• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.622-628
• /
• 2003

The purpose of this study is to evaluate the effect of local wall thinning on the collapse of elbow subjected to internal pressure and bending moment. Thus, the nonlinear 3D finite element analyses were performed to obtained collapse moment of elbow containing various wall thinning defects under two loading; modes (closing and opening modes) and defect locations (intrados and extrados). From the results of analyses, the influence of wall thinning defect on the global moment-rotation behavior of elbow was discussed, and the dependance of collapse moment of elbow on wall thinning depth, length, and circumferential angle was investigated under different loading mode and defect location.

• Journal of the Korean Society of Safety
• /
• v.23 no.3
• /
• pp.17-24
• /
• 2008

Elbows with various shapes of local wall thinning were numerically analyzed by finite element method to get load-displacement curves and the maximum loads. Results were compared with the experimental data obtained by another study. Elastic-plastic analysis were carried out under the combined loading conditions of internal pressure and in-plane bending loads. Two types of bending loads were considered such as elbow opening mode and elbow closing mode. Also, two different wall thinning geometries were modeled. Wall thinning area located extrados or intrados of elbow inner surface was considered. Longitudinal and circumferential lengths of the thinning area and the thinned thickness were varied for analysis. The results showed that the maximum load of the wall-thinned elbow decreased with increasing of the circumferential thinning length and the thinned thickness in both of extrados and intrados thinning locations in both loading types. The maximum load obtained by the analysis were in good agreement with the experimentally measured maximum load with the same wall thinning type and dimensions. This supports accuracy of the analysis results obtained in this study.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.1
• /
• pp.8-17
• /
• 2003

Fracture behaviors of pipes with local wall thinning are very important for the integrity of nuclear Power Plant. In Pipes of energy Plants, sometimes, the local wall thinning may result from severe erosion-corrosion (E/C) damage. However, the effects of local wall thinning on strength and fracture behaviors of piping system were not well studied. In this paper, the monotonic bending tests were performed of full-scale carbon steel pipes with local wall thinning. A monotonic bending load was applied to straight pipe specimens by four-point loading at ambient temperature without internal pressure. From the tests, fracture behaviors and fracture strength of locally thinned pipe were manifested systematically. The observed failure modes were divided into four types; ovalization. crack initiation/growth after ovalization, local buckling and crack initiation/growth after local buckling. Also, the strength and the allowable limit of piping system with local wall thinning were evaluated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.11
• /
• pp.1675-1680
• /
• 2010

Flow Accelerated Corrosion (FAC) occurring during in-service conditions results in localized wall-thinning in the feeder pipes of CANDU. The wall-thinning of the feeder pipes is the main degradation mechanisms affecting the integrity of piping systems. In this paper, we assess the integrity of wall-thinned feeder pipes by limit load analysis. The limit loads for wall-thinning feeder pipes subjected to in-plane bending and internal pressure were determined on the basis of finte element limit analyses. The limit loads are determined from the results of limit analyses of elasticperfectly-plastic materials using the large geometry change. Closed-form approximations of limit load solutions for wall-thinning feeder pipes subjected to in-plane bending and pressure are proposed.

• Journal of Power System Engineering
• /
• v.18 no.5
• /
• pp.80-87
• /
• 2014

The pipelines are apt to erosion or corrosion because of the high-speed flow of water and steam with high temperatures or high pressures. This study was carried out a finite element analysis (FEA) and an experimental for the fracture behavior of T-joint pipes with local wall thinning under internal pressure. Local wall thinning was machined on the pipes in order to simulate erosion and corrosion of the metal. The configurations of the eroded area included an eroded ratio of d/t=0.80~0.963 and an eroded length of l=25 mm, 50 mm, and 102 mm. Three-dimensional elastic-plastic analyses were also carried out using FEA, which accurately simulates failure behaviors. In regards to the relationship between pressure and eroded, the criterion that indicates what can be used safely under operating pressure and design pressure were obtained from FEA. The FEA results were in relatively good agreement with that of the experiment.

