• Journal of Korea Foundry Society
• /
• v.36 no.5
• /
• pp.167-173
• /
• 2016

The effect of various types of heat-treatment on the mechanical properties of cast Alloy 718 has been investigated. Cast Alloy 718 bars were subjected to 'standard heat-treatment'_(SHT), 'HIP (Hot Isostatic Pressing) heat-treatment'_(HHT), and 'HIP-simulated heat-treatment'_(HS). In the absence of long time high temperature heat-treatment, a small amount of Laves phase remained in the 'SHT' specimen, and needle shaped ${\delta}$ precipitated in the vicinity of the Laves phase. Due to the formation of the Laves and ${\delta}$ phases in the 'SHT' specimen, it exhibited lower tensile properties than those of the others_specimens. On the other hand, the Laves phase was completely dissolved into the matrix after 'HHT' and 'HS' treatments. It is known that isostatic pressure reduces the self-diffusion coefficient, because of the lower self-diffusivity under HIP conditions in the interdendritic region, Nb segregation and the high amount of ${\gamma}^{{\prime}{\prime}}$ precipitation that occurs. Due to the higher fraction of coarse ${\gamma}^{{\prime}{\prime}}$ phases, the 'HHT' treated Alloy 718 showed excellent tensile strength.

• Journal of Magnetics
• /
• v.16 no.4
• /
• pp.337-341
• /
• 2011

The magnetic and magnetocaloric properties of $Gd_{1-x}Ce_xAl_2$ (x = 0, 0.25, 0.5, 0.75) intermetallic compounds alloys have been investigated in detail for the first time. XRD patterns indicated that all the samples were crystallized in a single phase with $MgCu_2$-type structure (Laves phase). Ce substitution for Gd increased the lattice parameters and decreased the Curie temperature from 163 K for x = 0 to 37 K for x = 0.75. A maximum entropy change of 3.82 J/kg K was observed when a 2 T magnetic field was applied to the x = 0 sample. This entropy change decreased with increasing Ce content to 2.04 J/kg K for the x = 0.75 sample.

• Korean Journal of Materials Research
• /
• v.6 no.11
• /
• pp.1099-1106
• /
• 1996

니켈-수소화물전지의 음극재료로서 주목을 받고 있는 다원계 Zr기 Laves 합금의 조성에 따른 결정구조, 방전특성등을 조사하였다. 전극은 아크 용해한 합금을 분쇄한 분말과 PVA를 다공성니켈 foam에 충진하여 제작하였고 충방전시험은 6M KOH 용액중에서 수행하였다. 대상 합금은 ZrNi2를 기본조성으로 하여 이중 Ni의 일부를 V, Mn, Cr, Mo 또는 W로 치환한 삼원계 및 사원계 합금이었다. 이들 합금의 충방전 실험결과 ZrV0.5Mn0.5Ni1.0의 경우가 260 mAh/g로 가장 높은 방전용량을 나타내었다. 이 합금의 방전용량은 방전전류밀도의 영향을 크게 받았으며 10 mA/g과 200mA/g의 방전전류에서 각각 300mAh/g와 150mAh/g이었다. 이 합금을 110$0^{\circ}C$에서 열처리한 경우 저율방전시에는 방전용량의 변화가 거의 없었으나 수소의 확산이 율속이 될 것으로 생각되는 고율 방잔시에서는 방전용량이 현저하게 감소하였다. 이러한 현상은 열처리에 의해 수소의확산을 용이하게 해주는 격자결함이 감소하기 때문이 아닌가 생각된다.

• Korean Journal of Materials Research
• /
• v.15 no.1
• /
• pp.19-24
• /
• 2005

For the good combination of high-temperature strength, toughness and creep property, $9-12\%$ chromium steels are often used for gas turbine compressors, steam turbine rotors, blade and casing. In this study, the correlation of microstructural evolution and mechanical properties was investigated fur the specimens heat-treated at 600, 650 and $700^{\circ}C$ for 1000, 3000 and 5000 hrs. The microstructure of as-received specimen was tempered martensite with a high dislocation density, small sub-grains and fine secondary phase such as $M_23C_6$. Aging for long-time at high temperature caused the growth of martensite lath and the decrease of dislocation density resulting in the decrease in strength. However, the evolution of secondary phases had influence on hardness, yield strength and impact property. In the group A specimen aged at $600^{\circ}C\;and\;650^{\circ}C$, Laves phase was observed. The Laves phase caused the increase of the hardness and the decrease of the impact property. In addition, the abrupt growth of secondary phases caused decrease of the impact property in both A and B group specimens.

• Transactions of the Korean hydrogen and new energy society
• /
• v.7 no.1
• /
• pp.11-18
• /
• 1996

The Laves phase alloy hydrides have some promising properties as electrode materials in reversible metal hydride batteries. In this work, the hydrogen storage performance, crystallographic parameters, surface morphology, surface area and electrochemical characteristics of the non-stoichiometric $ZrMn_{0.3}V_{0.7}Ni_{1.4+{\alpha}}$, $ZrMn_{0.5}V_{0.5}Ni_{1.4+{\alpha}}$($\alpha$ =0.0, 0.2, 0.4, 0.6) alloys were examined. These as-cast alloys were found to have mainly a cubic C15-type Laves phase structure by X -ray diffraction analysis. The equilibrium pressure of the alloy were increased as $\alpha$ increased in both two types alloy. In case of $ZrMn_{0.5}V_{0.5}Ni_{1.4+{\alpha}}$ alloys, discharge efficiency and the rate capability of the alloy were decreased as $\alpha$ increased but, these values were increased in case of $ZrMn_{0.3}V_{0.7}Ni_{1.4+{\alpha}}$ alloys. The differences of these electrode properties observed were dependent on the reaction surface area and the catalytic activity of unit area of the each electrode.

