• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.11a
• /
• pp.171-172
• /
• 2014

This is an experimental study on manufacturing of non-cement matrix. Materials like cement and blowing agent in foamed concrete is replaced by by-products from blast furnace slag and paper ash. Sample 43-PS-1 with density showed lowest. The compressive strength test result, showed a similar trend with density. And it showed that compressive strength of the 40-PS-1 was highest.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.714-719
• /
• 1998

저용융점을 가진 새로운 무기접착제인 단사정 HBO2가 알루미나 분말의 선택적 레이저 소결을 하기 위한 접착제로서 개발되었다. 12$0^{\circ}C$로 유지된 진공오븐 안에서 Boron Oxide 분말을 탄수시키면 단사정 HBO2가 만들어진다. 이것을 이용하여 만들어진 green body는 현재까지 알루미나 분말의 선택적 레이저 소결을 위하여 개발된 다른 무기 접착제들인 알루미늄(AI)과 Ammonium Phosphate(NH4H2PO4)을 이용하여 제조된 것에 비교하여 훨씬 높은 굽힘 강도를 가지고 있고 또 정밀도가 우수하였다. Green body를 열처리하여서 얻은 세라믹 시편도 똑같은 결과를 보여주었다. 이 이유는 단사정 HBO2가 낮은 점도를 보여주고 알루미나 분말에 대하여 좋은 젖음성을 가지고 있기 때문에 가능한 것으로 사료되어진다. 접착제로서 Boron Oxide의 양, 레이저 에너지밀도 등이 SLS에 의하여 제조되어진 복합재료의 굽힘강도에 미치는 영향이 조사되었다.

• Journal of Korea Foundry Society
• /
• v.43 no.5
• /
• pp.260-263
• /
• 2023

이 보고서에서는 무기 공정에서의 무기 인공 재생 모래의 특성을 중심으로 다음과 같이 정리할 수 있다. 1) ICP 발광 분광 분석을 통한 재생 모래의 Na⁺ 용출량, TP 휨강도 및 충전 밀동에는 높은 상관 관계가 확인되었다. 2) 현행 재생 방법 대비, 습식 연마 처리를 첨가함으로써 잔류 점결재가 제거되고 Na+ 용출량이 저감된 결과, 재생 모래의 TP 휨강도를 보다 개선 가능한 것이 확인되었다. 3) 재생 처리 공정 순서를 건식 연마 → 습식 연마 → 배소 처리로 함으로써, 가장 Na⁺ 용출량이 낮고, 높은 휨강도를 얻을 수 있는 것이 확인되었다. 4) 습식 연마 단계를 거치지 않고 배소 처리 온도와 처리 시간을 궁리함으로써 충분한 품질의 재생 모래를 얻을 수 있는 가능성이 시사되었다. 마지막으로, 무기 공정은 유기 공정에 비해 압도적으로 냄새가 적고 생산성이 높으며 인공 모래와의 병용을 통한 재생 처리시의 폐기물량 저감, 주조품의 고품질화 등 이점이 기대되는 공정이다.

• Journal of the Korea Concrete Institute
• /
• v.20 no.5
• /
• pp.653-660
• /
• 2008

The purpose of this study is to analyze the optimal mix design of the sound absorption material that is made from perlite and various binder systems for noise barrier wall. The polymer cement slurry which is made from two types of polymer dispersions, and silicone type inorganic material are used as binder. The test specimens are prepared with various polymer cement ratios, binder ratios, and tested for strengths, freezing and thawing and sound absorption performance by the tube and the reverberation room methods. From the test results, the difference of sound absorption coefficient by the tube method is a little recognized, however, noise reduction coefficient (NRC) of test specimens bound by the polymer cement slurry is in the ranges of 0.48 to 0.51. They are a little higher than those bound by cement only, and are lower values than recommended value of 0.7 by the Ministry of Environment. However, the sound absorption coefficient of test specimens at low frequency range of 250 to 500 Hz by reverberation room method shows very high values as 0.84 to 1.00, and 0.57 to 0.77 at the high frequency. The test specimens with polymer cement slurry binder have a good balance between performance and cost, and have proper properties in strengths, freezing and thawing resistance as sound absorption material for noise barrier wall. It is apparent that the good sound absorption material can be produced according to the optimum mix design that is recommended from this study.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.6
• /
• pp.489-495
• /
• 2020

Whereas the control of the hydration heat in mass concrete has been important as the concrete structures enlarge, many conventional strategies show some limitations in their effectiveness and practicality. Therefore, In this study, as a solution of controling the heat of hydration of mass concrete, a method to reduce the heat of hydration by controlling the hardening of cement was examined. The reduction of the hydration heat by the developed Phosphate Inorganic Salt was basically verified in the insulated boxes filled with binder paste or concrete mixture. That is, the effects of the Phosphate Inorganic Salt on the hydration heat, flow or slump, and compressive strength were analyzed in binary and ternary blended cement which is generally used for low heat. As a result, the internal maximum temperature rise induced by the hydration heat was decreased by 9.5~10.6% and 10.1~11.7% for binder paste and concrete mixed with the Phosphate Inorganic Salt, respectively. Besides, the delay of the time corresponding to the peak temperature was apparently observed, which is beneficial to the emission of the internal hydration heat in real structures. The Phosphate Inorganic Salt that was developed and verified by a series of the aforementioned experiments showed better performance than the existing ones in terms of the control of the hydration heat and other performance. It can be used for the purpose of hydration heat of mass concrete in the future.

