiO_2$ nanocolloid. In addition, the friction coefficient was slightly increased by increasing the heat treatment temperature.