• Steel and Composite Structures
• /
• v.20 no.4
• /
• pp.931-950
• /
• 2016

Ratcheting deformation of pressurized Z2CND18.12N stainless steel $90^{\circ}$ elbow pipe with local wall thinning subjected to constant internal pressure and reversed bending was studied using finite element analysis. Chen-Jiao-Kim (CJK) kinematic hardening model, which was used to simulate ratcheting behavior of pressurized $90^{\circ}$ elbow pipe with local wall thinning at extrados, flanks and intrados, was implemented into finite element software ANSYS. The local wall thinning was located at extrados, flanks and intrados of $90^{\circ}$ elbow pipe, whose geometry was rectangular cross-section. The effect of depth, axial length and circumferential angle of local wall thinning at extrados, flanks and intrados on the ratcheting behaviors of $90^{\circ}$ elbow pipe were studied in this paper. Three-dimensional elastic-plastic analysis with Chen-Jiao-Kim (CJK) kinematic hardening model was carried out to evaluate structural ratcheting behaviors. The results indicated that ratcheting strain was generated mainly along the hoop direction, while axial ratcheting strain was relatively small.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.10
• /
• pp.1227-1234
• /
• 2012

In this study, fatigue tests were carried out using real-scale pipe bend specimens with wall-thinning defects under a cyclic bending load together with a constant internal pressure of 10 MPa. The wall-thinning defect was located at the extrados and the intrados of the pipe bend specimens. A fully reversed cyclic in-plane bending displacement was applied to the specimens. For the pipe bends with wall thinning at the extrados, an axial crack occurred at the crown of the pipe bend rather than at the extrados where the defect was located. In addition, the fatigue life was longer than that of a sound pipe bend predicted from the design fatigue curve in ASME Sec.III, and it was less dependent on the axial length of the wall-thinning defect. For the pipe bends with wall thinning at the intrados, a circumferential crack occurred at the intrados. In this case, the fatigue life was much shorter than that of a sound pipe bend predicted from the design fatigue curve, and it clearly decreased with decreasing axial length of the wall-thinning defect.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.5 s.236
• /
• pp.734-742
• /
• 2005

The present study proposes the integrity evaluation model for a straight pipe with local wall thinning defect, which reflects the characteristics of training shape and loading condition in the Piping of nuclear power plant. For this purpose, a series of finite element analyses are performed under various defect geometries and loading conditions, and real pipe experiment data performed previously is employed. The model includes the effect of thinning length as well as thinning depth and width, and also it considers the combined loading effect between internal pressure and bending moment. The proposed model has been validated using the results of finite element analysis and pipe experiment data. The results indicate that the proposed model provides more reliable predictions of pipe failure than the current existing model, in terms of accuracy, consistency, and conservativeness of results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.7
• /
• pp.1014-1020
• /
• 2004

The present work complies the elastic stress concentration factor for a pipe with local wall thinning, based on detailed three-dimensional elastic FE analysis. To cover practically interesting cases, a wide range of pipe and defect geometries are considered, and both internal pressure and global bending are considered. Resulting values of stress concentration factors are tabulated for practical use, and the effect of relevant parameters such as pipe and defect geometries on stress concentration factors are discussed. The present results would provide valuable information to estimate fatigue damage of the pipe with local wall thinning under high cycle fatigue.

• Corrosion Science and Technology
• /
• v.15 no.4
• /
• pp.182-188
• /
• 2016

Significant piping wall thinning caused by Flow-Accelerated Corrosion (FAC) and Erosion-Corrosion (EC) continues to occur, even after the Mihama Power Station unit 3 secondary pipe rupture in 2004, in which workers were seriously injured or died. Nuclear power plants in many countries have experienced FAC and EC-related cases in steam cycle piping systems. Korea has also experienced piping wall thinning cases including thinning in the downstream straight pipe of a check valve in a feedwater pump line, the downstream elbow of a control valve in a feedwater flow control line, and failure of the straight pipe downstream of an orifice in an auxiliary steam return line. Cause analyses were performed by reviewing thickness data using Ultrasonic Techniques (UT) and, Scanning Electron Microscope (SEM) images for the failed pipe, and numerical simulation results for FAC and EC cases in Korea Nuclear Power Plants. It was concluded that the main cause of wall thinning for the downstream pipe of a check valve is FAC caused by water vortex flow due to the internal flow shape of a check valve, the main cause of wall thinning for the downstream elbow of a control valve is FAC caused by a thickness difference with the upstream pipe, and the main cause of wall thinning for the downstream pipe of an orifice is FAC and EC caused by liquid droplets and vortex flow. In order to investigate more cases, additional analyses were performed with the review of a lot of thickness data for inspected pipes. The results showed that pipe wall thinning was also affected by the operating condition of upstream equipment. Management of FAC and EC based on these cases will focus on the downstream piping of abnormal or unusual operated equipment.