• Journal of the Korean Wood Science and Technology
• /
• v.33 no.2 s.130
• /
• pp.29-39
• /
• 2005

Formaldehyde emissions from wood-based panels bonded with pine and wattle tannin-based adhesives, urea-formaldehyde resin (UF), melamine-formaldehyde resin (MF), and co-polycondensed resin of urea-melamine-formaldehyde (UMF) were measured by the Japanese standard method using a desiccator (JIS A 1460) and the EN 120 (European Committee For Standardization, 1991) method using the perforator value. In formaldehyde emission, all particleboards made using the wattle tannin-based adhesive with three different hardeners, paraformaldehyde, hexamethylenetetramine, and tris(hydroxyl)nitromethan (TN), satisfied the requirements of grade $E_1$. But only those made using the pine tannin-based adhesive with the hexamine as hardener met the grade $E_1$ requirements. Hexamine was effective in reducing formaldehyde emission in tannin-based adhesives when used as the hardener. While the UF resin showed a desiccator value of $7.1mg/{\ell}$ and a perforator value of 12.1 mg/100 g, the MF resin exhibited a desiccator value of $0.6mg/{\ell}$ and a perforator value of 2.9 mg/100 g. According to the Japanese Industrial Standard and the European Standard, the formaldehyde emission level of the MDF panels made with UF resin in this study came under grade $E_2$. The formaldehyde emission level was dramatically reduced by the addition of MF resin. The desiccator and perforator methods produced proportionally equivalent results. Gas chromatography, a more sensitive and advanced method, was also used. The samples for gas chromatography were gathered during the experiment involving the perforator method. The formaldehyde contents measured by gas chromatography were directly proportional to the perforator values.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.4
• /
• pp.409-418
• /
• 2017

This work attempted to manufacture glued-laminated timber (Glulam) bonded with melamine-urea-formaldehyde (MUF) resin adhesives at various melamine contents from 20% to 50% under high frequency (HF) heating for a very short time. Two preparation methods were employed to prepare MUF resin adhesives with different melamine contents: one-batch method of synthesizing MUF resins in a single batch, and two-batch method of mixing urea-formaldehyde (UF) resin with melamine-formaldehyde (MF) resin that had been synthesized separately. As the melamine content increased, the gelation time and peak temperature of MUF resins decreased. The adhesion performance of plywood showed that the one-batch MUF resin adhesive with 50% melamine content only satisfied the standard requirement of water resistance. Thus, the one-batch MUF resin adhesive with 50% melamine content was applied for bonding wood lamina from four softwood species such as Japanese larch, Korean red pine, Korean pine and Japanese cedar to manufacture Glulam under HF heating. All Glulam samples bonded with the one-batch MUF resin adhesives with 50% melamine content except those from Korean Red Pine satisfied the requirement in water soaking or boiling water delamination test as an exterior grade Glulam. The presence of rosin in Korean Red Pine was believed to be responsible for its poor adhesion. These results showed that the one-batch MUF resin adhesives with 50% melamine content provided acceptable water resistance with exterior grade Glulam manufactured under HF heating.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.5
• /
• pp.58-66
• /
• 2007

The objective of this research was to develop environment-friendly adhesives for face fancy veneer bonding of engineered flooring. Urea-formaldehyde (UF)-tannin and melamine-formaldehyde (MF)/PVAc hybrid resin were used to replace UF resin in the formaldehyde-based resin system in order to reduce formaldehyde and volatile organic compound (VOC) emissions from the adhesives used between plywoods and fancy veneers. Wattle tannin powder (5 wt%) was added to UF resin and PVAc (30 wt%) to MF resin. These adhesive systems showed better bonding than commercial UF resin with a similar level of wood penetration. The initial adhesion strength was sufficient to be maintained within the optimum initial tack range. The standard formaldehyde emission test (desiccator method) and VOC analyzer were used to determine the formaldehyde and VOC emissions from engineered flooring bonded with commercial UF resin, UF-tannin and MF/PVAc hybrid resin. By desiccator method, the formaldehyde emission level of UF resin showed the highest but was reduced by replacing with UF-tannin and MF/PVAc hybrid resin. MF/PVAc hybrid satisfied the $E_1$ grade (below $1.5mg/{\ell}$). VOC emission results by VOC analyzer were similar with the formaldehyde emission results. TVOC emission was in the following order: UF > UF-tannin > MF/PVAc hybrid resin.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.6
• /
• pp.913-922
• /
• 2016

