• Corrosion Science and Technology
• /
• 제5권2호
• /
• pp.69-76
• /
• 2006

Premature cracking of the epoxy coatings applied on ship's ballast tanks(BT) can lead to damage of ship's hulls. To avoid this, it's important to have clear understanding of the underlying mechanism and primary factors of the coating crack. In this study, the efforts were made to clarify the integrated effects of main factors, i.e., initial coating shrinkage, thermally induced strain, steel-structural strain and the intrinsic coating flexibility at the initial and after aging, to the early cracking phenomena of epoxy coating in the ship's ballast tank. The coating crack is caused by combination of thermal stress, structural stress, and internal stresses which is closely related to chemical structures of the coatings. On the other hand, thermal stresses and dimensional stabilities would rarely play a major role in coating crack for ballast tank coatings with rather large flexibility. Crack resistance of the coatings at early stages can be estimated roughly by measuring internal stress, FT-IR and $T_g$ value of the coatings. A new screening test method was also proposed in this study, which can be possibly related to the long-term resistance of epoxy-based paints to cracking.

• 한국작물학회지
• /
• 제34권1호
• /
• pp.14-22
• /
• 1989

벼 잎집무늬마름병에 대하여 저항성반응이 다른 품종을 시험하여 병균접종구, 자연구 및 약제방제구를 두어 병 발생에 의한 수량감소률의 품종간 차이를 2년간에 걸쳐 조사한 결과를 요약하면 다음과 같다. 1. 시험한 품종 중에서 가야벼는 병균접종구나 자연구에서의 발병정도가 가장 낮았으며 태백벼, 관악벼 및 Labelle은 균발생이 심하였고, 약제방제구에서는 병이 거의 발생하지 않았다. 2. 중반저항성품종인 가야벼는 2년간에 걸쳐 병균접종구 및 자연구에서의 수량감소률이 0.3∼5％로 공시품종 중에서 가장 낮았으며 이병성품종인 태백벼는 6.8∼25.8％로 가장 높았고 관아벼와 Labelle도 각각 10％내외의 수량감소률을 보였다. 3. 시험품종의 저항성정도에 관계없이 동일한 품종내에서 잎집무늬마름병의 병반이 지엽까지 진전된 분얼경에서는 등숙비육과 정조천립중이 감소하여 건전경에 비하여 이삭무게가 25％이상 감소하였다. 4. 잎집무늬마름병에 대하여 상위엽으로의 병반진전이 더디게 되었기 때문에 수량감소율이 낮았다.

• 소성∙가공
• /
• 제8권1호
• /
• pp.101-107
• /
• 1999

The upset forging stage is the initial work in the forging process. It is used to remove the segregation and cavities of the ingot. Specially in handling large sized ingot, an improper upset forging can cause serious surface tearing. However, there is no detail reference for stable upset forging work. To resolve this difficulty, we studied several factors such as upset forging time, temperature varation of ingot, damage, load and stain rate etc., by using the rigid-plastic finite element approach available in the DEFORM code. Numerical simulation results indicated that: the load value of upset forging works shows severe decreasing trend at a certain point, same as strain rate. Also defects were found to be concentrated around the upper and lower portions of the ingot. With these results, we can estimate a guideline for stable upset forging work.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 2001년도 ICCAS
• /
• pp.175.2-175
• /
• 2001

The strip profile and shape control is one of the most important technologies in Hot Rolling Mill System. Because the unbalance of strip´s shape and wave appearance between stands has a bad effect on Hot Rolling Mill System by making the inferior thickness, strip´s damage and so forth in factories. Many competition Plate Mill introduced shape control system, for example, pair cross-mill, work roll bender, which includes shape measuring instruments and shape control mathematical models. Shape meter, which is equipped for flatness, only does feedback control at the top of coil. And, for crown, we depend on initial setup value and there is no feedback control. Therefore we predict the shape of strip using rolling pressure, bender force and tension of inter-stand in ...

• 한국레이저가공학회지
• /
• 제17권1호
• /
• pp.13-16
• /
• 2014

Indium Tin Oxide (ITO) has been used widely for transparent conducting thin films. In this work, the feasibility of a laser sintering process to fabricate ITO thin films on flexible substrates is examined. Nanoparticles of ~10 nm were spin coated on a Si wafer and then sintered by a KrF excimer laser. The sintered structure was characterized by scanning electron microscopy. Polycrystalline structures were fabricated by the process without thermally damaging the substrate. The electrical resistivity of the film was reduced to ~ 1/1000 of the initial value. This work demonstrates that nanosecond laser sintering of ITO particles can be a useful tool to fabricate ITO films on various flexible substrates.

• 한국정밀공학회지
• /
• 제13권11호
• /
• pp.25-31
• /
• 1996

In this paper, three different types of commercial tools -P20, NC123K and ceramic- have been used to cut austempered ductile iron(ADI). In the austempered condition the materials are hard, strong and difficult to machine. Thus, we selected a optimum tool material among three different types of used tools in machining of austempered ductile iron. It was used acoustic emission (AE) to know cutting characteristic for selected tool and investigate characteristic of AE signal according to cutting condition and relationship between AE signal and flank wear land of the ceramic tool. The obtained results are as follows ; (1) The ceramic tool among three different types of tools is the best in machining austempered ductile iron. (2) In case of ceramic tool, the amplitude level of AE signal(AErms) is mainly affected by cutting condition and it is proportional to cutting speed. (3)There have been the relationship of direct proportion between the amplitude level of AE signal and flank wear land of the tool. (4) It was observed that the value of AErms was only affected by cutting speed. Therefore it is possible to in-process detec- tion of ceraic tool's wear in case the initial value of AErms at each cutting speed decided.

