• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.256-261
• /
• 2009

Hydrophilic and transparent $TiO_2$ thin film was fabricated by sol-gel method and the properties of contact angle, surface morphology, and transmittance were measured. In addition, surfactant Tween 80 was used for increasing the hydrophilic property of thin film. When the contents of Tween 80 in $TiO_2$ solution was 0, 10, 30, 50wt%, the contact angles of $TiO_2$ thin film were $41.4^{\circ}$, $18.2^{\circ}$, $16.0^{\circ}$, $13.2^{\circ}$, respectively. Fabricated $TiO_2$ thin film showed the photocatalytic property that decomposed methylene blue and decreased the absorbance of solution after UV irradiation. $TiO_2$ thin films fabricated with the solution of 30 wt% Tween 80 were deposited on glass (bare), antimony tin oxide (ATO), fluorine tin oxide (FTO), indium tin oxide (ITO) coated glass substrates, and the contact angle and transmittance of thin film was measured. The contact angles of thin films deposited on four substrates were $16.2\sim27.1^{\circ}$ and was decreased to the range of $13.2\sim17.6^{\circ}$ after UV irradiation, Especially, the thin films coated on ATO and FTO glass substrate showed high transmittance of 74.6% in visible range, respectively, and low transmittance of 54.2% and 40.4% in infrared range, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.187-187
• /
• 2015

The past thirty years have seen increasingly rapid advances in the field of Indium Tin Oxide (ITO) transparent thin film.[1] However, a major problem with this ITO thin film application is high cost compared with other transparent thin film materials.[2] So far, in order to overcome this disadvantage, we show a transparent ITO/Ag/i-ZnO multilayer thin film electrode can be the solution. In comparison with using amount of ITO as a transparent conducting material, intrinsic-Zinc-Oxide (i-ZnO) based on ITO/Ag/i-ZnO multilayer thin film showed cost-effective and it has not only highly transparent but also conductive properties. The aim of this research has therefore been to try and establish how ITO/Ag/i-ZnO multilayer thin film would be more effective than ITO thin film. Herein, we report ITO/Ag/i-ZnO multilayer thin film properties by using optical spectroscopic method and measuring sheet resistance. At a certain total thickness of thin film, sheet resistance of ITO/Ag/i-ZnO multilayer was drastically decreased than ITO layer approximately $40{\Omega}/{\square}$ at same visible light transmittance.(minimal point $5.2{\Omega}/{\square}$). Tendency, which shows lowly sheet resistive in a certain transmittance, has been observed, hence, it should be suitable for transparent electrode device.

• Journal of Korean Ophthalmic Optics Society
• /
• v.7 no.2
• /
• pp.155-161
• /
• 2002

We studied the formation of nickel nano thin film that have various electrochromic properties. Nickel thin film having various thickness will apply photoelectronic devices, specially, electrochromic devices. These devices will apply lens, battery, glass and solar cell that have light, thin, simple and small that applied nanotechnology and quantum dot. Nickel thin film was coated by electrochemical method on ITO electrode. We studied the thin film properties by Cyclic voltammetry, Chronoamperometry. Impedance. X-ray diffraction analysis and Atomic force microscopy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.11a
• /
• pp.302-305
• /
• 1995

ITO(indium tin oxide) that is both conductive in electricity and transparent to the visible ray is called transparent conducting thin film. Nowaday, according to the development of flat panel display such as LCD(Liquid Crystal display, EL(electolumine- scence display), PDP(plasma display panel), ECD(electrocromic display), the higher quality in the low temperature process has been asked to reduce the production cost and to have a good uniformity on a large substrate. In this study, we prepared indium tin oxide(ITO) by a cylindrical DC magnetron sputtering with Indium-tin (9:1) alloy target instead of indium-tin oxide target. To reduce the defact in ITO, the effect on ITO by varing the magnetic field intensity and the applied voltage ares studied. the resistivity of the film deposited in oxygen partial pressure of 5% and substrate temperature of 140$^{\circ}C$. is 1.6${\times}$10$\^$-1/$\Omega$$.$cm with 85% optical transmission in viaible ray.

• Journal of Ocean Engineering and Technology
• /
• v.21 no.1 s.74
• /
• pp.59-63
• /
• 2007

The thin film of indium tin oxide (ITO) was prepared using the inclination opposite target type DC magnetron sputtering equipment onto the glass substrate at room temperature, using oxidized ITO with In2O3 and SnO2in a weight ratio of 9:1. The elastic modulus and hardness of the ITO thin films, prepared at different deposition conditions, were determined through anano-indentation experiment. The work pressure was varied from $2.6{\times}10-1\;to\;8.3{\times}10-1Pa$. The results show that the variation of work pressure during film deposition could vary significantly, according to the elastic modulus and hardness of the ITO thin films. It also can be seen that a minimum value exists in the film resistivity for the ITO thin films, prepared according to the variation of work pressure. However, the ITO film produced at room temperature had a microstructure in which a X ray diffraction peak is not clear, regardless of the work pressure.

