• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1177-1185
• /
• 1996

Y-TZP/Ce-TZP ceramics having relative sintered densities of>95% average grain sizes of 0.36$\mu\textrm{m}$ microhar-dness of 1150 kg/mm2 fracture strength of 390-830 MPa and toughness of 6.4-10.2 MPa$.$mm1/2 were prepared by conventional sintering of 3 mol% Y2O3-ZrO2 and 12 mol% CeO2-ZrO2 powders at 1400 and 1500$^{\circ}C$ The average grain sizes of Y-TZP/Ce-TZP ceramics were mainly governed by those of Ce-TZP. White increasing Ce-TZP content toughness increased while microhardness and fracture strength decreased. With comparing microhardness and toughness fracture strength was more sensitive on not only grain size but also other factors such as microstructural and compositional variations. The densification of Y-TZP/Ce-TZP cermaics was not greatly affected by composition and soaking time at temperature over 1400$^{\circ}C$ With increasing CE-TZP content the stability of t-ZrO2 decreased under thermal aging in air whereas increased in hydrothermal atmosphere and aqueous solution.

• Journal of the Korean Ceramic Society
• /
• v.45 no.3
• /
• pp.185-189
• /
• 2008

In order to fabricate porous ceramics, hydrated sodium silicate was synthesized by hydrothermal reaction using anhydrous sodium silicate. The microstructural and the structural characteristics of the expanded ceramics were observed depending on heat treatment temperature (550, 600, 650, $700^{\circ}C$) and then the effect of these characteristics on the compressive strength and the temperature gradient was investigated. As the heat treatment temperature was increased, the compressive strength was decreased from $0.717KN/cm^2\;(550^{\circ}C)\;to\;0.166KN/cm^2\;(700^{\circ}C)$. The temperature gradient was increased with increasing the experimental temperature regardless of the heat treatment temperature. The temperature gradient of the expanded ceramics which was heat treated at $650^{\circ}C\;was\;300^{\circ}C$. The bulk specific gravity, porosity, pore size, pore characteristics and wall thickness were varied depending on heat treatment temperature, and the compressive strength and the temperature gradient were governed by the complex effects of these factors.

• Journal of Korea Foundry Society
• /
• v.13 no.4
• /
• pp.359-368
• /
• 1993

Mg-9wt.%Al and Mg-9wt.%-1.6wt%Zn/SiCp(particle size $40{\mu}m$) metal-matrix-composite specimens were manufactured by rheo-compocasting method, known for its effect of improving the wettability. The ceramic reinforcement particles(SiCp) were dispersed in the semi-solid magnesium alloy matrix slurry being vigorously stirred in a high frequency induction furnace under inert atmosphere. A microstructural study of the dispersed particles in the specimens, prepared under different conditions as regards the time(10min, 20min, 30min) and temperature of the stirring, was made with the aid of optical microscope and SEM. The effect of superheating was also observed. It is revealed that 30 minutes' stirring time of the semi-solid at 40% solid fraction temperature(Mg-9wt.%Al : $590^{\circ}C$, AZ91 : $576^{\circ}C$), as determined by the lever rule, gives a satisfactorily uniform distribution of the particles. The superheating is observed to enhance further the uniformity.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.413-415
• /
• 2000

Piezoelectric ceramics of PZT have been developed to apply for transformers in notebook. Use of piezoelectric ceramics in applications like piezoelectric transformers was made possible by the development of new materials with high electromechanical coupling coefficients and high mechanical quality factor. "Hard" ferroelectiric ceramics of complex composition based on lead zirconate titanate with Mn additive have been prepared. The perovskitic phase reaction of the oxides. The crucial role played by the intermediate mixing and grinding procedures in the assessment of the final properties of the material was investigated. Densification up to approximately the theoretical density value was achieved. The polarization was obtained by subjecting the samples at $30kVcm^{-1}$ poling electric field, in a silicon oil bath heated at $110^{\circ}C$. Their microstructural and morphological properties were checked by X-ray diffraction analysis and scanning electron microscopy. The optimized samples presented very high qualify and electromechanical coupling factors, together with small dielectric loss.

• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.22-27
• /
• 2014

In the past, cold crack was commonly observed in the HAZ(heat affected zone) of high-strength steels. Applying to TMCP(thermo-mechanical controlled process) and HSLA(high strength low alloy) steels, cold crack tends to increase the occurrence in the weld metal. It is generally understood that cold crack occurs when the following factors are present simultaneously : diffusible hydrogen in the weld metal, a susceptible microstructure and residual stress. In particular, many studies investigated the microstructural effect on the cold crack in HAZ and the cold crack in weld metals starts to receive the special attendance in modern times. The purpose of the study is to review the effect of weld microstructures (grain boundary ferrite, Widm$\ddot{a}$nstatten ferrite, acicular ferrite, bainite and martensite) on cold crack in the weld metals. Among various microstructures of weld metals, acicular ferrite produced the greatest resistance to the cold crack due to the fine interlocking nature and high-angle grain boundary of the microstructure.

