• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.79-87
• /
• 1997

Anti-reflective and anti-static double layered films were prepared on the VDT panel by sol-gel spin-coating method. Their electrical, opticla, and mechanical properties were investigated. The outer SiO2 film with low re-fractive index was coated over the inner ATO(Antimony-doped Tin Oxide)-SiO2 film which was prepared by mixing ATO sol with SiO2 at molar ratio of 68:32 to satisfy the interference condition of double layers. The heat treatment was conducted at 45$0^{\circ}C$ for 30 min where residual organics were completely removed. The sheet resistance of ATO single layer showed the minimum value of 6$\times$107$\Omega$/$\square$ at 3 mol% addition of Sb and that of SiO2/ATO-SiO2 increased slightly with increasing SiO2 mol% up to 30 mol%, and then increased steeply to the value of 3$\times$108$\Omega$/$\square$ at 32 mol%. The reflectance of double layered films was about 0.64% at the wavelength of 550nm and the transmittance increased about 3.20%. The hardness of double layered films was almost the same as that of uncoated VDT panel, 471.4kg.f/mm2.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.57 no.5
• /
• pp.808-815
• /
• 2008

The composites were fabricated 61[vol.%] ${\beta}$-SiC and 39[vol.%] $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at 1650[$^{\circ}C$] for 4 hours. The present study investigated the influence of the content of $Al_2O_3+Y_2O_3$ sintering additives on the microstructure, mechanical and electrical properties of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Phase analysis of SiC-$TiB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), ${\beta}$-SiC(3C), $TiB_2$, and In Situ YAG($Al_2Y_3O_{12}$). The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. There is another reason which pressureless annealed temperature 1650[$^{\circ}C$] is lower $300{\sim}450[^{\circ}C]$ than applied pressure sintering temperature $1950{\sim}2100[^{\circ}C]$. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[Mpa], 54.60[Gpa] and 2.84[Gpa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. The electrical resistivity showed the lowest value of 0.0117[${\Omega}{\cdot}cm$] for 16[wt%] $Al_2O_3+Y_2O_3$ additives at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from $25^{\circ}C$ to 700[$^{\circ}C$]. The resistance temperature coefficient of composite showed the lowest value of $-2.3{\times}10^{-3}[^{\circ}C]^{-1}$ for 16[wt%] additives in the temperature ranges from 25[$^{\circ}C$] to 100[$^{\circ}C$].

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.12
• /
• pp.27-36
• /
• 2019

The demand for a low dispersion lens with a small refractive index and a high refractive index is increasing, and accordingly, there is an increasing need for a releasable protective film with high heat resistance and abrasion resistance. On the other hand, the optical industry has not yet established a clear standard for the manufacturing process and quality standards for mold-releasing protective films used in aspheric glass lens molding. Optical lens manufacturers treat this technology as proprietary information. In this study, an experiment was conducted regarding the optimization of ion etching, magnetron, and arc current at each source and filter part, and bias voltage in FCVA (filtered cathode vacuum arc)-based Ta-C thin film coatings. This study found that compared to iridium-rhenium alloy thin film sputtering products, the coating conditions were improved by approximately 50%, 20%, and 40% in terms of thickness, hardness, and adhesive strength of the film, respectively. The thin-film coating process proposed in this study is expected to contribute significantly to the development and utilization of glass lenses, which will help enhance the minimum mechanical properties and quality of the mold-release thin film layer required for glass mold surface forming technology.

• Weed & Turfgrass Science
• /
• v.2 no.3
• /
• pp.221-229
• /
• 2013

This paper reviews current status of weed control practices in herbicide-resistant crops to examine weed management strategies in cope with cropping herbicide-resistant crops in the near future. Herbicide-resistant crops were rapidly adopted weed management technologies due to broad-spectrum weed control without crop injury. Transgenic glyphosate-resistant cultivars in soybean, corn, canola, and cotton were adopted to manage weeds at lower cost in a simplified weed management system. Dual stack crops with glyphosate and glufosinate resistance were developed to control glyphosate resistant weeds in corn, soybean and cotton. New multiple herbicide-resistant crops with resistance to glyphosate and glufosinate, acetolactate synthase (ALS) inhibitors, synthetic auxin herbicides, 4-hydroxyphenyl pyruvate dioxygenase (HPPD) inhibitors or acetyl Coenzyme A carboxylase (ACCase) inhibitors will expended the utility of existing herbicide technologies to manage the evolution of resistant weeds. However, herbicide resistant crops alone cannot solve weed problems and thus studies on diverse weed managements using an array of alternating herbicides of mode of action, mechanical, and cultural practices are needed for integrated weed management systems in the future.

