• Structural Engineering and Mechanics
• /
• 제76권5호
• /
• pp.663-674
• /
• 2020

In this study, partially restrained beam-column moment joints in the weak-axis direction were examined using three large-scale specimens subject to cyclic loading in order to assess the seismic resistance of the joints of low-rise steel structures and to propose joint details based on the test results. The influence of different number of bolts on the moment joints was thoroughly investigated. It was found that the flexural capacity of the joints in the direction of weak axis was highly dependent on the number of high-tension bolts. In addition, even though the flexural connections subjected to cyclic loading was perfectly designed in accordance with current design codes, severe failure mode such as block shear failure could occur at beam flange. Therefore, to prevent excessive deformation at bolt holes under cyclic loading conditions, the holes in beam flange need to have larger bearing capacity than the required tensile force. In particular, if the thickness of the connecting plate is larger than that of the beam flange, the bearing capacity of the flange should be checked for structural safety.

• International Journal of Naval Architecture and Ocean Engineering
• /
• 제11권2호
• /
• pp.671-678
• /
• 2019

In this paper, the low cycle fatigue failure and ratcheting behavior, as well as their interaction of AH32 steel were experimentally investigated under uniaxial cyclic loading. The effects of mean stress, stress amplitude and stress ratio on the low cycle fatigue life and ratcheting strain were discussed. It was found that the ratcheting strain increased while the fatigue life decreased with the increase of mean stress and stress amplitude, and the increasing stress ratio would result in smaller ratcheting and larger fatigue life. Two kinds of failure modes, i.e. low cycle fatigue failure due to crack propagates and ratcheting failure due to large plastic strain will take place respectively. Based on the experimental results, considered the effect of ratcheting on fatigue life, a model with the maximum stress and ratcheting strain rate was proposed. Comparison with the experimental result showed that the new model provided a good prediction for AH32 steel.

• 멤브레인
• /
• 제14권4호
• /
• pp.289-297
• /
• 2004

유기물과 질소를 동시에 제거하기 위하여 연속회분식으로 운전한 MBR (membrane bioreactor)시스템에서 미생물농도와 슬러지 부하량이 막오염과 미생물 활성에 미치는 영향을 살펴보았다. 막오염은 MLSS (mixed liquor suspended solid) 농도 증가에 따라 조금씩 증가하는 경향을 보였고, 그 효과는 비포기 조건보다 포기 조건에는 좀더 두드러지게 나타났다. MLSS 농도는 막오염에 직접적인 커다란 영향을 주지는 않으나, 지나치게 높은 MLSS에서 유도되는 낮은 슬러지 부하에서는 막오염이 크게 증가하는 현상이 발견되었고, 이러한 조건에서는 포기에 의한 막 세척 효과도 크게 줄어들었다. 미생물의 개별 활성도는 슬러지 부하가 감소할수록 지속적으로 감소하는 경향을 나타내었다 반응조 전체 활성도 또한 17,000 mg/L 이상의 높은 MLSS로부터 유도되는 낮은 슬러지 부하율에서는 높은 미생물 농도에도 불구하고 오히려 감소했는데 이는 기질 부족으로 인한 경쟁으로 활성도가 떨어지고, 용액의 점성 증가로 인해 산소 전달율이 저하되었기 때문이다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2004년도 추계학술대회 논문집
• /
• pp.487-490
• /
• 2004

In this paper, we investigated the characteristics of initiation and propagation behavior for fatigue crack observed by changing various shapes of initial crack and magnitudes of loading in modified compact tension shear(CTS) specimen subjected to shear loading. In the low-loading condition, the secondary fatigue crack was created in the notch root due to friction on the pre-crack face grew to a main crack. In the high-loading condition, fatigue crack under shear loading propagated branching from the pre-crack tip. Influenced by the shear loading condition, fatigue crack propagation retardation appeared in the initial propagation region due to the reduction of crack driving force and friction on crack face. In both cases, however, fatigue cracks grew in tensile mode type. The propagation path of fatigue crack under the Mode II loading was 70 degree angle from the initial crack regardless of its shape and load magnitude.