This study attempted to measure molecular weight (MW) of melamine-urea-formaldehyde (MUF) resins prepared by two different synthesis methods: the one-step MUF resins were synthesized in one batch procedure, while the two-step MUF resins were prepared by a physical mixing of urea-formaldehyde (UF) resin with melamine-formaldehyde (MF) resin that had been synthesized in a separate procedure. The properties of medium density fiberboard (MDF) panels bonded with two types of MUF resins were also investigated. MWs of these MUF resins were measured using gel permeation chromatography (GPC). In addition, this study measured the MWs of one-step MUF resin during its synthesis procedure. The performance of two types of MUF resins was evaluated by determining properties of MDF panels prepared in laboratory. As the synthesis procedure progressed, both number average MW ($M_n$) and weight average MW ($M_w$) of one-step MUF resin gradually increased, while the polydispersity index (PDI) decreased. And low Mw species of the resin predominantly decreased as the synthesis step progressed. The one-step MUF resin showed greater $M_n$ and $M_w$ than those of the two-step ones even though the PDI values of both resins were very similar each other. As expected, the one-step MUF resin resulted in better properties of MDF panels than those of two-step resins. In particular, the one-step MUF resin provided better internal bond (IB) strength and thickness swelling (TS) with MDF panels than those of two-step ones, indicating better water resistance of the one-step resin. These results suggest that the preparation method of MUF resins have a great impact on the MW and final panel properties.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.2
• /
• pp.37-45
• /
• 2006

The viscoelastic properties of blends of melamine-formaldehyde (MF) resin and poly(vinyl acetate) (PVAc) for engineered flooring used on the Korean traditional ONDOL house floor heating system were investigated by dynamic mechanical thermal analysis (DMTA). Because MF resin is a thermosetting adhesive, the effect of MF rein was shown across all thermal behaviors. The addition of PVAc reduced the curing temperature. The DMTA thermogram of MF resin showed that the storage modulus (E') increased as the temperature was further increased as a result of the cross-linking induced by the curing reaction of the resin. The storage modulus (E') of MF resin increased both as a function of increasing temperature and with increasing heating rate. From isothermal DMTA results, peak $T_{tan{\delta}}$ values, maximum value of loss modulus (E") and the rigidities (${\Delta}E$) of MF/PVAc blends at room temperature as a function of open time, peak $T_{tan{\delta}}$ and maximum loss modulus (E") values were found to increase with blend MF content. Moreover, the rigidities of the 70:30 and 50:50 MF/PVAc blends were higher than those of the other blends, especially of 100% PVAc or MF. We concluded that blends the MF/PVAc blend ratios correlate during the adhesion process.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.3
• /
• pp.327-333
• /
• 2015

To measure the dimensional stability of three softwoods by vacuum pressurization of water soluble melamine-formaldehyde (MF) resin impregnation process, properties of resin treated compressed woods (compregs) were measured after impregnating the water soluble MF resin into three coniferous wood species for different impregnation times and resin concentrations. As the resin concentration was higher and impregnation time was longer, coefficients of volumetric shrinkage and anti-volumetric swelling efficiency increased, but coefficients of volumetric swelling, anti-volumetric swelling efficiency and absorption decreased. Also, weight percent gain increased remarkably as the resin concentration was high, but there was no uniform relationship with impregnation time.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.13 no.3 s.31
• /
• pp.242-251
• /
• 1989

