• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.435-438
• /
• 2005

Single phase $Zn_4Sb_3$ with $98.5\%$ of theoretical density was successfully produced by direct hot pressing of elemental powders containing $1.2 at\%$ excess Zn for compensating the evaporation during the process. Temperature dependences of thermoelectric properties were investigated from 4 K to 300 K. Seebeck coefficient, electrical conductivity, thermal conductivity as well as thermoelectric figure of merit showed the discontinuity in variation at 242K, indicating the $\alpha-\beta$, phase transformation. Interestingly, it was found that lattice thermal conductivity by phonons is dominant in total thermal conductivity of $\alpha-\beta$. Therefore, it is expected that thermoelectric properties can be improved by reduction of lattice thermal conductivity inducing lattice scattering centers by doping and solid solution.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.204-209
• /
• 2004

SiC materials have been extensively studied for high temperature components in advanced energy system and advanced gas turbine. However, the brittle characteristics of SiC such as low fracture toughness and low strain-to fracture still impose a severe limitation on practical applications of SiC materials. For these reasons, $SiC_f/SiC$ composites can be considered as a promising for various structural materials, because of their good fracture toughness compared with monolithic SiC ceramics. But, high temperature and pressure lead to the degradation of the reinforcing fiber during the hot pressing. Therefore, reduction of sintering temperature and pressure is key requirements for the fabrication of $SiC_f/SiC$ composites by hot pressing method. In the present work, Monolithic LPS-SiC was fabricated by hot pressing method in Ar atmosphere at 1760 $^{\circ}C$, 1780 $^{\circ}C$, 1800 $^{\circ}C$ and 1820 $^{\circ}C$ under 20 MPa using $Al_2O_3-Y_2O_3$ system as sintering additives in order to low sintering temperature. The starting powder was high purity ${\beta}-SiC$ nano-powder with an average particle size of 30 nm. Monolithic LPS-SiC was evaluated in terms of sintering density, micro-structure, flexural strength, elastic modulus and so on. Sintered density, flexural strength and elastic modulus of fabricated LPS-SiC increased with increasing the sintering temperature. In the micro-structure of this specimen, it was found that grain of sintered body was grown from 30 nm to 200 nm.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.1
• /
• pp.70-75
• /
• 2013

It has fabricated membrane electrode assemblies (MEA) for proton exchange membrane fuel cell by hot-pressing method. The hot-pressing was used for the fabrication of MEA which is composed of commercial platinum electrode on carbon paper. The performance of MEA was studied with different fabrication conditions of temperature, pressure and torque. As the temperature increased, the performance of MEA was increased. and started to decrease l after arrived at the maximum performance of MEA. This is related with good contact between electrode and polymer electrolyte membrane at high temperature and microstructural change at much higher temperature. Similarly, as the pressure increased, the performance of the MEA increased up to highest values and start to decrease. According to the our results, the maximal performance of the MEA was at the temperature of $140^{\circ}C$ and the pressure of $1.5{\times}10^3$ kPa. The optimal torque to assemble the single stack was 3.2 N m.

• Korean Journal of Materials Research
• /
• v.21 no.10
• /
• pp.542-545
• /
• 2011

Half-Heusler alloys are a potential thermoelectric material for use in high-temperature applications. In an attempt to produce half-Heusler thermoelectric materials with fine microstructures, TiCoSb was synthesized by the mechanical alloying of stoichiometric elemental powder compositions and then consolidated by vacuum hot pressing. The phase transformations during the mechanical alloying and hot consolidation process were investigated using XRD and SEM. A single-phase, half- Heusler allow was successfully produced by the mechanical alloying process, but a minor portion of the second phase of the CoSb formation was observed after the vacuum hot pressing. The thermoelectric properties as a function of the temperature were evaluated for the hot-pressed specimens. The Seebeck coefficients in the test range showed negative values, representing n-type conductivity, and the absolute value was found to be relatively low due to the existence of the second phase. It is shown that the electrical conductivity is relatively high and that the thermal conductivities are compatibly low in MA TiCoSb. The maximum ZT value was found to be relatively low in the test temperature range, possibly due to the lower Seebeck coefficient. The Hall mobility value appeared to be quite low, leading to the lower value of Seebeck coefficient. Thus, it is likely that the single phase produced by mechanical alloying process will show much higher ZT values after an excess Ti addition. It is also believed that further property enhancement can be obtained if appropriate dopants are selectively introduced into this MA TiCoSb System.

