• Fashion & Textile Research Journal
• /
• v.11 no.3
• /
• pp.474-480
• /
• 2009

The purpose of this study is to prepare the hardness of polyester(PET) fabric by thermal bonding with low melting component of bicomponent fiber and to describe the change of physical properties of thermal bonded PET fabrics. The PET fabrics were prepared with regular PET fiber as warp and bicomponent fiber as weft. The bicomponent fiber of sheath-core type were composed with a regular PET core and low melting PET sheath. The thermal bonding of PET fabric was carried out in pin tenter from 120 to $195^{\circ}C$ temperature range for 60 seconds. In this study, we investigated the physical properties and melting behavior of PET fiber and the effect of the temperature of the pin tenter on the thermal bonding, mechanical properties. Melting peak of warp showed the thermal behavior of general PET fiber. However, melting peak of weft fiber(bicomponent fiber) showed the double melting peak. The thermal bonding of the PET fabric formed at about temperature of lower melting peak. The optimum thermal bonding conditions for PET fabrics was applied at $190{\sim}195^{\circ}C$ for 60seconds by pin tenter. On the other hand, the tensile strength of the PET fabric decreased with an increasing temperature of thermal bonding.

• Korean Journal of Human Ecology
• /
• v.12 no.4
• /
• pp.529-537
• /
• 2003

This study was conducted to manufacture the soluble micro-fiber and to synthesize low melting polymer for the interior fabric not to use the polyurethane resin causing some problems. Low melting polyester for weft yarn was introduced by adding 30-40 mol% ratio of isophthalic acid to a main chain of polyethylene terephthalate to decrease the melting temperature up to heat setting temperature. Micro-fiber for warp yarn consisted of both soluble and insoluble components with multi-layered structure. When the soluble micro-fiber was treated by alkaline hydrolysis with 3-5% concentration of NaOH, it showed the turning point at 28% weight loss since soluble polyester was hydrolyzed approximate five times faster than regular polyester.

• Journal of Fashion Business
• /
• v.13 no.1
• /
• pp.82-90
• /
• 2009

This research was made to manufacture the fabric for interior uses by spinning a low melting mono 4 denier PET staple fiber with a soluble 1.4 denier fine PET fiber. The blended yarn has a thickness ranging from 10's to 14's, and the soluble PET fine fiber was dissolved to make a pore in the polymer. Thereby a snap property was decreased and a resilience property was improved to be suitable for a functional synthetic leather. In order to attain the optimum condition, a mechanical property according to fineness, and mixing ratio of low melting polymer, warp density, weft density and blending ratio, and a heat contraction ratio according to blending ratio were experimented. The warp density, 220 T/inch of fine denier PET and the weft density, 64 T/inch of thick denier PET were generated to 4/4 both twill weave fabric having constant tensile property and thickness.

• Fashion & Textile Research Journal
• /
• v.11 no.4
• /
• pp.661-666
• /
• 2009

The purpose of this study is to analyze the dyeability of polyester(PET) fabric by thermal bonding with low melting component of bicomponent fiber and to describe the change of physical properties of thermal bonded PET fabrics. The PET fabrics were prepared with regular PET fiber as warp and bicomponent fiber as weft. The bicomponent fiber of sheath-core type was composed with a regular PET core and low melting PET sheath. The thermal bonding of PET fabric was carried out in pin tenter($195^{\circ}C$) for 60 seconds. In this study, we investigated the dye ability and fastness of the dyed PET fabric. Dye ability of E-type dyestuff is higher than S-type dyestuff. In the case of E- type dyestuff, the saturated dyeing time was 10minutes at $130^{\circ}C$. The washing fastness and light fastness were excellent as 4-5grade.

• Textile Coloration and Finishing
• /
• v.21 no.3
• /
• pp.37-42
• /
• 2009

The low melting PET yarn has sheath/core structure: sheath portion consists of low melting point PET and core portion is regular PET. Dyeing properties of fabric made from low melting PET yarn were investigated at different dyeing temperatures. It was found that the exhaustion yield on the low melting PET fabric was higher than on regular PET fabric. The total K/S value of the dyed low melting PET fabric increased as heat setting temperature increased above $150^{\circ}C$ because the sheath portion of the low melting yarn melted. Although fastness to light of the low melting PET fabric was similar to regular PET fabric, fastness to washing was inferior to regular PET fabric by 1 grade.

• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.173-183
• /
• 2012

Recently, experimental studies to prevent explosive spalling based on spalling mechanism and addition of Polypropylene fiber in high strength concrete (HSC) are performed actively. However, with respect to ultra high strength concrete (UHSC), its compact internal structure is more difficult release vapor pressure at rapid rising temperature compared to HSC. Therefore, in this study, an experiment was conducted to evaluate spalling properties of UHSC using ${\Box}$ $100mm{\times}100{\times}H200mm$ rectangular specimen according to ISO-834 standard fire curve. With respect melting point of fiber, three fiber types of Polyethylene, Polypropylene, and Nylon fibers with melting temperature of $110^{\circ}C$, $165^{\circ}C$, and $225^{\circ}C$, respectively, were considered. Mixed fiber of 0.15% and 0.25% of concrete volume was used to consider spalling properties based on water vapor pressure release. Then, TGDTA test on fiber and FEM analysis were performed. The results showed that it is difficult to prevent initial spalling without loss of fiber mass even if fiber melting temperature is low. Also, in preventing thermal spalling, fiber that melts to rapidly create porosity within 10 minutes of fire is more effective than that of low melting temperature property of fiber.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.20 no.3
• /
• pp.342-349
• /
• 2011

The purpose of this paper is to describe experimental results about the butt welding and bead on plate welding of the high power Continuous Wave (CW) Fiber laser for Ultra-low carbon Interstitial Free(IF) steel plate for gear part of car. After being welded of the gear parts by the fiber laser and electron beam Microstructures of melting zone had been mixed acicular, granular bainitic, quasi-polygonal and widmanstatten ferrite because of a radical thermal diffusion after welding, difference of critical volume and grain size. As a result of experiment, when gear parts were welded by the fiber laser and electron beam, the fiber laser welding has been stable properties without internal defects more than the electron beam welding. Therefore it has the very advantages of welding high quality and productivity more than conventional melting method. The optimal welding processing parameters for gear parts were as follows : the laser power and welding speed were 3kWatt, 30mm/sec respectively. At this time heat input was $21.2{\times}10^3J/cm^2$.

• Textile Coloration and Finishing
• /
• v.24 no.2
• /
• pp.113-120
• /
• 2012

Jacquard floor covering could be prepared from low-melting/regular sheath-core hybrid polyester, where the fiber is dyed in yarn state. With regard that the expected high shrinkage of the hybrid polyester in water makes problems in yarn dyeing, low-temperature dyeing properties of the hybrid polyester were studied. The rate of shrinkage of low-melting hybrid polyester exceeds 9% in hot water above $90^{\circ}C$, at such condition, cheese yarn dyeing is very difficult. Although disperse dyes exhaust in a relatively high speed on low-melting hybrid polyester, diffusion of these dyes to the core regular polyester was extremely slow under $90^{\circ}C$. Foron Blue E-BL 150, an anthraquinone E-type disperse dye, showed appreciable diffusion after 48hrs dyeing at $90^{\circ}C$. The fastness to rubbing and drycleaning were improved by one grade after reduction cleaning.

• Proceedings of the Korean Fiber Society Conference
• /
• 1997.04a
• /
• pp.328-332
• /
• 1997

Hot stretching focused on the improvement of properties of poly(L-lactic acid) fiber. Some aliphatic polyesters are biodegradable under microbial attack and the new unique applications are expected. Generally, these materials have a somewhat low melting temperature and low mechanical properties compared with the aromatic polyesters. In this study, melt-spinning of poly(L-lactic acid) was conducted. We investigated effects of the stretching and the molecular orientation of aliphatic polyester fibers on the change of fine-structure. Glass transition temperature, molecular orientation and crystallinity increased according to the increase of stretching ratio.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.76-79
• /
• 2003

Recently, many attempts have been made to develop high strength and high modulus fibers from conventional polymers such as poly(vinyl alcohol) (PVA)[1-4] and polyethylene (PE). PVA has potentiality to yield high strength and high modulus fiber, since they have high theoretically attainable moduli because of their planar zig-zag structure. As PVA has a melting temperature as high as 230$^{\circ}C$ in contrast to PE with a low melting temperature such as 130$^{\circ}C$, it seems possible that high strength and high modulus fibers comparable to Aramid can be fabricated from PVA. (omitted)