The purpose of this study was to investigate the changes in easy-care and strength properties of the wet fixation processed viscose rayon fabrics. Rayon fabrics were treated with mixed resins of melamine formaldehyde (MF) and DMDHEU by one bath and two bath wet fixation processes. The MF/DMDHEU mixed resin concentrations were 50/100, 50/150, 100/100, 100/150 and 150/100(g/1). Magnasium chloride was used as a catalyst. Treated fabrics were evaluated by nitrogen content, DP rating, wrinkle recovery angle, breaking strength, tearing strength and abrasion resistance. The properties were compared to the fabrics treated by conventional Pad-Dry-Cure (PDC) method. Wet fixation processed fabrics showed DP ratings of higher than 3 and higher than 275 degrees of wrinkle recovery angles in all the mixed resin concentrations. Wet fixation processed fabrics showed increase in breaking strength and tearing strength but decrease in abrasion resistance. However, the decrease in abrasion resistance was much less than the conventional PDC treated fabrics. The one bath wet fixation processed fabrics showed better physical properties than the two bath processed fabrics in general. The optimum treatment condition was the mixed resin concentration of MF/DMDHEU, 100/100 g/l in one bath wet fixation process.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.6
• /
• pp.787-796
• /
• 2017

A low dimensional stability and poor bending strength properties were main problems in particleboard manufacturing. The objective of this research was to evaluate the effect of mixed wood species and urea-formaldehyde (UF) or urea-melamine-formaldehyde (UMF) resins on the physical and mechanical properties of three-layer particleboards. The ratio of face/core/back layer was 1 : 2 : 1. The resin content of 12% for both UF resins and UMF resins (UF/MF = 70/30% w/w) was used. The results of this study showed that the utilization of S.mahagony shaving using both UF and UMF resins caused a decrease in the thickness swelling and water absorption of the boards. Thickness swellings of particleboard made of Sengon/Sengon/Sengon (SSS), Mahogany/Mahogany/Mahogany (MMM), Sengon/Mahogany/Sengon (SMS), and Mahogany/Sengon/Mahogany (MSM) were in the range of 23%, 12~16%, 14~16%, and 13~21%, respectively. The board bonded with UMF resin demonstrated better dimensional stability than that bonded with UF resin alone. Modulus of elasticity (MOE) and modulus of rupture (MOR) of particleboards made of S. mahagony shaving in the surface layer in both MMM and MSM boards were better than those of the SSS and SMS. MOE of MMM and MSM board was in the ranges of 24,000 to $26,000kg.cm^{-2}$ and 18,000 to $21,000kg.cm^{-2}$ respectively. Meanwhile, the MOR of board was in the ranges of 200 to $240kg.cm^{-2}$ and 190 to $228kg.cm^{-2}$, respectively.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.13 no.4
• /
• pp.357-369
• /
• 1989

The purpose of this study was to investigate the effects of treatment temperature and time on the, of easy-care and strength properties of the wet fixation processed rayon fabrics. Viscose rayon fabrics were treated with mixed resins of melamine formaldehyde (MF) and DMDHEU by one bath and two bath wet fixation processes. The MF/DMDHEU mixed resin concentrations were 50/100, 50/150, 100/100 and 100/150(g/1). Magnasium chloride was used as a catalyst. The wet fixation conditions were 24hrs at room temperature,20 mins at $75^{\circ}C$ and 5 mins at $105^{\circ}C$ Wet fixation processed fabrics did not show the difference in the resin add-one, DP ratings and wrinkle recovery angles by the different treatment temperatures and times. DP ratings were in the order of $105^{\circ}C>75^{\circ}C>room$ temp, in one bath and two bath wet fixation. Breaking and tearing strength of one bath processed fabrics showed in the order of $75^{\circ}C>room\;temp>105^{\circ}C$ The breaking strength of two bath processed fabrics showed in the order of $105^{\circ}C>75^{\circ}C>room$ temp. Tearing strength showed in the order of $75^{\circ}c>105^{\circ}C>room$ temp. Abrasion resistances were in the order of $75^{\circ}C>105^{\circ}C>room$ temp. in one bath and two bath processes.