• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.05a
• /
• pp.20-23
• /
• 2001

Hypereutectic Al-25Si alloy, which is expected to be applied to the cylinder-liner-part of the engine-block of an automobile due to its excellent wear resistance, low density and low thermal expansion coefficient, has been fabricated through a spray forming process. The obtained microstructure of the hypereutectic Al-25Si alloy appeared to consist of Al matrix and equiaxed Si particles of average diameter of 5-7 mm. To characterize the deformation behavior of this alloy, a series of load relaxation and compression tests have been conducted at temperatures ranging from RT to $500^{\circ}C$. The strain rate sensitivity parameter (m) of this alloy has been found to be very low (0.1) below $400^{\circ}C$ and reached maximum value of about 0.2 at $500^{\circ}C$. During the deformation above $300^{\circ}C$ in compression, strain softening has been observed. The diagram of extrusion pressure vs. ram-speed has been constructed. The extrusion has been successfully conducted at the temperatures of $300^{\circ}C$ and above with the ratio of area reduction of 28 and 40 in this study.

• Journal of Korea Foundry Society
• /
• v.26 no.3
• /
• pp.123-128
• /
• 2006

Mechanical and thermal properties of spray-cast hypereutectic Al-20wt.%Si-xwt.%Fe alloys (x=0, 1, 3, 5) were investigated. After the spray-casting, hot extrusion was performed at $400^{\circ}C$. Intermetallic compound (${\beta}-Al_5FeSi$) and primary Si are observed in the spray-cast aluminum alloys. The size of primary Si and intermetallic compound of the spray-aluminum alloys became finer and more uniformly distributed than that of the permanent mold cast ones. Ultimate tensile strength of the spray-cast aluminum alloys increased by increasing Fe contents, but that of the permanent mold cast aluminum alloys decreased by increasing Fe contents possibly due to increased amount of coarse intermatallic compound. The coefficient of thermal expansion (CTEs) of the aluminum alloys became lower with finer primary Si and intermetallic compound, and this is attributed to the increased amount of interfacial area between the aluminum matrix and the phases of finer Si and intermetallic compound.

• Journal of Korea Foundry Society
• /
• v.15 no.5
• /
• pp.483-493
• /
• 1995

The microstructural changes during semi-solid state processing of hypereutectic Al-Si alloy has been investigated in the present study. Stirring of semi-solid slurry results in the morphological changes of the primary Si particles, i.e. from angular rod shape to near-spherical shape. Besides the spherodization of primary Si particles, the average particle size increases, especially, at much higher rate in the final stage than that in the early stage of stirring. Various microstructure characterization techniques, such as anisotropic etching, SEM imaging and ECP analysis, reveal that the spherodization of primary Si particles occurs by the combinations of the mechanisms of coalescence, fracture, and wear of the individual particles. Isothermal shearing of hypereutectic Al-Si at $580^{\circ}C$ shows that spherical ${\alpha}-Al$ particles are formed by the dissociation of Al-Si eutectic structure at the early stage of isothermal shearing. The spherical ${\alpha}-Al$ particles gradually grow by the mechanisms of Ostwald ripening and coalescence of the particles.

• Journal of Welding and Joining
• /
• v.29 no.2
• /
• pp.88-93
• /
• 2011

This study produced hypereutectic Al-Si clad layer on 1050 Al alloy by a novel laser cladding method. Pure Si powder was mixed with organic binder to make fluid paste which could be screen-printed on the 1050 Al alloy plate. Pulsed Nd:YAG laser was irradiated on the Si paste layer to melt and alloy with Al substrate. Different laser power of 99 W, 179 W and 261 W, was used to see the difference of the microstructure, composition and hardness of the clad layers. When laser power of 179 W was used, the clad layer had overall Si content of 38wt% and composed of fine primary Si particles and fine eutectic phase. At laser power of 261 W, the clad layer had overall Si content of 24wt% and composed of mainly fine eutectic phase. Vickers hardness of HV176.7 and HV150.3 on the clad layer was obtained at laser power of 179 W and 261 W, respectively.

• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.365-370
• /
• 1997

The effects of changes in microstructure of Si phase on the thermal expansion coefficients(CTEs) and tensile properties of the hypereutectic Al-Si foundry alloy(A390) were investigated experimentally. Specimens were prepared by various fabrication processes, such as a permanent mold casting, a squeeze casting and a spray casting process, and subsequently hot-extruded. CTEs of the spray-cast specimen were found to be about 10% lower than those of the permanent mold-cast specimen, and the CTEs of the hypereutectic Al-Si alloy(A390) were changed proportionally with the size of Si phase. Ultimate tensile strength of the spray-cast and hot-extruded specimen was dramatically improved about 100% with improved elongation, compared to that of permanent mold-cast specimen. These improvements are mainly attributed to the reduction in size and aspect ratio of the brittle Si phase, and the elimination of the microvoids/porosities formed during casting.

• Korean Journal of Metals and Materials
• /
• v.48 no.11
• /
• pp.1003-1008
• /
• 2010

In this study, the effect of the reinforcement on the wear behaviour and mechanical properties of hypereutectic Al-Si alloys was investigated. The Gas atomized hypereutectic Al-20Si alloy powders were mixed with 1, 3, and 5 wt.% AlN and TiC ceramic particles and consolidated by hotpress. The Al-20Si powder has both finely dispersed primary Si phases and eutectic structures. The Al-20Si-AlN, TiC composites showed that the reinforcements were distributed along the boundary of the Al-20Si alloy. The UTS increased with increasing the AlN, TiC contents. At a lower load, with an increasing weight fraction of reinforcements, the wear rate decreased in both composites and the wear mechanism was adhesive wear. At a higher load, the shape of the debris changes the mechanism of the AlN composites to abrasive-adhesion wear and this resulted in an increase of the wear rate.

• Journal of Korea Foundry Society
• /
• v.13 no.1
• /
• pp.17-24
• /
• 1993

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.474-480
• /
• 1998

Microstructural characteristics of semi-solid state processed hypereutectic Al-Si alloys have been investigated. Main concern of the present study is to investigate the effects of P and Sr addition on the size and morphology change of the primary Si particles. Refinement of the primary Si particles was observed with the addition of P and Sr at the early stage of semi-solid state processing, but such a refining effects became negligible resulting in Si particles with a near-spherical morphology with continuous stirring. This implies that the microstructural transformation mechanism became more dependent to stirring effects than to the alloying effects during semi-solid state processing. Brittle fracture and agglomeration were proposed as the mechanisms for microstructural alterations during semi-solid state processing.

• Journal of Korea Foundry Society
• /
• v.21 no.6
• /
• pp.328-335
• /
• 2001

The objective of this study is to investigate on manufacturing Al-scrap into hypereutectic Al-Si alloy by using electromagnetic force. The Fe element in the aluminium scrap was controlled by intermetallic compound method and using EMF(electromagnetic force). The most lumped compound was found after 10min holding at $690^{\circ}C$. A number of segregated compound was revealed when imposed to EMF at 30A. The refinement of primary Si particles was achieved by EMF stirring. Primary Si particles were refined and spheroidized most of all with the magnetic intensity of 180G for 10 min.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.416-421
• /
• 1995

Recently Al-Cu-P alloys are used to refine primary Si of hypereutectic Al-Si alloys. Because it has inside AlP compound that acts as nucleation site in the melt, Al-Cu-P alloy has good refinement effect in lower holding temperature and after shoter holding times. In this study Al-Cu-P refinement agent was made by mechanical alloying method. When Al-13.5wt%Cu-1.5wt%P was alloyed mechanically for 30hr in Ar atmosphere by high energy ball mill, it had the refinement effect that showed primary Si size of about $30{\mu}m$ in Al-20wt%Si at $760^{\circ}C$, treated for 15min.