• 한국세라믹학회지
• /
• 제20권3호
• /
• pp.211-216
• /
• 1983

This work aims at characterizing silicon grains and its compacts. In order to remove iron silicon grains were washed with 5N hydrochloride at 60-7$0^{\circ}C$ for 170 hrs, and then followed the chemical analysis by atomic absorption spectrophotometer X-ray diffraction analysis SEM observation and specific surface area determination by B. E. T. Mixtures of graded silicon particles with two or three different sizes were made into packings by mechanical vibration. The mixtures were used to make compacts with 10 mm in diameter and 70mm in length by isostatically pressing at 1, 208 kg/$cm^2$ (20 kpsi) and 4, 255kg/$cm^2$ (60 kpsi) respectively. Bulk densities of packings and compacts were measured. A slip made of magnesium nitrate solution and fine silicon particles was spray-dried and then decomposed at 30$0^{\circ}C$ for the purpose of coating the uniform layer of magnesium oxide on the surface of particles. The results obtained are as follows: (1) About two thirds of iron content could be removed from silicon by washing silicon powders with hydrochloride. (2) Uniform layer of magnesium oxide on the surface of silicon could be prepared by spray-drying suspension and by decomposing it. (3) B. E. T. specific surface area of fine silicon particles was 2, 826.753$m^3$/kg. (4) In the binary system with two sizes of 40-53$\mu\textrm{m}$ particles and <10$\mu\textrm{m}$ particles the maximum bulk density of packing was 55% of theoretical value and that of compacts made at the pressure of 4, 255 kg./$cm^2$ (60 kpsi) was 73% of theoretical value. (5) In the ternary system with three sizes the maximum bulk density of packing was 1.43 g/$cm^3$and that of compacts was 1.80g/$cm^3$which is equivalent to 77.6% of theoretical value. The composition of the closest compact was consisted of 50% of 40-53$\mu\textrm{m}$ particles 20% of 10-30$\mu\textrm{m}$ particles and 30% of <10$\mu\textrm{m}$ parti-cles.

• 공학논문집
• /
• 제7권1호
• /
• pp.99-103
• /
• 2005

The ferrimagnetic resonance technique, with the inclusion of shaper anisotropy effects, was used to obtain information about the early stages in the precipitation of magnesium ferrite from iron-doped magnesia. The very small magnesioferrite particles were produced by precipitation method from solid solution of iron ion in single crystal magnesia. The temperature dependence of the resonance anisotropy field for a coherent assembly of hyperfine magnesium ferrite precipitates was investigated in the range 100~400K. The results are interpreted in terms of the shape anisotropy of the precipitates.

• 한국분말재료학회지
• /
• 제17권2호
• /
• pp.142-147
• /
• 2010

The ultrafine titanium carbonitride ($TiC_xN_y$) particles below 100 nm in mean size, including various carbon and nitrogen contents (x=0.55~0.9, y=0.1~0.5), were successfully synthesized by new Mg-thermal reduction process. Nanostructured sub-stoichiometric titanium carbide ($TiC_x$) particles were initially produced by the magnesium reduction of gaseous $TiCl_4+x/2C_2Cl_4$ at $890^{\circ}C$ and post heat treatments in vacuum were performed for 2 hrs to remove residual magnesium and magnesium chloride mixed with $TiC_x$. Finally, well C/N-controled $TiC_xN_y$ phases were successfully produced by nitrification heat treatment under normal $N_2$ gas atmosphere at $1150^{\circ}C$ for 2 hrs. The values of purity, mean particle size and oxygen content of produced particles were about 99.3%, 100 nm and 0.2 wt.%, respectively.

• 한국분말재료학회지
• /
• 제19권5호
• /
• pp.356-361
• /
• 2012

The ultra-fine and less agglomerated titanium carbonitride particles were successfully synthesized by magnesiothermic reduction with low feeding rate of $TiCl_4+1/4C_2Cl_4$ solution. The sub-stoichiometric titanium carbide ($TiC_{0.5{\sim}0.6}$) particles were produced by reduction of chlorine component by liquid magnesium at $800^{\circ}C$ of gaseous $TiCl_4+1/4C_2Cl_4$ and the heat treatments in vacuum were performed for 5 hours to remove the residual magnesium and magnesium chloride mixed with produced $TiC_{{\sim}0.5}$. The final $TiC_{{\sim}0.5}N_{0{\sim}0.5}$ particle with near 100 nm in mean size and high specific surface area of $65m^2/g$ was obtained by nitrification under nitrogen gas at $1,150^{\circ}C$ for 2 hrs.

• 한국주조공학회지
• /
• 제14권3호
• /
• pp.240-247
• /
• 1994

TiC particulate reinforced magnesium matrix composites were fabricated by melt stirring method. The effect of alloying elements on TiC particulate dispersion into molten magnesium and mechanical properties were investigated. The incorporation time is defined as the time required for dispersion of solid particles into molten metal. The incorporation time of TiC particles into molten pure magnesium was remarkably shorter and the particulated dispersion was more uniform than that of pure aluminum which was reported previously. The incorporation time was, prolonged by the addition of Al, Bi, Ca, Ce, Pb, Sn or Zn. The tensile strength increased and elongation decreased by the addition of Cu or Sn into the matrices and composites. Although, the tensile strength of the matrices and composites increased by alloying with Ca or Ce, the maximum elongation was observed at a content of about 1% for the matrices. By alloying with Zn, the tensile strength increased for the matrices and composites, but the elongation of the matrices increased. The pure magnesium and its alloy matrix composites reinforced with 20vol% TiC have the tensile strength of about 400MPa. This value is compared with the tensile strength of SiC whisker reinforced magnesium matrix composites fabricated by liquid infiltration method at the same volume fraction. There fore, the melt strirring method which has the advantages of simple process is considered to be efficient in fabricating magnesium matrix composites.

