• Journal of Surface Science and Engineering
• /
• v.30 no.3
• /
• pp.167-174
• /
• 1997

WC-C0 base cemented carbides were plasma nitrided to obtain more hadened surface layer. The surface hardness of Hv1338 which is higher than a non-treated ane by 30%, and the hardened layer thickness of about 50$\mu\textrm{m}$ were obtained by the treatment of 3hrs under the conditions of $550^{\circ}C$, and 5torr of gas pressure of which composition was 1:1 of $N_2:H_2$. The nitrided surfaces has WIN and W2N phases in the non-coated samples and AIN phase in the alumina coated sampled as the results of X-ray results, and showed surface roughnness of 5$\mu\textrm{m}$ which were caused by the sputtering action of the plasma gasee. The hardenened layer exihibits an enhanced wear resistance the cuttability test.

• Korean Journal of Materials Research
• /
• v.12 no.6
• /
• pp.427-430
• /
• 2002

Plasma nitrocarburizing treatment was performed for SCM 435 steel by using a plasma ion nitriding system. The effects of the variation of nitrogen and methan contents upon the hardened layer was investigated. Both the thickness of the compound layer and the amount of $\varepsilon$ phase in the compound layer increased with increasing nitrogen content. However, the thickness of the compound layer decreased due to unstable plasma for an atmosphere containing 90% $N_2$ gas content in the gas mixture. The amount of $\varepsilon$phase in the compound layer increased with increasing $CH_4$ gas content. For $CH_4$ gas content more than 2% in the gas mixture, the thickness of the compound layer decreased due to the formation of $\theta$ phase.

• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.71-76
• /
• 2013

Gas nitriding is a surface hardening process where nitrogen is introduced into the surface of a ferrous alloy. During fusion welding of nitrided carbon steel, the nitride inside weld metal is dissolved and generates nitrogen gas, which causes porosities - blow holes and pits. In this study, several laser welding processes such as weaving welding, two-pass welding, dual beam welding and laser-arc hybrid welding were investigated to elongate the weld pool to enhance nitrogen gas evacuation. The surface pits were successfully eliminated with elongated weld pool. However blowholes inside the weld metal were effective reduced but not fully disappeared.

• Korean Journal of Materials Research
• /
• v.19 no.9
• /
• pp.457-461
• /
• 2009

Recently, metal molding has become essential not only for automobile parts, but also mass production, and has greatly influenced production costs as well as the quality of products. Its surface has been treated by carburizing, nitriding and induction hardening, but these existing treatments cause considerable deformation and increase the expense of postprocessing after treatment; furthermore, these treatments cannot be easily applied to parts that requiring the hardening of only a certain section. This is because the treatment cannot heat the material homogeneously, nor can it heat all of it. Laser surface treatment was developed to overcome these disadvantages, and, when the laser beam is irradiated on the surface and laser speed is appropriate, the laser focal position is rapidly heated and the thermal energy of surface penetrates the material after irradiation, finally imbuing it with a new mechanical characteristic by the process of self-quenching. This research estimates the material characteristic after efficient and functional surface treatment using HPDL, which is more efficient than the existing CW Nd:YAG laser heat source. To estimate this, microstructural changes and hardness characteristics of three parts (the surface treatment part, heat affect zone, and parental material) are observed with the change of laser beam speed and surface temperature. Moreover, the depth of the hardened area is observed with the change of the laser beam speed and temperature.

• Journal of Advanced Marine Engineering and Technology
• /
• v.36 no.1
• /
• pp.78-84
• /
• 2012

Mold may experience deterioration of molding quality as the abrasion of mold occurring due to friction between mold and molded product works as allowance in the course of press process. Therefore, to improve the wear-resistance of mold, methods like nitriding, carburizing, flame and induction surface hardening treatment etc have been applied. However, as such methods are accompanied by problems like shape limitation or product deformation etc, laser surface treatment technology is under review as surface treatment method that can solve such problems. Therefore, in this study, mold material cast iron was surface-treated by using high power diode laser. In previous report 1 and report 2, the heat treatment characteristics were compared by the differences of die materials and shapes, then this paper observed microstructure by using optical microscope and scanning electronic microscope to analyze the structural difference of hardened zone, interface area and base metal after heat treatment. And the structural condition was grasped through EDS. As a result of microstructure, hardened zone showed formation of acicular martensite.

