• Applied Microscopy
• /
• v.47 no.1
• /
• pp.43-49
• /
• 2017

A new method was introduced to distinguish the ferrite, bainite and martensite in transformation induced plasticity (TRIP) steel by using electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). EBSD is a very powerful microstructure analysis technique at the length scales ranging from tens of nanometers to millimeters. However, iron BCC phases such as ferrite, bainite and martensite cannot be easily distinguished by EBSD due to their similar surface morphology and crystallographic structure. Among the various EBSD-based methodology, image quality (IQ) values, which present the perfection of a crystal lattice, was used to distinguish the iron BCC phases. IQ values are very useful tools to discern the iron BCC phases because of their different density of crystal defect and lattice distortion. However, there are still remaining problems that make the separation of bainite and martensite difficult. For instance, these phases have very similar IQ values in many cases, especially in deformed region; therefore, even though the IQ value was used, it has been difficult to distinguish the bainite and martensite. For more precise separation of bainite and martensite, IQ threshold values were determined by a correlative TEM analysis. By determining the threshold values, iron BCC phases were successfully separated.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.21-30
• /
• 1999

The present study were investigated changes of precipitation behaviour of laves phase in ferrite single phase and ferrite-martensite dual phase and precipitation of laves phase under stress. Hardness changes in ferrite phase appeared two hardness peaks by precipitation of initial fine precipitator and laves phase in 3Mo-0.3Si and 3Mo-0.3Si-C specimens, respectively. Hardness changes in martensite phase of 3Mo-0.3Si-C specimen was lower in the initial stage of aging by carbide precipitation and after this, increased by re-hardening due to precipitation of laves phase. In the ferrite phase, laves phase was mainly precipitated, whereas in the martensite phase, carbide was preferentially formed during the initial stage of aging and with increasing aging time, laves phase and carbide were simultaneously precipitated by precipitation of laves phase at around carbide. In the ferrite-martensite interface, laves phase was mainly precipitated and carbide was mainly formed at boundary of lath martensite than grain boundary. Adding the stress in aging, fine precipitator of inital precipitation of laves phase precipitated in (100) of perpendicular to tensile direction and has grown to only followed<010>direction and also, volume fraction of laves phase increased. Consequently, the stress added was accelerated initial precipitation of laves phase.

• Korean Journal of Materials Research
• /
• v.28 no.3
• /
• pp.129-134
• /
• 2018

This study was carried out to investigate the effect of grain size on the damping capacity of the Fe-26Mn-4Co-2Al damping alloy. ${\alpha}^{\prime}$ and ${\varepsilon}-martensite$ were formed by cold working, and these martensites were formed with a specific direction and surface relief. With an increase in grain size, the volume fraction of ${\alpha}^{\prime}$ and ${\varepsilon}-martensite$ increased by decrement the austenite phase stability. This volume fraction more rapidly increased in cold-rolled specimen than in the specimen that was not cold-rolled. The damping capacity also increased more with the augmentation an increased grain size and more rapidly increased in cold-rolled specimen than in the specimen that was not cold rolled. The effect of grain size on the damping capacity was larger in the cold-rolled specimen than the specimen that was not cold-rolled. Damping capacity linearly increased with an increase in volume fraction of ${\varepsilon}-martensite$. Thus, the damping capacity was affected by the ${\varepsilon}-martensite$.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.2
• /
• pp.112-120
• /
• 1996

The effects of ${\varepsilon}$ martensite content and strain amplitude on damping capacity of an Fe-17%Mn alloy have been studied to establish damping mechanism of Fe-Mn system corresponding to the magnitude of strain amplitude. In a range of $1{\times}10^{-4}{\sim}3{\times}10^{-4}$ strain amplitude, the damping capacity is linearly proportional to the ${\varepsilon}$ martensite content, which suggests that stacking faults and ${\varepsilon}$ martensite variant boundaries are the principal damping sources. In the range of $4{\times}10^{-4}{\sim}6{\times}10^{-4}$ strain amplitude, however, a maximum damping capacity is observed around 68 vol.% ${\varepsilon}$. This behavior is very similar to dependence of relative area of ${\gamma}/{\varepsilon}$ interface on ${\varepsilon}$ martensite content. This means that in this strain range, ${\gamma}/{\varepsilon}$ interface acts as damping source in addition to the stacking faults and variant boundaries in Fe-17%Mn alloy.

