• Clean Technology
• /
• v.20 no.3
• /
• pp.232-240
• /
• 2014

The significance of thermoplastic polyolefin polypropylene (PP) lies in its potential to replace polyvinyl chloride (PVC), the most widely used material for automobile interiors (door trim, dash board), which discharges harmful compounds in certain conditions. Another benefit of PP (0.855 amorphous - 0.946 crystalline $g/cm^3$) is its low density compared to that of PVC ($1.1-1.45g/cm^3$), which reduces vehicle weight. Market demand for eco-friendly water-based adhesive/coating material is rising significantly as a substitute for solvent-based adhesive/coating material which emits VOC and causes harmful working conditions. Under such context, in this study, a series of eco-friendly waterborne polyurethane-urea primer (a paint product that allows finishing paint to adhere much better than if it were used alone) for hydrophobic PP were prepared from different mix of DMPA content, NCO/OH molar ratio, various wt% of silicone diol and various soft segment content, among which DMPA of 21 mole %, NCO/OH molar ratio of 1.2, modified silicone diol of 5 wt% and soft segment content of 73 wt% led to good adhesion strength. Additionally, the incorporation of optimum content of additives (0.5 wt% dispersing agent, 0.5 wt% levelling agent, 1.5 wt% antifoaming agent, 3.0 wt% matting agent) into the optimum waterborne polyurethane-urea also enabled good stability, levelling, antifoaming and non-glossy.

• Applied Chemistry for Engineering
• /
• v.3 no.4
• /
• pp.595-604
• /
• 1992

Carbonate-type polyurethane resins containing anionic moieties were systhesized from NCO-terminated prepolymer method. Membranes were manufactured from the polymer solution and the separation of aqueous ethanol solution was investigated. To enhance the property of urethane resin, carbonate-type polyol(PTMCG) was used. ${\alpha}^{\prime},{\alpha}^{{\prime}{\prime}}$-dimethylolpropionic acid was used as a chain extender to increase the hydrophilicily of the urethane membrane. The ionization of the pendent carboxylic groups in urethane resin was carried out using trimthylamine. To confirm the formation of anionic groups in urethane resin, IR spectra of model compounds were compared with those of urethane resins. It was confirmed that the concentration of hard segment and hydrogen bond contributed to the property of the concentration of hard segment and hydrogen bond contributed to the property of urethane resin in which the mole ratio of chain extender and polyol was from 3:1 to urethane resin in which the mole ratio of chain extender and polyol was from 3:1 to 5:1. The carbonate-type polyurethane containing pendent carboxylic grop(PU) had Tg of around-$25^{\circ}C$ and Tm, $45^{\circ}C$ measured by DSC. Transition temperatures of one containing pendent anionic group(APU) prepared from the ionization of PU shifted to $8{\sim}10^{\circ}C$ lower temperature region than those of PU. Pervaporation membrane was prepared through the casting method. N, N-dimethylformamide (DMF) were used as a solvent and hexamethylene diisocyanate(HMDl) as a crosslinking agent. Swelling degree increased with ethanol concentration in mixure and the control of the swelling degree of the membrane could be achieved by crossliking. The results of pervaporation were as follows : separation factor, 2.3~9.8 ; flux, $27{\sim}79.5g/m^2hr$. Pervaporation separation capacity could be enhanced by reducing the molecular weight of polyol from 2,000 to 1,000.