• Macromolecular Research
• /
• 제17권10호
• /
• pp.750-756
• /
• 2009

Stable, spherical, polystyrene particles were synthesized in ab initio dispersion polymerization by using the poly(methacrylic acid)[PMAA] macro-RAFT agent. The presence of the PMAA macro-RAFT agent on the polystyrene (PS) particles was confirmed by NMR and FTIR spectroscopy. The PS particle size was influenced by the concentration of the RAFT agent and monomer due to the initial nucleation. When the concentration of the PMAA macro-RAFT agent was increased from 2 to 10 wt% relative to the monomer, the average particle size decreased from 2.31 to 1.36 ${\mu}m$, the conversion decreased from 93.3 to 88.9%, the weight-average molecular weight increased from 46,300 to 150,200 g $mol^{-1}$ and the PDI decreased from 2.79 to 1.94, respectively. In particular, the incorporation of 10 wt% of PMAA macro-RAFT agent produced monodisperse PS spheres of 1.36 ${\mu}m$ with a coefficient of variation (CV) of 6.44%. Thus, the PMAA macro-RAFT agent worked as a reactive steric stabilizer providing monodisperse, micron-sized, PS particles.

• Elastomers and Composites
• /
• 제48권4호
• /
• pp.294-299
• /
• 2013

수용성 단량체인 메타크릴산 (MAA)을 단량체로 potassium persulfate (KPS)를 개시제로 이용하여 $70^{\circ}C$에서 $90^{\circ}C$ 사이의 선택된 온도에서 용액중합을 진행하였다. 물에 대한 메타크릴산의 농도가 감소하거나 개시제의 농도가 증가하면 분자량은 감소하였다. 중합반응온도는 폴리메타크릴산 (PMAA)의 분자량에 크게 영향을 미치지 않았다. Weissenberg 효과는 대부분의 반응온도에서 나타났으며, $90^{\circ}C$에서는 약하게 관찰되었다. 대부분의 중합반응에서 분산성지수는 1.5 이하로 관찰되었다. 교반속도가 증가하면서 분자량은 점진적으로 증가하다, 교반속도가 800 rpm에 이르면서 수평균 및 중량평균분자량이 동일하게 791,000 g/mol의 분자량을 갖는 단분산성의 PMAA가 구하여졌다. 유리전이온도는 $162^{\circ}C$로 측정되었다.