• Applied Chemistry for Engineering
• /
• v.21 no.5
• /
• pp.495-499
• /
• 2010

To develop chemical and biosensors, this paper studies sensing characteristics of bulk carbon nanotube (CNT) electrodes by means of their electrical impedance properties due to their large surface area and excellence chemical absorptivity. The sensors were fabricated in the form of film and nano web style by using composite process for mass production. The bulk composite electrodes were fabricated with singlewall and multi-wall carbon nanotubes based on host polymers such as Nafion and PAN, using a solution-casting and an electrospinning technique. The resistance and the capacitance of electrodes were measured with LCR meter under the various amounts of buffer solution to study the electrical impedance change properties of them. On the experimental of sensor electrode, impedance characteristics of the composite electrode are affected by its host polymer and nanofiller and its sensing response showed saturated result after applying some amounts of buffer solution for test chemical. Especially, the capacitance values showed drastic changes while the resistance values only changed within few percent range. It is deduced that the ions in the solution penetrated and diffused into the electrodes surface changed the electrical properties of the electrodes much like a doping effect.

• The Journal of Engineering Geology
• /
• v.21 no.4
• /
• pp.323-336
• /
• 2011

The hydro-mechanical behavior of the Earth's crust is strongly dependent on the fractional volume and geometrical structure of effective pore spaces. This study aims to understand the characteristics of pores using electrical impedance. We measured the electric impedance of core samples (diameter, 38-50 mm; length, 70-100 mm) of three types of granite (Hwangdeung, Pocheon, and Yangsan) and two types of sandstone (Boryung and Berea) with different porosities and pore structures, after saturation with saline water of varying salinities. The results show that resistance decreases but capacitance increases with increasing salinity of the pore fluid. For a given salinity, the resistivity and formation factor are reduced with increasing porosity of the rocks, and the capacitance increases. Berea sandstone shows anisotropy in resistance, tortuosity, and cementation factor, with these factors being highest normal to bedding planes. This result indicates that the connectivity of pores is weakest normal to bedding. In conclusion, the electrical characteristics of the tested samples are related not only to their porosity but also to the pore geometry.

• Journal of the Korean Geotechnical Society
• /
• v.27 no.12
• /
• pp.17-25
• /
• 2011

A fabric of soil media may change due to certain factors such as dissolution of soluble particles, desiccation, and cementation. The fabric changes affect the mechanical behavior of soils. The purpose of this study is to investigate the effects of geo-material dissolution on shear strength. Experiments and numerical simulations are carried out by using a conventional direct shear and the discrete element method. The dissolution specimens are prepared with different volumetric salt fraction in sand soils. The dissolution of the specimens is implemented by saturating the salt-sand mixtures at different confining stresses in the experimental study or reducing the sizes of soluble particles in the numerical simulations. Experimental results show that the angle of shearing resistance decreases with the increase in the soluble particle content and the shearing behavior changes from dilative to contractive behavior. The numerical simulations exhibit that macro-behavior matches well with the experimental results. From the microscopic point of view, the particle dissolution produces a new fabric with the increase of local void, the reduction of contact number, the increase of shear contact forces, and the anisotropy of contact force chains compared with the initial fabric. The shearing behavior of the mixture after the particle dissolution is attributed to the above micro-behavior changes. This study demonstrates that the reduction of shearing resistance of geo-material dissolution should be considered during the design and construction of the foundation and earth-structures.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.30 no.2
• /
• pp.102-111
• /
• 2014