• 한국응용과학기술학회지
• /
• 제26권4호
• /
• pp.385-393
• /
• 2009

Different types magnesium hydroxide groups have been obtained using the hydrothermal precipitation technique from magnesium sulfate and calcium carbonate solution. The Mg atom coordinated around O atom of ${SO_4}^{2-}$ in another layer to form a multi-layer structure crystal. The influence of synthesis parameters on the morphological characteristics and size of magnesium hydroxide groups precipitated in aqueous were investigated such as different of additive and pH. Magnesium hydroxide groups were decomposed gradually and converted finally to MgO particles after heated in air temperature up to $1050^{\circ}C$. The particle size and it's distribution morphology, crystal phase and thermal behavior of the samples were characterized through XRD, SEM, EDS, and TG/DTA.

• 대한금속재료학회지
• /
• 제48권9호
• /
• pp.813-818
• /
• 2010

In current automobile and electronic industries, the use of magnesium alloys where both energy and weight saving are attainable is increasing. Despite their light weight, there has been an inherent drawback arising from the surface vulnerable to be oxidized with ease, specifically under corrosive environments. To protect magnesium alloy from corrosion, the present work deals with the electrochemical response of the oxide layer on magnesium alloy specimen prepared by plasma electrolytic oxidation (PEO) method in an electrolyte with zirconia powder. Surface observation using scanning electron microscopy evidences that a number of zirconia particles are effectively incorporated into oxide layer. From the results of potentio-dynamic tests in 3.5 wt% NaCl solution, the PEO-treated sample containing zirconia particles shows better corrosion properties than that without zirconia, which is the result of zirconia incorporation into the coating layer. Corrosion resistance is also measured by utilizing salt spray tests for 120 hrs.

• 한국가스학회지
• /
• 제19권3호
• /
• pp.25-31
• /
• 2015

본 연구에서는 부유 Mg분진의 최소발화온도(MIT)에 있어서 입자 체류시간이 어떠한 영향을 주는지를 실험자료와 입자속도의 계산결과를 사용하여 조사하였다. 평균입경이 증가하면 Mg분진의 MIT는 증가하는 반면에 입자 체류시간(Residence time)은 지수함수적으로 감소하여 분진의 발화 가능성이 저하되는 요인이 될 수 있음을 계산을 통해 확인할 수 있었다. 또한 온도증가에 의한 입자속도에의 영향은 평균입경이 클수록 미세하지만 증가하는 결과가 얻어졌다.

• 한국응용과학기술학회지
• /
• 제31권1호
• /
• pp.92-100
• /
• 2014

비이온계면활성제 가운데 솔비톨계 계면활성제인 Span을 이용해 수열합성법으로 수산화마그네슘을 합성하였다. 수산화마그네슘 합성의 전구체는 염화마그네슘과 수산화나트륨을 사용하였다. 비이온 계면활성제는 안정제와 분산제 그리고 표면 개질제로 적용하였다. 비이온 계면활성제를 첨가하였을 경우 수산화마그네슘 입자는 좀 더 작고 균일한 크기와 좋은 분산성을 나타내었으며, 소수성 성질을 나타내었다. 합성된 입자의 특성은 PSA, SEM, EDS, XRD 그리고 FT-IR을 통해 확인하였다. 기기 분석을 통해 개질 전과 후의 수산화마그네슘의 소수성, 분산성 특성을 비교하였다. 또한 실험조건에 따라 수산화마그네슘 입자의 표면 개질 특성 변화를 확인하였다.

• Advances in materials Research
• /
• 제1권3호
• /
• pp.169-182
• /
• 2012

In this paper the intrinsic influence of micron-sized nickel particle reinforcements on microstructure, micro-hardness tensile properties and tensile fracture behavior of nano-alumina particle reinforced magnesium alloy AZ31 composite is presented and discussed. The unreinforced magnesium alloy (AZ31) and the reinforced nanocomposite counterpart (AZ31/1.5 vol.% $Al_2O_3$/1.5 vol.% Ni] were manufactured by solidification processing followed by hot extrusion. The elastic modulus and yield strength of the nickel particle-reinforced magnesium alloy nano-composite was higher than both the unreinforced magnesium alloy and the unreinforced magnesium alloy nanocomposite (AZ31/1.5 vol.% $Al_2O_3$). The ultimate tensile strength of the nickel particle reinforced composite was noticeably lower than both the unreinforced nano-composite and the monolithic alloy (AZ31). The ductility, quantified by elongation-to-failure, of the reinforced nanocomposite was noticeably higher than both the unreinforced nano-composite and the monolithic alloy. Tensile fracture behavior of this novel material was essentially normal to the far-field stress axis and revealed microscopic features reminiscent of the occurrence of locally ductile failure mechanisms at the fine microscopic level.