• Journal of Microbiology and Biotechnology
• /
• 제9권3호
• /
• pp.265-270
• /
• 1999

A three phase fluidized bed bioreactor immobilized with Thiobacillus sp. IW was tested to remove hydrogen sulfide and methylmercaptan with high loading rate. In a single gas treatment, the bioreactor removed 92- 98％ of hydrogen sulfide with loading rate of 15- 66 g/l/h and removed 87-98％ of methylmercaptan with loading rate of 14-60 gl/sup -1/h/sup -1/. In the mixed gas treatment, the removal efficiencies of hydrogen sulfide and methylmercaptan maintained at 89-99％ for various inlet loading rates and were not affected by the inlet loading ratio of both gases in low loading rates. When the inlet concentration of methylmercaptan increased 3.8 times and was maintained for 30 h to observe the response of the bioreactor to sudden environmental change, the removal efficiency of methylmercaptan was maintained at an average of 91％.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.302-307
• /
• 2004

This paper reviewed characteristics of fatigue crack behavior observed by changing various shapes of initial crack and magnitudes of loading in compact tension shear(CTS) specimen subjected to shear loading. In the high-loading condition, fatigue crack under shear loading propagated branching from the pre-crack tip. Meanwhile, the secondary fatigue crack in the low-loading condition which was created in the notch root due to friction on the pre-crack face grew to a main crack. Influenced by the mode II loading condition, fatigue crack propagation retardation appeared in the initial propagation region due to the reduction of crack driving force and friction on crack face. In both cases, however, fatigue cracks grew in tensile mode type. Propagation path of fatigue crack under the shear loading was 70 degree angle from the initial crack regardless of its shape and load magnitude.

• Steel and Composite Structures
• /
• 제39권3호
• /
• pp.229-241
• /
• 2021

This work focused on aluminum foam sandwich (AFS) with different foam core densities and different face-sheet thicknesses subjected to constant amplitude three-point bending cyclic loading to study its fatigue performance. The experiments were conducted out by a high frequency fatigue test machine named GPS-100. The experimental results showed that the fatigue life of AFS decreased with the increasing loading level and the structure was sensitive to cyclic loading, especially when the loading level was under 20%. S-N curves of nine groups of AFS specimens were obtained and the fatigue life of AFS followed three-parameter lognormal distribution well. AFS under low cyclic loading showed pronounced cyclic hardening and the static strength after fatigue test increased. For the same loading level, effects of foam core density and face-sheet thickness on the fatigue life of AFS structure were trade-off and for the same loading value, the fatigue life of AFS increased with aluminum foam core density or face-sheet thickness monotonously. Core shear was the main failure mode in the present study.

• 산업기술연구
• /
• 제22권A호
• /
• pp.3-8
• /
• 2002

In this study, extremely low cycle fatigue tests were carried out under push-pull loading conditions using graphite cast iron (GCD). In order to clarify the fatigue fracture mechanism of GCD in an extremely low cycle fatigue regime successive observations of internal fatigue damage were performed. The results obtained are as follows. (1) The process of extremely low cycle fatigue can be classified into three stages which are composed of the generation, growth and coalescence of microvoids inside materials. (2) In an extremely low cycle fatigue regime, microvoids originate from debonding of graphite-matrix interface.

• Nuclear Engineering and Technology
• /
• 제33권5호
• /
• pp.526-538
• /
• 2001

Fatigue tests in air and in room temperature water were performed to obtain comparable data and stable crack measuring conditions. In air environment, fatigue crack growth rate was increased with increasing temperature due to an increase in crack tip oxidation rate. In room temperature water, the fatigue crack growth rate was faster than in air and crack path varied on loading conditions. In simulated light water reactor (LWR) conditions, there was little environmental effect on the fatigue crack growth rate (FCGR) at low dissolved oxygen or at high loading frequency conditions. While the FCGR was enhanced at high oxygen condition, and the enhancement of crack growth rate increased as loading frequency decreased to a critical value. In fractography, environmentally assisted cracks, such as semi-cleavage and secondary intergranular crack, were found near sulfide inclusions only at high dissolved oxygen and low loading frequency condition. The high crack growth rate was related to environmentally assisted crack. These results indicated that environmentally assisted crack could be formed by the Electrochemical effect in specific loading condition.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 추계학술대회
• /
• pp.1045-1050
• /
• 2003

In this study, to investigate the effects of omitting low-amplitude cycles from a flight-simulation loading, crack growth tests are conducted on 2124-T851 aluminum alloy specimens. Three test spectra are generated by omitting small load ranges as counted by the rain-flow count method. The crack growth test results are compared with the data obtained from the flight-simulation loading. The experimental results show that omission of the load ranges below 5% of the maximum load does not significantly affect crack growth behavior, because these are below the initial stress intensity factor range. However, in the case of omitting the load ranges below 15% of the maximum load, crack growth rates decrease, and therefore crack growth curve deviates from the crack growth data under the flight-simulation loading. To optimize the load range that can be omitted, crack growth curves are simulated by the stochastic crack growth model. The prediction shows that the omission level can be extended to 8% of the maximum load and test time can be reduced by 59%.