• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.248.1-248.1
• /
• 2014

We present results from an experimental study of conductivity change of poly (3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) film according to the surface structuring. We demonstrate that the patterned structure was enhanced with approximately five times conductivity in comparison with non structure of PEDOT:PSS film. In order to patterning, we have fabricated polystyrene (PS) colloidal monolayer as a template with sphere diameter of 780nm and 1.8um. Structure has honeycomb shape and it provide shorter path way to flowing of electron. Pattern size was controlled by PS diameter and varied by Transformer Coupled Plasma (TCP) etching system. Conductivity was converted from sheet resistance which measured by 4-point prove. Film thickness was derived using Field Emission Scanning Electron Microscopy (FE-SEM) images.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.85.2-85.2
• /
• 2018

금속 나노구조체에서의 localized surface plasmon resonance와 surface-enhanced Raman scattering 현상은 센서를 비롯한 다양한 응용분야를 가지고 있다. 나노구조체 array 형성을 위한 대표적인 top-down 방식인 e-beam lithography 공정은 제조비용이 매우 높고 대량생산 및 대면적화에도 한계가 있기에 polystyrene(PS) bead의 self-assembly를 이용한 nanosphere lithography와 같은 bottom-up 방식이 폭넓게 연구되고 있다. Closed-packing된 PS bead의 monolayer를 얻기 위해서는 기판의 친수성 처리가 필요한데, 기존의 많은 연구에서는 기판의 표면개질에 화학적 공정을 이용하고 있다. 하지만 이는 기판 선택의 자유도를 떨어뜨리는 원인이 된다. 금속이나 실리콘 기판에서는 산성 용액을 이용한 화학적 처리방법을 적용할 수 있지만 SU-8과 같은 감광액 및 폴리머 기판에서는 산에 대한 내구성이 떨어져 화학적 공정의 도입이 불가능 하기 때문이다. 본 연구에서는 이러한 한계점을 극복하기 위해 $UV-O_3$ 공정으로 친수성 처리된 다양한 기판에서 spin coating을 통한 PS monolayer를 제조하였는데, UV 램프의 에너지 조절을 통해 기판에 붙어있는 유기물들을 효과적으로 제거할 수 있었고 $O_3$ 생성 및 분해 과정에서 기판 표면에 친수성 화학 작용기를 생성시킬 수 있었다. 제조된 PS layer를 mask로 사용하여 Ag, Al, Au 등 다양한 나노구조체 array를 형성하여 array 주기에 따른 플라즈몬 공명 특성을 분석하였다. 레이저 조사로 나노구조체의 형상을 변화시킴으로써 동일한 물질과 주기를 가진 array에서도 플라즈몬 특성의 변조가 가능함을 확인하였는데, 이는 금속 나노구조체의 응용측면에서 매우 고무적인 발견이다.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.10
• /
• pp.2280-2282
• /
• 2009

Amorphous zinc phosphate nanospheres were prepared via a sonochemical route. Zinc phosphate nanospheres were uniform in shape with an average diameter of 210 nm. The average diameter of nanospheres could be controlled by changing the pH of a precursor solution. This sonochemical method is simple, facile, economical, and environmentally benign. Non-crystalline characteristics of as-prepared zinc phosphate nanospheres were confirmed by X-ray diffraction, transmission electron microscopy, and FT-IR spectroscopy analyses. We believe this technique will be readily adopted in realizing other forms of zinc phosphate nanostructures.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.4
• /
• pp.999-1003
• /
• 2010

Raman spectra of a single layer graphene sheet placed in different gold substrates were obtained and are discussed in the context of surface enhanced Raman scattering (SERS). The gold substrates were composed of a combination of a thermally deposited gold film and a close-packed gold nanosphere layer. The SERS effects were negligible when the excitation wavelength was 514 nm, while the Raman signals were enhanced 3-to 50-fold when the excitation wavelength was 633 nm. The large SERS enhancement accompanied a spectral distortion with appearance of several unidentifiable peaks, as well as enhancement of a broadened D peak. These phenomena are interpreted as the local field enhancement in the nanostructure of the gold substrates. The difference in the enhancement factors among the various gold substrates is explained with a model in which the spatial distribution and polarization of the local field and the orientation of the inserted graphene sheet are considered important.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.90.2-90.2
• /
• 2013

Vertically-aligned silicon nanostructure arrays (SNAs) have been drawing much attention due to their useful electrical properties, large surface area, and quantum confinement effect. SNAs are typically fabricated by chemical vapor deposition, reactive ion etching, or wet chemical etching. Recently, metal-assisted chemical etching process, which is relatively simple and cost-effective, in combination with nanosphere lithography was recently demonstrated for vertical SNA fabrication with controlled SNA diameters, lengths, and densities. However, this method exhibits limitations in terms of large-area preparation of unperiodic nanostructures and SNA geometry tuning independent of inter-structure separation. In this work, we introduced the layerby- layer deposition of polyelectrolytes for holding uniformly dispersed polystyrene beads as mask and demonstrated the fabrication of well-dispersed vertical SNAs with controlled geometric parameters on large substrates. Additionally, we present a new means of building in vitro neuronal networks using vertical nanowire arrays. Primary culture of rat hippocampal neurons were deposited on the bare and conducting polymer-coated SNAs and maintained for several weeks while their viability remains for several weeks. Combined with the recently-developed transfection method via nanowire internalization, the patterned vertical nanostructures will contribute to understanding how synaptic connectivity and site-specific perturbation will affect global neuronal network function in an extant in vitro neuronal circuit.