• Journal of Advanced Marine Engineering and Technology
• /
• v.35 no.5
• /
• pp.600-607
• /
• 2011

Recently, high carbon steel has become essential not only for shipbuilding parts, but also mass production. Its surface has been treated by carburizing, nitriding and induction hardening, but these existing treatments cause considerable deformation and increase the expense of postprocessing after treatment; furthermore, these treatments cannot be easily applied to parts that requiring the hardening of only a certain section. This is because the treatment cannot heat the material homogeneously, nor can it heat all of it. Laser surface treatment was developed to overcome these disadvantages, and when the laser beam is irradiated on the surface and laser speed is appropriate, the laser focal position is rapidly heated and the thermal energy of surface penetrates the material after irradiation, finally imbuing it with a new mechanical characteristic by the process of self-quenching. This research estimates the material characteristic after efficient and functional surface treatment using HPDL, which is more efficient than the existing CW Nd:YAG laser heat source. To estimate, microstructural changes and hardness characteristics of two parts (the surface treatment part, and parental material) are observed with the change of laser beam speed and surface temperature.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.2
• /
• pp.57-64
• /
• 2002

The 22%Cr-5%Ni-3%Mo duplex and 18%Cr-8%Ni austenitic stainless steels have been nitrogen permeated under the $1Kg/cm^2$ nitrogen gas atmosphere at the temperature range of $1050^{\circ}C{\sim}1150^{\circ}C$. The nitrogen-permeated duplex and austenitic stainless steels showed the gradual decrease in hardness with increasing depth below surface. The duplex stainless steel showed nitrogen pearlite at the outmost surface and austenite single phase in the center after nitrogen permeation treatment, while the obvious microstructural change was not observed for the nitrogen-permeated austenitic stainless steel. After solution annealing the nitrogen-permeated stainless steels(NPSA treatment) at $1200^{\circ}C$ for 10 hours, the hardness of the duplex and austenitic stainless steels was constant through the 2 mm thickness of the specimen, and the ${\alpha}+{\gamma}$ phase of duplex stainless steel changed to austenite single phase. Tensile strengths and elongations of the NPSA-treated duplex stainless steel remarkably increased compared to those of solution annealed (SA) duplex stainless steel due to the solution strengthening effect of nitrogen and the phase change from a mixture of ferrite and austenite to austenite single phase, while the NP-treated austenitic stainless steel displayed the lowest value in elongation due to inhomogeneous deformation by the hardness difference between surface and interior.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.4
• /
• pp.1-14
• /
• 1991

In PECVD(Plasma-Enhanced Chemical Vapor Deposition) process, titanium nitride is thin and its adhesion is poor for the protective coatings. Therefore it has been studied that intermediate layer forms between substrate and TiN thin film. Using R.F. plasma nitriding, nitride layer was first formed, then TiN thin film coated by PECVD. The chemical composition of the coatings has been characterized using AES, EDS and their crystallographic structure by means of XRD. Mechanical properties such as microhardness and film adhesion have also been determined by vickers hardness test, scratch test and indentation test. As a result, there was no difference in chemical composition and structure between the TiN deposition only and the composite of TiN deposition on nitrided steel. It was found that nitrided substrate increased the hardness of TiN coatings and was beneficial in preventing the plastic deformation in the substrate. Therefore the effective load bearing capacity of the TiN coatings on nitrided steel was increased and their adhesion was improved as well. According to the results of this study, the processes that lead to the formation of composite layers characterized by good working properties, i.e., high microhardness, adhesion and resistance to deformation.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.3
• /
• pp.177-185
• /
• 1998

The purpose of this research is to investigate the effects of Co, Co-Ti addition on the sintering characteristic of $(Ti_{1-x}Alx)N$ material synthesized by the direct nitriding method for a application as a cermet material. The observed shrinkage rates of $(Ti_{1-x}Alx)N$ pellets increase with the additive (Co, Co-Ti) content, temperature and time, and also the pellets with the same additive content exhibit the shrinkage behavior that depends on the Ti/Al ratio. However, although the shrinkage rates in this study is the mast higher (36%), the density of the sintered $(Ti_{1-x}Alx)N$ pellet is below 80% density in theory because of the partial segregation and the dense band defect of AlCo compound. Consequentely, it is considered that Co was not effective as a binder material because the wettability of liquid Co metal on $(Ti_{1-x}Alx)N$ materials is poor, In $(Ti_{1-x}Alx)N$ with Ti-Co additive, the stoichiometric TiN is transformed by the under-stoichiometric TiNx(x<1.0) during sintering, leading to the good properties such as hardnees and hot oxidation.

• 연구논문집
• /
• s.28
• /
• pp.219-227
• /
• 1998

In order to investigate the interfacial structure between TiN and iron nitride, an AISI 4140 steel was nitrided to form a layer of thickness 15$\mum$ by DC ion nitriding, then the surface was bombarded with Ti ions and subsequently coated a TiN film of 5$\mum$ by arc ion plating method. The interfacial microstructure between TiN and iron nitride was characterized by optical microscope, SEM and XRD. So called black layer was observed in the duplex treatment. It was resulted from the decomposition of iron nitride during the bombardment. Its thickness was increased with increasing bombardment time at high bias voltage. But the thickness was greatly decreased when the iron nitride was bombarded with a nitrogen gas or at a reduced bias voltage. The adhesion strength of the top TiN coating was decreased with increasing thickness of the black layer. Furthermore, the reduced adhesion strength in this system was discussed in view of the interfacial structural relationship between TiN and iron nitride.