• Journal of Periodontal and Implant Science
• /
• v.47 no.1
• /
• pp.20-29
• /
• 2017

Purpose: The microstructural characteristics of trabecular bone were identified using micro-computed tomography (micro-CT), in order to develop a potential strategy for implant surface improvement to facilitate osseointegration. Methods: Alveolar bone specimens from the cadavers of 30 humans were scanned by high-resolution micro-CT and reconstructed. Volumes of interest chosen within the jaw were classified according to Hounsfield units into 4 bone quality categories. Several structural parameters were measured and statistically analyzed. Results: Alveolar bone specimens with D1 bone quality had significantly higher values for all structural parameters than the other bone quality categories, except for trabecular thickness (Tb.Th). The percentage of bone volume, trabecular separation (Tb.Sp), and trabecular number (Tb.N) varied significantly among bone quality categories. Tb.Sp varied markedly across the bone quality categories (D1: $0.59{\pm}0.22mm$, D4: $1.20{\pm}0.48mm$), whereas Tb.Th had similar values (D1: $0.30{\pm}0.08mm$, D4: $0.22{\pm}0.05mm$). Conclusions: Bone quality depended on Tb.Sp and number-that is, endosteal space architecture-rather than bone surface and Tb.Th. Regardless of bone quality, Tb.Th showed little variation. These factors should be taken into account when developing individualized implant surface topographies.

• Journal of Welding and Joining
• /
• v.7 no.2
• /
• pp.35-48
• /
• 1989

This study is concerned with a correlation of microstructure and local brittle zone (LBZ) in offshore structural steel welds. The influence of the LBZ on fracture toughness was investigated by means of simulated heat-affected zone (HAZ) tests as well as welded joint tests. Micromechanical processes involved in void and cleavage microcrack formation were also identified using notched round tensile tests and subsequent SEM observations. The LBZ in the HAZ of a multiphase welded joint is the interstitially reheated coarse grained HAZ, which is influenced by metallurgical factors such as effective grain size, the major matrix structure and the amount of high-carbon martensite-austenite (M-A) constituents. The experimental results indicate that Chirpy energy was found to scale monotonically with the amount of M-A constituents, confirming that the M-A constituent is the major microstructural factor controlling the HAZ toughness. In addition, voids and microcracks are observed to initiate at M-A constituents by the shear cracking process. Thus, the M-A constituent played an important role in initiating the voids and microcracks, and consequently caused brittle fracture.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.1
• /
• pp.6-12
• /
• 2017

In this study tensile and impact properties of three hypo-eutectoid steels containing different micro-alloying elements were investigated in terms of microstructural factors such as pro-eutectoid ferrite grain size, pearlite fraction, interlamellar spacing, and cementite thickness. Yield point phenomenon appeared in all the steel specimens during tensile testing, and ultimate tensile stress was mainly dependent on pearlite fraction. On the other hand, the refinement of austenite grain size caused by the addition of micro-alloying elements resulted in the increment of ferrite volume fraction and carbon contents in pearlite because of the refinement of pro-eutectoid ferrite grain size. As a result, cementite thickness in pearlite increased and had an effect on deteriorating the low temperature impact toughness.

• Geomechanics and Engineering
• /
• v.21 no.4
• /
• pp.337-348
• /
• 2020

Tropical organic soils having more than 65% of organic matters are named "peat". This soil type is extremely soft, unconsolidated, and possesses low shear strength and stiffness. Different conventional and industrial binders (e.g., lime or Portland cement) are used widely for stabilisation of organic soils. However, due to many factors affecting the behaviour of these soils (e.g., high moisture content, fewer mineral particles, and acidic media), the efficiency of the conventional binders is low and/or cost-intensive. This research investigates the impact of different constituents of cement-sodium silicate grout system on the compressibility behaviour of organic soil, including settlement and void ratio. A microstructure analysis is also carried out on treated organic soil using Scanning Electron Micrographs (SEM), Energy Dispersive X-ray spectrometer (EDX), and X-ray Diffraction (XRD). The results indicate that the settlement and void ratio of treated organic soils decrease gradually with the increase of cement and kaolinite contents, as well as sodium silicate until an optimum value of 2.5% of the wet soil weight. The microstructure analysis also demonstrates that with the increase of cement, kaolinite and sodium silicate, the void ratio and porosity of treated soil particles decrease, leading to an increase in the soil density by the hydration, pozzolanic, and polymerisation processes. This research contributes an extra useful knowledge to the stabilisation of organic soils and upgrading such problematic soils closer to the non-problematic soils for geotechnical applications such as deep mixing.

• Korean Journal of Metals and Materials
• /
• v.56 no.11
• /
• pp.796-804
• /
• 2018

The Charpy impact toughness of the heat affected zone (HAZ) of electro gas welded 390 MPa yield strength grade steel, manufactured by a thermo mechanically controlled process, was investigated. The effects of added Nb on the toughness of the steel and the factors influencing scatter in toughness are discussed in the present work. It was observed that adding Nb to the steel led to the deterioration of HAZ toughness. The presence of soluble Nb in the HAZ increased its hardenability and resulted in a larger amount of low toughness bainitic microstructure. Microstructural observations in the notch root area revealed the significant role of different microstructures in the area. In the presence of a larger amount of bainitic microstructures, the HAZ exhibited a lower Charpy toughness with a larger scatter in toughness. A softened zone with a lower hardness than the base metal was formed in the HAZ. However, theoretical analysis revealed that the presence of the zone might not be a problem in a real welded joint because of the plastic restraint effect enforced by surrounding materials.