• Journal of the Korean Applied Science and Technology
• /
• v.34 no.4
• /
• pp.705-716
• /
• 2017

In this study, Indium-Titanium hydroxide particle with 0.5, 1.0, 1.5 wt% of $TiO_2$ were synthesized by sol process and adding the base, ITiO(Indium Titanium Oxide) particles were obtained by gelling at $200^{\circ}C$ and $500^{\circ}C$. The ITiO particle's size with gel process at $200^{\circ}C$ was smaller than ITiO particle's size with gel process $500^{\circ}C$. The ITiO particle with gel process at $200^{\circ}C$ was used to fabricate dense ITiO target. ITiO targets with 0.5, 1.0, 1.5 wt% of $TiO_2$ were fabricated and used to obtain ITiO thin films onto glass by sputtering. Among those sputtered ITiOs' thin films, ITiO thin film with 0.4 % of $O_2$ and 0.5 wt% of $TiO_2$ showed the lowest specific resistance, highest charge mobility and lowest carrier concentration. It was found the light transmittance of the ITiO film were increased highly compared to light transmittance of ITO (Indium Tin Oxide) thin film over Infrared wavelength ranges.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.208-208
• /
• 2010

Indium zinc tin oxide (IZTO) thin films were studied as a possible alternative to indium tin oxide (ITO) films for providing low-cost transparent conducting oxide (TCO) for thin film photovoltaic devices. IZTO films were deposited onto glass substrates at room temperature. A dc/rf magnetron co-sputtering system equipped with a ceramic target of the same composition was used to deposit TCO films. Earlier studies showed that the resistivity value of $In_{0.6}Zn_{0.2}Sn_{0.2}O_{1.5}$ (IZTO20) films could be lowered to approximately $6{\times}10^{-4}ohm{\cdot}cm$ without sacrificing optical transparency and still maintaining amorphous structure through the optimization of process variables. The growth rate was kept at about 8 nm/min while the oxygen-to-argon pressure ratio varied from 0% to 7.5%. As-deposited films were always amorphous and showed strong oxygen pressure dependence of electrical resistivity and electron concentration values. Influence of forming gas anneal (FGA) at medium temperatures was also studied and proven effective in improving electrical properties. In this study, the chemical composition of the targets and the films varied around the $In_{0.6}Zn_{0.2}Sn_{0.2}O_{1.5}$ (IZTO20). It was the main objective of this paper to investigate how off-stoichiometry affected TCO characteristics including electrical resistivity and optical transmission. In addition to the composition effect, we have also studied how film properties changed with processing variables. IZTO thin films have shown their potential as a possible alternative to ITO thin films, in such way that they could be adopted in some applications where currently ITO and IZO thin films are being used. Our experimental results are compared to those obtained for commercial ITO thin films from solar cell application view point.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.14 no.4
• /
• pp.935-938
• /
• 2010

Indium-tin-oxide (ITO) films show a low electrical resistance and high transmittance in the visible range of an optical spectrum. The transparent electrodes have to get resistivity and sheet resistance less than $1{\times}10^{-3}{\Omega}/cm$ and $10^3{\Omega}/sq$ respectively and transmittance over 80% at wavelength of 380nm~780nm. This study establishes DC magnetron sputtering process condition on ITO thin film by measuring electrical and optical properties of the thin film. As results, we obtained $300\;{\mu}{\Omega}cm$ resistivity of ITO films with good transmittance (above 90 %) under 90:10 wt% composition rate of $In_2O_3:SnO_2$. Also, we understood that the ITO thin film by DC magnetron sputtering depends on the deposition condition, especially substrate temperature, and the composition rate of $In_2O_3:SnO_2$ that is one of the most critical parameters was successfully optimized for high qualified transparent electrodes.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.170-170
• /
• 2010

Thin-film transistors (TFT) have become the key components of electronic and optoelectronic devices. Most conventional thin-film field-effect transistors in display applications use an amorphous or polycrystal Si:H layer as the channel. This silicon layers are opaque in the visible range and severely restrict the amount of light detected by the observer due to its bandgap energy smaller than the visible light. Therefore, Si:H TFT devices reduce the efficiency of light transmittance and brightness. One method to increase the efficiency is to use the transparent oxides for the channel, electrode, and gate insulator. The development of transparent oxides for the components of thin-film field-effect transistors and the room-temperature fabrication with low voltage operations of the devices can offer the flexibility in designing the devices and contribute to the progress of next generation display technologies based on transparent displays and flexible displays. In this thesis, I report on the dc performance of transparent thin-film transistors using amorphous indium tin zinc oxides for an active layer. $SiO_2$ was employed as the gate dielectric oxide. The amorphous indium tin zinc oxides were deposited by RF magnetron sputtering. The carrier concentration of amorphous indium tin zinc oxides was controlled by oxygen pressure in the sputtering ambient. Devices are realized that display a threshold voltage of 4.17V and an on/off ration of ${\sim}10^9$ operated as an n-type enhancement mode with saturation mobility with $15.8\;cm^2/Vs$. In conclusion, the fabrication and characterization of thin-film transistors using amorphous indium tin zinc oxides for an active layer were reported. The devices were fabricated at room temperature by RF magnetron sputtering. The operation of the devices was an n-type enhancement mode with good saturation characteristics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.439-440
• /
• 2008

Indium Zinc Tin Oxide (IZTO) thin films for transparent thin film transistor (TTFT) were deposited on glass substrate at room temperature by facing targets sputtering (FTS). The FTS system was designed to array two targets facing each other and forms the high- density plasma between. Two different kinds of targets were installed on FTS system. One is ITO ($In_2O_3$ 90wt.%, $SnO_2$ 10wt.%), the other is IZO($In_2O_3$ 90wt%, ZnO 10wt%). The conductive and optical properties of IZTO thin film is determined depending on variation of DC power and working pressure. Therefore, IZTO thin films were prepared with different DC power and working pressure. As-deposited IZTO thin films were investigated by a UV/VIS spectrometer, an X-ray diffractometer (XRD), a scanning electron microscopy (SEM), a Hall Effect measurement system. As a result, all IZTO thin films deposited on glass substrate showed over 80% of transmittance in visible range (400~800 nm) at $O_2$ gas flow rate. We could obtain IZTO thin films with the lowest resistivity $5.67\times10^{-4}$ [$\Omega{\cdot}cm$] at $O_2$ gas flow rate 0.4 [sccm).