• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.2
• /
• pp.96-113
• /
• 1996

It has been found that the misfit dislocations in heavily boron-doped layers originate from wafer edges. Moreover, the propagation of the misfit dislocation into a heavily boron-doped region can be suppressed by placing a surrounding undoped region. Using a surrounding undoped region the disloction-free heavily boron-deoped silicon membranes have been fabricated. The measured surface roughness, fracture strength, and residual tensile stress of the membrane are 20.angs. peak-to-peak, 1.39${\times}$10$^{10}$ and 2.7${\times}$10$^{9}$dyn/cm$^{2}$, while those of the conventional heavily boron-doped silicon membrane with high density of misfit dislocations are 500 peak-to-peak, 8.27${\times}$10$^{9}$ and 9.3${\times}$10$^{8}$dyn/cm$^{2}$ respectively. The differences between these two membranes are due to the misfit dislocations. Young's modulus has been extracted as 1.45${\times}$10$^{12}$dyn/cm$^{2}$ for both membranes. Also, the effective lattice constant of heavily boron-doped silicon, the in-plane lattice constant of the conventional membrane, and the density of misfit dislocation contained in the conventional membrane have been extracted as density of misfit dislocation contained in the conventional membrane have been extracted as density of misfit dislocation contained in the conventional membrane have been extracted as 5.424.angs. 5.426.angs. and 2.3${\times}$10$^{4}$/cm for the average boron concentration of 1.3${\times}$10$^{20}$/cm$^{-23}$ cm$^{3}$/atom. Without any buffer layers, a disloction-free lightly boron-doped epitaxial layer with good crsytalline quality has been directly grown on the dislocation-free heavily boron-doped silicon layer. X-ray diffraction analysis revealed that the epitaxial silicon has good crystallinity, similar to that grown on lightly doped silicon substrate. The leakage current of the n+/p gated diode fabricated in the epitaxial silicon has been measured to be 0.6nA/cm$^{2}$ at the reverse bias of 5V.