• Title/Summary/Keyword: isotropic Nd$_2$Fe$_{14}$B magnetic powders

Search Result 2, Processing Time 0.015 seconds

A Study on the Isotropic Nd$_2$Fe$_{14}$B/Epoxy Bonded Magnets with High Characteristics (고특성 등방성 Nd$_2$Fe$_{14}$B/에폭시 본드자석의 연구)

  • 조태식;정원용
    • Polymer(Korea)
    • /
    • v.26 no.1
    • /
    • pp.98-104
    • /
    • 2002
  • This study was investigated to fabricate the isotropic $Nd_2Fe_{14}B$/epoxy bonded magnets with high characteristics paroduced by compression molding. The magnetic characteristics of the bonded magnets were directly proportional to the density of the magnets and were enhanced by using raw $Nd_2Fe_{14}B$ magnetic powders, having the mean particle size of $200{\mu} m$.without additional milling process. The high characteristics of the bonded magnets were achieved at the following conditions: epoxy resin of 2.0 wt%, silane coupling agent of 0.8 wt%, curing agent of 0.7 wt% on the base of magnetic powders, and curing condition of $150^{\circ}C$/3 hrs. The bonded magnets at the optimum conditions indicated the high characteristics such as the density of 6.1 g/㎤, the remanent flux density of 7.1 kG, the maximum energy product of 9.7 MGOe, and the compressive strength of 17 kg/$mm^2$.

Magnetic Properties and Microstructure of Nanocrystalline NdFeB Magnets Fabricated by a Modified Hot Working Process

  • Kim, Hyoung-Tae;Kim, Yoon-Bae;Jeon, Woo-Yong;Kim, Hak-Shin
    • Journal of Magnetics
    • /
    • v.7 no.4
    • /
    • pp.138-142
    • /
    • 2002
  • Magnetic properties, microstructure and texture of NdFeB magnets fabricated by a modified hot working process from commercial melt-spun powders (Magnequench; MQPA, MQPB and MQPB+) have been investigated. The hot-pressed isotropic magnet made from MQPA powder, which contains higher Nd content than that of MQPB or MQPB+, shows higher coercivity. The magnet also shows homogenous and fine grains with higher coercivity for higher consolidation pressure. The hot-deformed MQPA magnet shows a strong anisotropy along the press direction with homogeneous platelet Nd$_2$Fe$_{14}$B grains of 50∼100nm in thickness and 200∼500nm in length. The hot-deformed MQPB+ magnet, however, shows low remanence and low coercivity. The microstructure of the magnet consists of two areas; undeformed Nd$_2$Fe$_{14}$B grains and well-aligned but large grains with 3∼4 $\mu$m in length. Low Nd content attributes to the formation of the two different area.