Purpose: Surface damage and bonding strength difference after micromechanical treatment of zirconia surface are to be studied yet. The aim of this study was to evaluate the difference of fracture resistance and bonding strength between more surface-damaged group from higher air-blasting particle size and pressure, and less damaged group. Materials and Methods: Disk shape zirconia ($LAVA^{TM}$) was sintered and air-blasted with $30{\mu}m$ particle size (Cojet), under 2.8 bar for 15 seconds, $110{\mu}m$ particle size (Rocatec), under 2.8 bar for 15 seconds, and $110{\mu}m$ particle size (Rocatec), under 3.8 bar for 30 seconds respectively. Biaxial flexure test and bonding failure load test were performed serially (n = 10 per group). For bonding test, specimens were bonded on the base material having similar modulus of elasticity of dentin with $200{\mu}m$-thick resin cement for tension of surface damage. Failure load of bonding was detected with acoustic emission (AE) sensor. Results: There were no significant differences both in the biaxial flexure test and bonding failure load test between groups (P > 0.05). Sub-surface cracks were all radial cracks except for two specimens. Conclusion: Within the limitations of no aging under monotonic load test, surface damage from higher air-blasting particle size and pressure was not significant. Evaluations of failure load with bonded zirconia disks was clinically relevant modality for surface damage and bonding strength, simultaneously.

• Korean Journal of Materials Research
• /
• v.8 no.5
• /
• pp.457-463
• /
• 1998

New neutron shielding materials, KNS-201, KNS-301 and KNS-601 have been fabricated to be used for radioactive material shipping and storage cask. The base materials are a modified and a hydrogenated bisphenol- A type and novolac type epoxy resin, and aluminium hydroxide and boron carbide are added. These shielding materials offer good fluidity at processing, which makes it possible to form this resin shield into complicated geometric shapes such as radioactive material shipping and storage cask. Several measurements were made for the shielding materials to evaluate the thermal and mechanical properties and radiation resistance. The properties of the shielding materials are as follows: onset temperatures 2S7~28$0^{\circ}C$, thermal conductivities 0.9S~1.14W/m. K, thermal expansion coefficients 0.77~1.26x$10_{-6}{\circ}C_{-1}$, combustion characteristics < 80$0^{\circ}C$, ATB(average time of burning) < 5sec, AEB(average extent of burning) < 5mm, tensile strengths 2.5~3.2kg/$\textrm{mm}^2$, compressive strengths 13.2~1S.2kg/$\textrm{mm}^2$, flexural strengths 5.2 -6.4kg/$\textrm{mm}^2$. In general, the concerned properties of KNS-201, KNS-301 and KNS-601 were revealed to be better than those of NS-4- FR. foreign neutron shielding material. It is also observed that the radiation resistance of KNS- 601 was better than those of KNS-201 and KNS-301.

• Journal of the Korea Concrete Institute
• /
• v.14 no.3
• /
• pp.307-314
• /
• 2002

Utilization of demolished-concrete as recycled aggregate has been researched for the purpose of substituting for insufficient natural aggregate, saving resources and protecting environment. There, however, are some Problems not only the large difference of dualities in recycled aggregates but also a little deterioration of mechanical properties in recycled aggregate concrete in comparison with that of natural aggregate concrete. In this study, the test results of freez and thaw durability of concrete with demolished-concrete recycled aggregate(DRA) arc as follows. Improvement of crushing process is an important assignment because that adhered mortar on source-concrete recycled aggregate(SRA) and DRA highly affects thc qualifies of recycled aggregate. The compressive strength of recycled aggregate concrete was not highly different in comparison with that of control concrete. But the resistance to penetration of Cl in recycled aggregate concrete was shown smaller than that of control concrete because of adhered mortar on recycled aggregate. The resistance to frcezing and thawing of recycled aggregate concrete was highly different due to adhered mortar on recycled aggregate, and durability factor of concrete with NA-SRA and DRA was more decreased than that of control concrete. On the other hand, durability factor of concrete with AA-SRA was larger than that of control concrete. It, therefore, is necessarily required that recycled aggregate including adequate entrained air should be used for satisfying the freez and thaw durability of recycled aggregate concrete.