• Journal of the Korea Institute of Building Construction
• /
• v.11 no.3
• /
• pp.256-264
• /
• 2011

By implementing an analysis on the liquid flame proof agent infiltration of microwave-heated wood under soaking conditions (room temperature soaking, heat soaking), its correlation with wood temperature, and the structure of wood and permeating components after soaking in flame proof agent, which was carried out as basic research in order to improve the fire resistance performance of the wood itself, it is found that the infiltration increases as the microwave heating time increases, while for heat soaking, it is found that high infiltration as well as the stable permeability of flame proof agent is achievable. Also, when the wood temperature is more than $80^{\circ}C$, the infiltration by the flame proof agent increased, and a very even infiltration of flame proof agent was observed, which implies that the liquid flame proof agent has a dependency on temperature change of the wood as a condition to penetrate into the wood. As a result of fine structure analysis, the flame proof agent transfer between cells through pits was considered as a cause to increase the infiltration of flame proof agent, and it is also shown that for heat soaking among the permeating component analysis, as the crystallized flame proof agent around the heartwood and sapwood inner pits increases, the flame proof agent can penetrate into the the heartwood part.

• Journal of the Korea Institute of Building Construction
• /
• v.11 no.2
• /
• pp.162-170
• /
• 2011

As the result of implementing a treated material test and durability test after quickly drying S.P.F. species, a type of softwood structural material, within a short period time, soaking it in liquid phosphate flame proof agent for an hour, microwave heating it, and compressing it from 3.8cm to 1cm, when setting the appropriate heating time of microwave heating at 7 minutes at 5kW, it is observed that it satisfies the target water content (4~5%). It is shown that in a water content measurement of the wood that is compressed after being softened by soaking in the flame proof agent, drying and heating at 3kW for 9 minutes, all specimens satisfied 12~14%, the appropriate water content for exterior wood. Also, it is shown that in terms of the flame performance obtained through a flame resistance treatment of the compressed wood and a treated material test, the specimen soaked in flame proof agent for 30 minutes was the most excellent, and that the performance test result of the compressed wood in all areas, such as nail withdrawal resistance, compression, bending strength, and shearing strength, were all improved in their mechanical features to twice to three times better performances.