• Korean Journal of Materials Research
• /
• v.23 no.2
• /
• pp.128-134
• /
• 2013

A study on the corrosion behavior of Inconel alloys and Incoloy 800H in molten salt of LiCl-$Li_2O$ was investigated at $650^{\circ}C$ for 24-312 hours in an oxidation atmosphere. The order of the corrosion rate was Inconel 600 < Inconel 601 < Incoloy 800H < Inconel 690. Inconel 600 showed the best performance suggesting that the content of Fe, Cr and Ni are the important factor for corrosion resistance in hot molten salt oxidation conditions. The corrosion products of Inconel 600 and Inconel 601 were $Cr_2O_3$ and $NiFe_2O_4$, In case of Inconel 690, a single layer of $Cr_2O_3$ was formed in the early stage of corrosion and an outer layer of $NiFe_2O_4$ and inner layer of $Cr_2O_3$ were formed with an increase of corrosion time. In the case of Incoloy 800H, $Cr_2O_3$ and $FeCr_2O_4$ were observed. Most of the outer scale of the alloys was observed to be spalled from the results of the SEM analysis and the unspalled scale which adhered to the substrate was composed of three layers. The outer layer, the middle one, and the inner one were Fe, Cr, and Ni-rich, respectively. Inconel 600 showed localized corrosion behavior and Inconel 601, 690 and Incoloy 800H showed uniform corrosion behavior. Ni improves the corrosion resistance and too much Cr and/or Fe content deteriorates the corrosion resistance.

• Nuclear Engineering and Technology
• /
• v.55 no.1
• /
• pp.71-79
• /
• 2023

Air ingress incidents are major safety accidents in very-high-temperature reactors (VHTRs). Air containing a high volume fraction of oxygen may cause severe oxidation of core components at the VHTR, especially for the significantly thin alloy tube wall in the intermediate heat exchanger (IHE). The research objects of this study are Inconel 617 and Incoloy 800H, two candidate alloys for IHE in VHTR. The air ingress accident scenario is simulated with high-temperature air flow at 950 ℃. A continuous oxide scale was formed on the surfaces of both the alloys after the experiment. Because the oxide scale of Inconel 617 has a loose structure, whereas that of Incoloy 800H is denser, Inconel 617 exhibited significantly more severe internal oxidation than Incoloy 800H. Further, Inconel 617 showed a significant decrease in ultimate tensile strength and plasticity after aging for 200 h, whereas Incoloy 800H maintained its tensile properties satisfactorily. Through control experiment under vacuum, we preliminarily concluded that serious internal oxidation is the primary reason for the decline in the tensile properties of Inconel 617.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.51-51
• /
• 2003

• Korean Journal of Materials Research
• /
• v.10 no.7
• /
• pp.471-477
• /
• 2000

Corrosion behavior of Fe-Ni-Cr alloy in molten salts of LiCl and LiCl-$Li_2O was investigated in the tempera-ture range of $650~850^{\circ}C$. In the molten salt of LiCl, and internal oxidation of Fe occurred in the KSA(Kaeri Superalloy)-1 alloy without containing Cr, while a dense protective oxide scale of $LiCrO_2$ was formed in the KSA-4, Incoloy 800H and KSA-5 alloys. In the mixed molten salt of LiCl-$Li_2O$, internal oxidation of Fe and Cr took place in the KSA-1 and KSA-4 alloys, respectively. Non-protective porous oxide scales consisting of $LiCrO_2$ and Ni were formed in the Incoloy 800H and KSA-5. The corrosion rate of the alloys increased with the increase in Cr content and the corrosion rate followed the parabolic law for the alloy containing Cr content less than 8%, and the linear law for the alloy containing Cr content more than 8%. Such a corrosion behavior of the alloy in the mixed molten salt of LiCl-$Li_2O$ was interpreted in terms of the basic fluxing mechanism of protective oxide scale of $Cr_2O_3$.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.985-991
• /
• 1999

Corrosion behaviors of Incoloy 800H, KSA(Kaeri Superalloy)-6, Inconel 600 and Hastelloy C-276 in molten salts were investigated in the temperature range of 650 ~ $850^{\circ}C$. Due to $\textrm{Li}_{2}\textrm{O}$-induced basic fluxing mechanism, the corrosion rates of the alloys in mixed molten salt of LiC1-$\textrm{Li}_{2}\textrm{O}$ were significantly higher than those in molten salt of LiCl. In the mixed molten salt, Fe-base alloys showed higher corrosion resistance than the Ni-base alloys. and Hastelloy C-276 with high Mo and W contents exhibited the highest corrosion rate among the examined alloys. The single layer of $\textrm{LiCrO}_{2}$ was formed in molten salt of LiCl and two phase structure of a scale consisted of oxides and Ni was formed in the mixed molten salt.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.12
• /
• pp.1421-1426
• /
• 2014

To improve the inherent safety of the sodium-cooled fast reactor (SFR), the supercritical $CO_2$ ($S-CO_2$) Brayton cycle is being considered as an alternative power conversion system to steam the Rankine cycle. In the $S-CO_2$ system, a PCHE (printed circuit heat exchanger) is being considered. In this type of heat exchangers, diffusion bonding is used for joining the thin plates. In this study, the diffusion bonding characteristics of various austenitic alloys were evaluated. The tensile properties were measured at temperatures starting from the room temperature up to $650^{\circ}C$. For the 316H and 347H types of stainless steel, the tensile ductility was well maintained up to $550^{\circ}C$. However, the Incoloy 800HT showed lower strength and ductility at all temperatures. The microstructure near the bond line was examined to understand the reason for the loss of ductility at high temperatures.