• Transactions of the Korean hydrogen and new energy society
• /
• v.5 no.1
• /
• pp.1-8
• /
• 1994

Lattice structure, hydrogen absorption characteristics, discharge capacity and cycle life of $V_{22}Ti_{16}Zr_{16}Ni_{39}X_7$(X= Cr, Co, Fe, Mn, Al) alloys were investigated. The matrix phases of these alloys were the C14 Laves phase. Chromium-containing alloy had a vanadium-rich phase in addition to the Laves phase. The chromium, maganese, or aluminum-containing alloys had lower hydrogen equilibrium pressure and larger hydrogen absorption content than the cobalt or iron-containing alloys. The discharge capacities of these alloys were 270~330mAh/g. The discharge capacity according to the alloying element X decreased in the order of Mn>Cr>Co, Al)Fe. The charge/discharge cycle lives of the chromium, cobalt or iron-containing alloys were longer than those of maganese or aluminum-containing alloys due to the lower vanadium dissolution rate.

• Transactions of the Korean hydrogen and new energy society
• /
• v.19 no.6
• /
• pp.482-489
• /
• 2008

Ti-Cr alloys consist of BCC solid solution, C36, C14 and C15 Laves phase at high temperature. Among others, the BCC solid solution phase was reported to have a high hydrogen storage capacity. However, activation, wide range of hysteresis at hydrogenation/dehydrogenation, and degradation of hydrogen capacity due to hydriding/dehydriding cycles must be improved for its application. In this study, to improve such problems, we added a Nb. For attaining target materials, Ti-10Cr-xNb(x=1, 3, 5wt.%) specimens were prepared by arc melting. The arc melting process was carried out under argon atmosphere. As-received specimens were characterized using XRD(X-ray diffraction), SEM(Scanning Electron Microscopy) with EDX(Energy Dispersive X-ray) and TG/DSC(Thermo Gravimetric Analysis/Differential Scanning Calorimetry). In order to examine hydrogenation behavior, the PCI(pressure-Composition-Isotherm) was performed at 293, 323, 373 and 423K.

• Transactions of the Korean hydrogen and new energy society
• /
• v.4 no.1
• /
• pp.11-19
• /
• 1993

The kinetic studies of the hydrogen induced amorphization in $ErCo_2$ Laves phase is observed by the internal standard method using X-ray diffraction intensities. The activation energy and rate constant exponent for the amorphization in $ErCo_2$ are found to be 26 kcal/mole and 0.78, respectively. From these results, it is believed that the mechanism of the hydrogen induced amorphization in $ErCo_2$ is related to the motion of Co atoms. Though there are many similar physical properties between $ErCo_2$ and $ErNi_2$, the activation energy for the amorphizatin in $ErCo_2$ is larger than that in $ErNi_2$ and the amorphization rate in $ErCo_2$ is slower. It is suggested that these differences of activation energy for the hydrogen induced amorphization and the amorphization rate between $ErCo_2$ and $ErNi_2$ is due to the occurence of structural change on forming crystalline hydride.

• Transactions of the Korean hydrogen and new energy society
• /
• v.8 no.3
• /
• pp.121-129
• /
• 1997

$ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ alloy ingot (bulk alloy) made by the arc melting was found to be consisting of mostly of $ZrV_{0.2}Mn_{0.98}Ni_{1.04}$ matrix alloy and $ZrV_{0.01}Mn_{0.13}Ni_{1.2}$ 2nd phase alloy. The former alloy had the form of the C15 type Laves alloy structure and the latter one had the intermetallic compound structure of $Zr_9Ni_{11}$. In order to investigate the effect of these two phases on the electrochemical charge-discharge characteristics of bulk $ZrV_[0.1}Mn_0.7}Ni_{1.2}$ alloy, the matrix and the 2nd phase alloys were fabricated separately by arc melting method and their electrochemical characteristics were studied and compared with the bulk alloy. It was found that the discharge capacity was the lowest of 160 mAh/g in the 2nd phase alloy. The matrix alloy exhibited 200 mAh/g. Both were lower than that of the bulk alloy of 250 mAh/g. The matrix and the bulk alloys showed a similar properties in the activation stage, the high rate dischargeability and the self discharge characteristics. Also a signigicant capacity decrease was observed after activation in both alloys. Whereas the 2nd phase alloy showed the very different characteristics. This alloy was found to be difficult to activate. However the capacity was remained constant after the activation. Also the self discharge rate was seen to be better than those of the matrix and the bulk alloys.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.1
• /
• pp.27-34
• /
• 2000

This present study were investigated effect of Ni contents on the microstructure and strength characteristic in 9Cr ferritic heat-resistant steel added 1.7%W in place of Mo in order to restrain laves phase formation. The result obtained from this study are as follow. Volume fraction, number of particles per unite area and particle size of carbide decreased with increase of Ni contents. Other side, carbides of $M_{23}C_6$ type was mainly precipitated in this steel, but laves phases could not precipitated in spite of increasing of aging time. With increase of tempering temperature, hardness was increased, and maximum value was showed around 873k by secondary hardening due to precipitation of $W_2C$ type carbide and then, was decreased. Tensile and yield strength due to decrease precipitation amount of carbide and number of particles per unite area was decreased, but elongation and impact value was increased. In case of aged specimen after tempering than tempered specimen, strength was higher and elongation was lower due to increasing of precipitated amount of carbide and number of particles per unite area.