• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.1
• /
• pp.11-16
• /
• 2011

This study was carried out in order to elucidate the effect of latex dosage and properties on aging behavior of coated paper. The coated paper with five different coating formulations were prepared and also four different latices were used. The coated paper were thermally aged at $105^{\circ}C$ for 14 days and the optical properties were measured. Increasing latex content increased the magnitude of reduction in brightness and whiteness. In addition, the variations in CIE a$^*b^*$ were larger with increasing latex dosage. Latex which has the lower gel content and the higher Tg showed the higher reduction in brightness and whiteness and much variation in CIE a$^*b^*$. However the particle size of latex didn't affect to thermal behavior of coated paper. These results indicate that latex which has higher Tg and lower gel content is the one of the main factors affecting aging behavior of coated paper.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 1999.04a
• /
• pp.7-16
• /
• 1999

The aim of this research was to evaluate the influences of coating components and structures on ink absorbency. The ink absorbency was measured as porosity, K&N ink absorption, gloss and ink set-off. In order to obtain the relationship between the coating structure and the ink absorbency, the binder level was adjusted and two types of pigments were examined. One of the pigments was known to make the porous coating structure and the other one had strong ink affinity. The effects of coating components were studied by applying six different types of latex and various additives . In this research, CLC(cylindrical laboratory coater) and Prufbau printability tester were used. It was found that the decreasing latex dosage and introducing porous pigment were effective solutions to increase ink absorbency. However, the ink absorbency could not be improved by applying the fine pigment even though it had strong ink affinity. Among the characters of the latex, particle size and surface tension were found to have the strong effect on ink absorbency. The ink absorbency increased with large particle size and low surface tension latex. The additives were varied and it was found that applying to the top coating was effective.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.47 no.1
• /
• pp.10-16
• /
• 2015

Bio-binder is well known as a promising alternative binder for SB latex because it is eco-friendly and inexpensive, compared to synthetic latex. SB latex in top coating color was substituted with starch-based bio-binder to investigate its effects on the coating color and its coated paper properties. Bio-binder contributed to the increase of coating color viscosity, and the improvement of water retention. Most optical properties except opacity were deteriorated by the increase of bio-binder dosage. It was also found that the increase of bio-binder substitution in top coating color brought about the increase of roughness, and decrease of coated paper gloss, print gloss, dry and wet pick strength. However the stiffness and the ink set-off of the bio-binder coated paper were improved. Overall, mostly adverse effects of bio-binder on the properties of coating color and its paper were observed. Therefore, it is not recommended to use bio-binder as top coating color.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.1
• /
• pp.17-22
• /
• 2011

The conventional coated paper has many functional problems for printed RFID tag. This study was carried out in order to evaluate the effect of coating color components on conductivity of printed coated paper. It has been well known that the efficiency of printed RFID tag is influenced by surface properties of substrate. The required properties for suitable substrate of printed RFID tag are high smoothness and waterproof property. In this study high grammage base paper surface sized with PVA was used. Coated paper was manufactured with five different formulations. Types of coating pigments and dosage of latex were varied. It was obtained high smoothness and also less binder demand with clay than GCC. On the other hand, suitable surface resistance and smoothness of coated paper for RFID tag was obtained with 20% of latex. Besides it shows the possibility of using coated paper for printed RFID tag.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2011.04a
• /
• pp.339-347
• /
• 2011

This study was carried out in order to manufacture the high quality coated paper. High quality coated paper includes not only present state but also the state of the future. So in this study, acrylic-styrene emulsion which polymerized in laboratory was compared with SB(Styrene-butadiene) latex during thermal aging. The coated paper with three different formulations which controlled the dosage of acrylic-styrene emulsion were prepared. The coated paper were thermally aged at $105^{\circ}C$ for 18days and the optical properties were measured. Brightness, whiteness and CIE L value were higher during thermal aging with increasing amount of acrylic-styrene emulsion. CIE $a^*$ value was higher and CIE $b^*$ value decreased with increasing amount of acrylic-styrene emulsion. These results indicate that high quality coated paper which has anti -thermal aging property can be manufactured with acrylic-styrene emulsion.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2011.04a
• /
• pp.327-338
• /
• 2011

This study was carried in order to manufacture the high quality coated paper. High quality includes not only properties of coated paper but also final print quality. In this study, new acrylic-styrene emulsion was polymerized in laboratory and compared with styrene-butadiene latex. Low-shear viscosity of coating color was decreased with increasing acrylic-emulsion dosage. WRV was increased with addition and decreased with substitution of acrylic-emulsion. Paper gloss, brightness and whiteness were increased and PPS and opacity was slightly decreased with acrylic-emulsion. Ink gloss was increased with using No. 3 acrylic-emulsion due to lower ink setting properties. However No.1, 2 emulsion shows opposite situation. Surface strength of coated paper was increased with using No. 3 acrylic-emulsion These results indicate that high quality coated paper can be manufactured with using No. 3 acrylic-emulsion.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.44 no.1
• /
• pp.37-42
• /
• 2012

This study was carried in order to manufacture the high quality coated paper. High quality includes not only physical and optical properties of coated paper but also final print quality. In this study, new acrylic-styrene emulsion was polymerized in laboratory and compared with conventional styrene-butadiene latex. Low-shear viscosity of coating color was decreased with increasing acrylic-emulsion dosage. Small amount of acrylic emulsion addition increased water retention, but further addition decreased it. Acrylic-emulsion addition improved paper gloss, brightness and whiteness, but decreased PPS and opacity slightly. Ink gloss was increased with using No. 3 acrylic-emulsion due to lower ink setting properties. However No. 1 and 2 emulsion showed the opposite result. Surface strength of coated paper was increased with using No. 3 acrylic-emulsion. These results indicate that high quality coated paper can be manufactured with using No. 3 acrylic-emulsion.