• Tribology and Lubricants
• /
• 제38권5호
• /
• pp.222-226
• /
• 2022

Between diaphragms made of stainless steel (SUS), which is the main component of a hydrogen gas compressor, micro-slip occurs owing to repeated bending, resulting in scratches on the surface. The surface scratch of the compressor part is a problem with airtightness, which reduces the efficiency of the compressor; in severe cases, damage is a possibility. In this study, the changes in friction and wear characteristics due to the surface polishing of SUS and carbon-based solid lubricant films (graphene and CNT) were analyzed. Bare SUS, polished SUS, graphene film, and CNT film specimens were prepared. The surface roughness of the SUS was significantly reduced by surface polishing but increased by carbon-based solid lubricating films. In contrast, the friction coefficient maintained a similar value after surface polishing but was significantly reduced by the carbon-based solid lubricant films. In particular, the graphene film exhibited the lowest initial friction coefficient, while the CNT film exhibited the lowest overall average friction coefficient. Regarding the wear rate, polished SUS exhibited the lowest value, but the surface condition of the wear track showed that the carbon-based solid lubricating films were relatively less damaged. Although the wear rate measured was largely attributed to the solid lubricating film peeling off, the SUS surface under the film was considered protected.

• 한국재난정보학회 논문집
• /
• 제17권2호
• /
• pp.245-253
• /
• 2021

연구목적: 본 연구는 화재발생 건축물 정보, 신고자 취득 정보 등 초기 정보를 활용하여 화재현장의 위험도를 예측하여, 재난 발생 초기에 효과적인 소방자원 동원 및 적절한 대응을 위한 피해최소화 전략 수립을 지원하는 위험도 예측 모델을 개발하고자 한다. 연구방법: 화재 통계 데이터 상에서 화재의 피해규모와 관련된 변수 규명을 위해 머신러닝 알고리즘을 이용한 변수간 상관성 분석을 실시하여 예측 가능성을 검토하고, 데이터 표준화 및 이산화 등의 전처리를 통해 학습 데이터 셋을 구축하였다. 이를 활용하여 예측 정확도가 높은 것으로 평가 받고 있는 복수의 머신러닝 알고리즘을 테스트하여 가장 정확도가 높은 알고리즘을 적용한 위험도 예측 모델을 개발하였다. 연구결과: 머신러닝 알고리즘 성능 테스트 결과 랜덤포레스트 알고리즘의 정확도가 가장 높게 나왔으며, 위험도 등급에 대해서는 중간치에 대한 정확성이 상대적으로 높은 것으로 확인되었다. 결론: 화재 통계 상 피해규모 데이터의 편향성에 의해 예측모델 정확도가 제한적으로 나타났으며, 예측 모델 성능 개선을 위해 데이터 정합성 및 결손치 보완 등을 통한 데이터 정제가 필요하다.

• 멤브레인
• /
• 제27권3호
• /
• pp.248-254
• /
• 2017

내염소성 원생동물인 크립토스포리디움, 지아디아 등 병원성 미생물의 제거에 대한 신뢰성을 확보하기 위해 정수처리 공정에서 막여과 시스템이 각광받고 있으며, 이러한 신뢰성을 보증하기 위해 막 완결성에 대한 연구가 중요시되고 있다. 막 완결성 시험은 크게 직접법과 간접법으로 분류되는데, 직접법 중 압력기반의 시험은 버블포인트 이론을 근간으로 병원성 미생물의 최소 크기인 $3{\mu}m$ 크기 이상을 감지할 수 있는 감도로 USEPA Guidance Manual에서 제시하고 있다. 간접법은 온라인 상태에서 연속적인 운전이 가능하다는 점에서 널리 사용되지만, 직접법에 비해 현저히 낮은 막 손상 감지 감도를 가지고 있으며, 손상 부위를 특정 지을 수 없는 한계가 있기에 이러한 감지 감도를 개선해야 할 필요가 있다. 따라서 본 연구에서는 압력 손실 시험에 의한 막 완결성 시험을 통해 막 파단 형태별, 파단 개수, 초기설정압력값에 따른 압력손실률과 LRVDIT 신뢰성 범위를 상호 비교함으로써 막 손상에 따른 감도의 결과를 정량화하여 UCL 기준을 나타내어 비교 평가하였다.

• 한국전자통신학회논문지
• /
• 제11권4호
• /
• pp.395-402
• /
• 2016

DC ${\mu}$-Grid 기반의 충/방전 시스템에서 배터리의 동작 변환 시, 망 전압의 fluctuation이 발생하게 되며, 과다한 fluctuation은 충/방전 시스템의 손상 및 고장을 일으킬 수 있다. 따라서 본 논문에서는 DC ${\mu}$-Grid 기반의 충/방전 시스템에서 fluctuation 완화용 커패시터의 적용 및 설계 포인트에 대하여 연구하였다. 컴퓨터 시뮬레이션 결과, 3개의 충전 배터리 set와 5개의 방전 배터리 set의 조건으로 운영되는 DC ${\mu}$-Grid 기반 충/방전 시스템에서 600V/35mF의 초기 값을 갖는 fluctuation 완화용 커패시터를 적용하였을 때 충/방전에 의한 fluctuation을 약 66.3% 감소시킬 수 있었으며, 추가적으로 초기 망 전압 안정화 시 발생하는 fluctuation 또한 약 73% 감소시킬 수 있었다.