• Polymer(Korea)
• /
• v.29 no.6
• /
• pp.613-616
• /
• 2005

In this word as the first step to develop optical biosensors for a single cell level analysis, the preparation method of nano-scale polymer hydrogel spheres containing an enzyme was set up and the feasibility of the spheres as optical biosensors was investigated. The horseradish peroxidase (HRP) was encapsulated in the PEG hydrogel spheres by suspension photopolymerization, yielding spheres of the average size of 305 nm. After the polymerization, the incorporation and activity of HRP within the spheres were determined by the production of fluorescence resulted from the enzymatic reaction between HRP and $\H_{2}O_{2}$. The fluorescence emission response of the HRP-loaded PEG hydrogel spheres increased by nearly 300$\%$ as hydrogen peroxide concentration was changed from 0 to 11 nM in the presence of Amplex Red. The results suggest that the method to prepare the PEG hydrogel nanospheres containing an enzyme could be used for developing optical biosensors to measure various analytes in the very small samples like a single cell.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.256-256
• /
• 2015

이산화 바나듐 ($VO_2$)은 340 K 임계온도를 기점으로 금속-절연체 상전이를 통해 전기적, 광학적 특성이 가역적으로 변하는 물질로 잘 알려져 있다. 그러나 낮은 가시광 투과율과 비선호적인 색상(황갈색)으로 인해 열변색 스마트 창호응용과 관련하여 해결해야 할 문제로 남아있다. 본 연구에서는 상기 문제를 해결하고자 고분자 나노 구 템플릿을 응용하여 2차원의 벌집구조를 갖는 $VO_2$ 박막을 졸 겔 방법을 통해 제작하였으며 가시광 투과율 향상을 유도하였다. 나노 구의 지름과 코팅조건에 따라 구조변화를 유도하였으며 FE-SEM과 AFM을 통해 박막의 구조적 변화를 측정하였다. 결과로부터 나노 구의 역상모양을 갖는 박막이 형성 되었으며 직경에 따라 패턴 간격이 확연하게 변화되었음을 확인 하였다. 나노 구가 위치하고 있던 자리로부터 빈 공간형성을 유도할 수 있었으며 이는 가시광 투과율향상에 직접적 영향을 주었다. 또한 상기 패턴화된 $VO_2$ 박막은 광학 스위칭 효율을 유지하면서 주기적 패턴으로부터 시각적으로 광결정유도를 통한 미적 시너지를 보였며 본 연구로부터 $VO_2$기반 스마트 창호 응용에 많은 기여가 기대된다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.8
• /
• pp.646-650
• /
• 2012

Multifunctional structures with two kinds of materials have been intensively investigated in order to improve their electrical characteristic with two functions simultaneously. However, the research regarding of multifunctional ceramic sensor is still in a preliminary stage and how to integrate them with low-cost and high-yield mass production process remains a challenge issue. In this study, we fabricated the multifunctional ceramic sensor composed of temperature and gas sensors. Moreover, we investigated the CO sensing properties of three dimensional nanostuctured $Nb_2O_5$ thin film gas sensors fabricated with silica ($SiO_2$ nanosphere (${\O}$= 750 nm). Compared to plain films, the nanostructured films show enhanced gas sensing of greater sensitivity and a faster response. This result reveals that significantly increased sensitivity is an increase in the effective surface area for the adsorption of gas molecules.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.7
• /
• pp.2004-2008
• /
• 2014

This paper reports the facile synthesis methods of zinc oxide (ZnO) nanoparticles, Z1-Z10, using diethylene glycol (DEG) and polyethylene glycol (PEG400). The particle size and morphology were correlated with the PEG concentration and reaction time. With 0.75 mL of PEG400 in 150 mL of DEG and a 20 h reaction time, the ZnO nanoparticles began to disperse from a collective spherical grain shape. The ZnO nanoparticles were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and a $N_2$ adsorption-desorption studies. The Brunauer-Emmett-Teller (BET) surface areas of Z4, Z5 and Z10 were 157.083, 141.559 and 233.249 $m^2/g$, respectively. The observed pore diameters of Z4, Z5 and Z10 were 63.4, 42.0 and 134.0 ${\AA}$, respectively. The pore volumes of Z4, Z5 and Z10 were 0.249, 0.148 and 0.781 $cm^3/g$, respectively. The photocatalytic activity of the synthesized ZnO nanoparticles was evaluated by methylene blue (MB) degradation, and the activity showed a good correlation with the $N_2$ adsorption-desorption data.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.429.2-429.2
• /
• 2014

ZnO nanowire is known as synthesizable and good mechanical properties. And, stimuli-responsive polymer is widely used in the application of tunable sensing device. So, we combined these characteristics to make precise tunable sensing devise. In this work, we investigate the dependence of ZnO nanowire alignment and morphology on si substrate using nanosphere template with various conditions via hydrothermal process. Also, pH-temperature dependant tuning ability of nanostructure was studied. The brief experimental scheme is as follow. First, Zno seed layer was coated on a si wafer ($20{\times}20mm$) by spin coater. And then $1.15{\mu}m$ sized close-packed PS nanospheres were formed on a cleaned si substrate by using gas-liquid-solid interfacial self-assembly method. After that, zinc oxide nanowires were synthesized using hydrothermal method. Before the wire growth, to specify the growth site, heat treatment was performed. Finally, NIPAM(N-Isopropylacrylamide) was coated onto as-fabricated nanostructure and irradiated by UV light to form the PNIPAM network. The morphology, structures and optical properties are investigated by FE-SEM(Field Emission Scanning electron Microscopy), XRD(X-ray diffraction), OM(Optical microscopy), and WCA(water contact angle).