• Analytical Science and Technology
• /
• v.26 no.4
• /
• pp.245-255
• /
• 2013

Identification of paint on victim's clothing and a vehicle are valuable for forensic examination when investigating hit-and-run accidents. Automotive paints on clothes are used to prove a victim caused by traffic accident and to identify a suspected vehicle. The comparison of transferred paints between victim's vehicle and suspected vehicle can be an important evidence in reconstructing the accident situation and in discovering the truth. The paints such as white, yellow, red, blue, or black are hard to examine particle shape under a stereomicroscope because of it is not included aluminum, pearl, and mica flakes in the pigments. The aim of this study under forensic aspect is to compare pigment among basecoat layers of solid paints by identifying inorganic elemental compositions and binder resins of pigments using by micro-FT-IR and micro-XRF spectrometer. The pigment samples were analyzed by using two methods of FT-IR: Reflectance and ATR method. Two methods of FT-IR were useful in discriminating binder resins of pigments by comparing characteristic peaks and patterns of spectra. Also, XRF spectrometer could identify the elemental compositions in inorganic pigments of trace paints which are difficult to compare the identification by FT-IR.

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1085-1092
• /
• 2001

The high efficient AC powder EL devices classified by low cost and low power consumption type fabricated using screen printing method with film thickness and organic binder. Brightness and current density were measured at frequency range of 400Hz∼1kHz and voltage range of 50∼300V$\_$rms/ to estimate optoelectrical properties of AC powder EL devices, respectively. Frequency generator was used as system producing frequency and voltage of a sine wave. Also brightness and current density were measured by luminometer and multimeter. In the case of low cost type AC powder EL device, brightness and current density were about 43 cd/m$^2$and 20$\mu$A/cm$^2$when the thickness of phosphor and dielectric layer was 45∼50$\mu$m under no addition of plasticizer respectively. In the case of low power consumption type AC powder EL device, brightness and current density were about 74 cd/m$^2$and 30∼40$\mu$A/cm$^2$when the thickness of phosphor and dielectric layer was 45∼50$\mu$m and 15∼20$\mu$m under addition of 15wt% plasticizer respectively. Also, AC powder EL device fabricated in this study showed absolutely excellent characteristics as the lifetime was longer than products of other company.

• Journal of the Korean Electrochemical Society
• /
• v.25 no.1
• /
• pp.42-49
• /
• 2022

In this study, the surface protection film based on organic-inorganic composite is manufactured for suppressing lithium dendrite growth, and the film is applied on the surface of Li metal negative electrode for lithium metal batteries (LMBs). The film is consist of the polyvinylidene fluoride (PVDF) polymeric binder which has good mechanical strength and high electrochemical stability, and carbon black (Super-P) which has outstanding electrical conductivity as the inorganic compound. First, in order to confirm the suppression of the internal short circuit by the lithium dendrite, the time required for the short circuit is measured while a constant current is continuously applied. As a result, the internal short circuit is delayed in proportion to the carbon black content of the film, and it is significantly delayed than bare Li metal electrode which does not use protection film. The cycle performance of the thick protection film (8 ㎛), is worse than that of the thin film (4 ㎛). However, as the carbon black content of the film increased, the cycle performance is improved. Thus, the surface protection film based on carbon black/PVDF composite can delay the internal short circuit, and has low overvoltage during the cycle. However, more stable cycle performance needs to be built through further improvements.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.37-44
• /
• 2017

Red mud is an inorganic by-product produced from the mineral processing of alumina from Bauxite ores. The development of alkali-activated slag-red mud cement can be a representative study aimed at recycling the strong alkali of the red mud as a construction material. This study is to investigate the optimum water content, compressive strength, water absorption and efflorescence of alkali-activated slag-red mud soil pavement according to binder type. The results showed that the optimum water content, moisture absorption coefficient and efflorescence area of alkali-activated slag-red mud soil pavement increased but the compressive strength of that decreased as the redmud content increased.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.5
• /
• pp.1354-1358
• /
• 2008

Environmental-friendly nontocxic flame retardant paint which can overcomes the restriction of harmful materials for human body and environments such as Pb, Hg, Cd, $C^{+6}$, PBB/PBDE by EU and domestic Ministry of Environment was developed. Developed paint is the water-soluble organic inorganic hybrid material that VOC(volatility organic compound) discharge is low, and that human riskiness and environmental pollution is minimized not using the kinds of halogen materials. $Mg(OH)_2$, $Sb_{2}O_{3}$, and Zinc borate were used as flame retardant materials, 2% Micell and water were used as binder and solvent, respectively. Results showed the optimum activity was obtained when the ratio of those frame retardant agents($Mg(OH)_2$, $Sb_{2}O_{3}$, Zinc borate made by 1: 2: 2), binder(2% Micell) and water was 1: 0.5: 0.5.