• Journal of Power System Engineering
• /
• v.17 no.2
• /
• pp.114-120
• /
• 2013

This study was carried out to investigate the relationship between mechanical properties and damping capacity in high manganese austenitic stainless steel with two phase mixed structure of reversed austenite and deformation induced martensite. Reversed austenite of ultra-fine grain size less than $0.3{\mu}m$ was obtained by reversion treatment. Two phase structure of deformation induced martensite and reversed austenite was obtained by annealing treatment at range of $500^{\circ}C{\sim}700^{\circ}C$ for various time in cold rolled high manganese austenite stainless steel. In stainless steel with two phase mixed structure of martensite and austenite, damping capacity decreased rapidly with the increasing hardness and strength. With the increasing elongation, damping capacity was increased rapidly and then, slowly increased.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.5
• /
• pp.283-292
• /
• 2004

The effects of the annealing parameters on microstructures were examined in a cold-rolled high strength steel containing 0.1% C, 0.5% Si, 1.5% Mn, and 0.04% Nb. It was impossible to avoid martensite in the microstructure even though the continuous annealing parameters were controlled. This indicates that the alloying elements such as silicon and manganese contributing to manganese equivalent($Mn_{eq}$) should be reduced to produce the ferrite-pearlite microstructure for the solid solution and precipitation hardened steel. It was found that a decrease in the rapid cooling temperature to $520^{\circ}C$ was effective to change the microstructure from ferrite-martensite to ferrite-pearlite-martensite. Typical dual-phase properties exhibiting a low yield ratio and a continuous yielding behavior were obtained when the rapid cooling temperature was in the range of $680^{\circ}C$ to $600^{\circ}C$. The critical volume fraction of martensite for the typical properties of dual-phase steel was about 11 percent.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.2
• /
• pp.85-90
• /
• 2000

The influence of transformation cycles (${\alpha}^{\prime}{\leftrightarrow}{\gamma}^{\prime}$) on the microstructure and mechanical properties of lath and lenticular martensites has been studied in Fe-Ni alloys. The width of lath in Fe-15%Ni alloy decreased with increasing the number of transformation cycles, while no appreciable change in dislocation density inside the lath was observed. In case of Fe-31%Ni alloy, a number of dislocations were additionally introduced into the martensite plate after the transformation cycling. Tensile strength and Vickers hardness of lath martensite decreased with the increase in number of transformation cycles, whereas those of lenticular martensite increased up to 1 cycle and then remained constant. Elongation of two alloys was deteriorated after 1 transformation cycling, corresponding to the tensile strength. But the decrement of elongation in Fe-31%Ni alloy was smaller than that in Fe-15%Ni alloy.

• Journal of Korea Foundry Society
• /
• v.13 no.5
• /
• pp.432-440
• /
• 1993

Ductile cast iron has a good ductility and toughness than those of gray cast iron, because the shape of graphite is spheroidal. Also, it has been reported that, additional strengthening and toughening of the ductile cast iron can be obtainded from the proper combination of matrix structures by the heat treatment and addition of alloying elements. In this study the effect of special heat treatment and addition of alloying elements(Ni, Mo) on the multi-phase(ferrite-bainite-martensite) structures, strength and toughness of ductile cast iron were studied systematically. In water quenching from $770^{\circ}C$, the martensite volume(%) increased, but the ferrite volume(%) decreased with increment of Ni content. In as cast, pearlite volume(%) and hardness increased with increment of Mo and Ni contents. And with the increment of the destabilization austempering holding time, the bainite volume(%) increased but the martensite volume(%) decreased. As destabilization austempering holding time is same, bainite volume(%) decreased, martensite increased with the increment of Ni and Mo contents. The hardness and tensile strength decreased, but impact energy increased with the decrease of Ni and Mo contents, and increment of holding time of destabilization austempering treatment.

• Advances in materials Research
• /
• v.4 no.1
• /
• pp.1-12
• /
• 2015

Low carbon steel of composition 0.05C - 0.18 Mn - 0.012 Si is intercritically annealed at temperatures $750^{\circ}C$, $775^{\circ}C$ and $800^{\circ}C$. The equilibrated alloys of different amounts of austenite with varying carbon contents are quenched in iced water. The same alloys are subcritically annealed at $675^{\circ}C$ and $700^{\circ}C$ for varying periods of times; the subcritically annealed alloy samples are quenched in iced water. Optical, scanning electron and transmission electron microscopy are carried out for all the samples. The dislocation structure, its distribution and density present in the above prepared duplex ferrite martensite steels are studied. The martensites are found to be highly dislocated due to lattice invariant deformation. At the same time ferrite adjoining the martensite areas also exhibits quite a high dislocation density. The high dislocation density is favorable for strain ageing and hence bakes hardenability. EDS analyses were carried out for both martensite and ferrite phases; it is found that the degree of supersaturation in ferrite together with carbon content in martensite varies with the process parameters. The microhardness test results show that the hardness values of different phases differ appreciably with process parameters. The microstructures and the corresponding microanalyses reveal that differently processed steels contain phases of varying compositions and different distribution.

• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.87-92
• /
• 2020

This study deals with the effects of austempering time on the microstructure and mechanical properties of ultra-high strength nanostructured bainitic steels with high carbon and silicon contents. The steels are composed of bainite, martensite and retained austenite by austempering and quenching. As the duration of austempering increases, the thickness of bainitic ferrite increases, but the thickness of retained austenite decreases. Some retained austenites with lower stability are more easily transformed to martensite during tensile testing, which has a detrimental effect on the elongation due to the brittleness of transformed martensite. With increasing austempering time, the hardness decreased and then remained stable because the transformation to nanostructured bainite compensates for the decrease in the volume fraction of martensite. Charpy impact test results indicated that increasing austempering time improved the impact toughness because the formation of brittle martensite was prevented by the decreased fraction and increased stability of retained austenite.