• Transactions of Materials Processing
• /
• v.18 no.8
• /
• pp.616-624
• /
• 2009

In this work we demonstrate the hot-embossing process under different forming conditions such as forming temperature, load, and holding time in pressing, in order to determine the suitable conditions required for linear patterning on polymer plates (PC). Results showed that the replicated pattern depth increased in proportion to an increase in the forming temperature, load, and time. The reduction of the workpiece thickness increased according to the holding time in the pressing process. In the process of time, the reduction ratio of the workpiece thickness decreased due to the surface area increment of the workpiece, while the pressure on the workpiece declined. In order to reduce the bulging ratio we introduced a temperature difference between the upper and the lower punch.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.171-175
• /
• 1998

$Al_2O_3$-TiC composites were prepared from aluminum, titanium oxide, and carbon fibers by self-propagating high-temperature synthesis(SHS). After the SHS reaction, the TiC phase in the sample was found either fibrous or non-fibrous shape. The fraction of the fibrous TiC phase varied with the amount of $Al_2O_3$ diluent addition. The optimum amount of diluent to make fibrous carbide was determined to be 30%. The fibers were hollow inside and made of multiple grains with a composition of titanium carbide. The hollow fiber formation mechanism was suggested and discussed. The synthesized powders were consolidated to dense composites by hot pressing at $1750^{\circ}C$ under 30 MPa.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.347-358
• /
• 1994

Creep densification and grain growth of alumina powder compacts during high temperature processing were investigated. The creep densification and grain growth of alumina powder compacts during various sintering processes were analyzed by employing the consitutive model by Kwon and Kim. Theoretical results from the constitutive model were compared with various experimental data of alumina powder compacts in the literature including pressureless sintering, sinter forging and hot pressing. The proposed constitutive equations were implemented into finite element analysis program (ABAQUS) to simulate densification for more complicated geometry and loading conditions. The effects of friction between die and powder compact or punch and powder compact during sinter forging and hot pressing are investigated by using the finite element method. Also, high temperature forming processing of alumina compact with complicated shape was simulated.

• Journal of Powder Materials
• /
• v.3 no.4
• /
• pp.246-252
• /
• 1996

$Bi_{2}Te_{3}-Sb_{2}Te_{3}$, $Bi_{2}Te_{3}-Bi_{2}Se_{3}$ solid solutions are of great interest as materials for thermoelectric energy conversion. One of the key technologies to ensure the efficiency of thermoelectric device is to obtain chemically homogeneous solid solutions. In this work, the new process with rapid solidification followed by hot pressing was investigated to produce homogeneous thermoelectric materials. Characteristics of the materials were examined with XRD, SEM, EPMA-line scan and bending test. Property variations of the materials were investigated as a function of variables, such as excess Te quantity and hot pressing temperature. Quenched ribbons are very brittle and consisted of homogeneous $Bi_{2}Te_{3}$, $Sb_{2}Te_{3}$ solid solutions. When the process parameters were optimized, the maximum figure of merit was 3.073$\times$$10^{-3}K^{-4}$. The bending strength of the material, hot pressed at 45$0^{\circ}C$, was 5.87 kgf/${mm}^2$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.957-958
• /
• 2006

Fe doped skutterudite $CoSb_3$ with a nominal composition of $Fe_xCo_{1-x}Sb_{12}(0{\leq}x{\leq}2.5)$ have been synthesized by mechanical alloying (MA) of elemental powders, followed by vacuum hot pressing. Phase transformations during mechanical alloying and vacuum hot pressing were systematically investigated using XRD. Single phase skutterudite was successfully produced by vacuum hot pressing using as-milled powders without subsequent annealing. However, second phase of $FeSb_2$ was found to exist in case of $x\geq2$, suggesting the solubility limit of Fe with Co in this system. Thermoelectric properties as functions of temperature and Fe contents were evaluated for the hot pressed specimens. Fe doping up to x=1.5 with Co in $Fe_xCo_{4-x}Sb_{12}$ appeared to increase thermoelectric figure of merit (ZT) and the maximum ZT was found to be 0.78 at 525K in this study.

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.561-567
• /
• 1991

Submicron ${\alpha}-SiC$ powder with $Al_2O_3$ addition was hot-pressed under the controlled heating and pressurizing schedule. $SiO_2$ layer on ${\alpha}-SiC$ powder was effective for the sintering of ${\alpha}-SiC$ powder when $Al_2O_3$ was used as an additive. Applying of pressure under the controlled schedule accelerated the rearrangment of SiC grains, yielding 98% of theoretical density of SiC even at $1900^{\circ}C$. Flexural strength of the specimen containing 2 wt% $Al_2O_3$ was increased as increasing the hot-pressing temperature up to $2050^{\circ}C$ and maximum value was 800 MPa, while the flexural strength of the specimen containing 10 wt% $Al_2O_3$ was decreased as increasing the hot-pressing temperature above $2000^{\circ}C$ due to the formation of continuous grain boundary phase. Fracture toughness of the specimens was in the range of $3.5~4.5\;MNm^{-3/2}$ regardless of the amount of $Al_2O_3$ addition.