• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.5
• /
• pp.25-30
• /
• 2010

The authors have studied on the corrosion resistance of the hot stamped steel sheets for the application to automotive parts. Recently automotive companies have focused on the hot stamped parts to meet the light weighting needs and the safe reason. Because of the cost reduction of the hot stamped parts, automotive companies increase the usage of the coated steel sheets, especially Al-Si coated steel sheets. The coated layer of Al-Si coated steel sheets contains up to 50% of Fe, which was diffused from the steel sheet, after hot stamping. The hot stamped steel sheet was not phosphated due to the oxidation layer of the coating, however, the result of the water resistance test is similar to that of the conventional GA steel sheets. The pitting depth and the weight reduction of the coated layer of hot stamped steel sheets are less than those of GA steel.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.2
• /
• pp.155-165
• /
• 2018

The objective of the research was to evaluate the effect of particle pre-treatment on physical, mechanical, and durability of jatropha fruit hulls (JFH) particleboard. The pre-treatments included were immersing in cold water, hot water, and acetic acid solution. After each treatment, the particles were dried up to 3% moisture content. Urea-formaldehyde (UF) resin was used to fabricate particleboards with board size, thickness and density target of 25 cm by 25 cm, 0.80 cm, and $0.70g/cm^3$, respectively. Board pressed at $130^{\circ}C$ for 10 minutes, and $25kg/cm^2$ pressure. The evaluation of particleboard followed the JIS A 5908-2003. Whilist their resistance to subterranean termite test (mass loss, mortality, antifeedant value and feeding rate) refers to the Indonesian standard (SNI 01.7207-2006). The physical and mechanical properties of particleboards showed that all pre-treatments decreased the pH of particles. Overall, all particle immersing treatments resulted of better physical and mechanical properties of particleboard than those of untreated ones. The acetic acid treatment resulted the best physical and mechanical properties of particleboard. Based on the mass loss of JFH particleboard, hot water and acetic acid treated particleboards were classified into weak resistance to subterranean attack. The other two treatments were classified into very weak resistance. Hot water treated particleboard provided the highest mortality and antifeedant as much as 87.40% and 34.20%, respectively. Based on antifeedant classification, hot water treated particleboards were classified into moderately strong resistance, while other treatments were categorized into weak resistance. The lowest feeding rate value ($45.30{\mu}g/termite/day$) was attained by hot water treatment.

• Journal of Adhesion and Interface
• /
• v.7 no.3
• /
• pp.16-25
• /
• 2006

Water vapour permeable and water resistant film was laminated to made footwear woven fabric and non-woven fabrics by screen type with thermosetting reactive hot melt adhesive. Optimum conditions of each process were investigated, and the properties of film laminated fabric with optimum conditions are evaluated. The results are as follows. Thermosetting reactive polyurethane hot melt is retain proper heat resistance differently thermoplastic hot melt. Optimum melting adhesive process conditions are as follows ; drum temperature $95^{\circ}C$, hose temperature $97^{\circ}C$, feeding pipe temperature $100^{\circ}C$, screen temperature $105^{\circ}C$, pressure of opposite roller $1kgf/cm^2$, pressure of laminating roller $3kgf/cm^2$, finishing speed 15 m/min, melting temperature $120^{\circ}C$, cooling time 20 s, pressing temperature $130^{\circ}C$, pressing time 30 s. As the thickness of film was increased, the water vapour permeability was decreased but water resistance was increased, and the effect of film is dominant over all the others in the air permeability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.307-312
• /
• 1997

The sea water resistance of cement and concrete must be compared when it used for construction in the ocean. The sea water resistance of the concrete specimens using three types of cements such as ordinary Portland cement, sulfate resistance Portland cement, blastfurnace slag cement were studied. In this study, an accelerated test for access sea water resistance by subjecting the concrete specimens to repeated cycles of concentrated sea water immersion and hot wind drying was employed. This study proved that sulfate resistance Portland cement had higher resistance for sea water.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2000.05a
• /
• pp.115-121
• /
• 2000

As the development of industry water quality of river is going to bad because of waste water of an industrial complex and general home agricultural chemicals exhaust of $SO_3$ and CO gas acid rain and so on. Corrosion damage of boiler factory equipment and so forth occur quickly due to using of the polluted water resulting in increasing leak accident. Especially working life of hot water boiler using the polluted water becomes more short and energy loss increases. The cathodic protection method is the most economical and reliable one to prevent corrosion damage of steel structures. Mg-base alloys galvanic anode protection of cathodic protection method is suitable for than application of hot water boiler using water with high specific resistance such as tap water. This paper is studied on the cathodic protection characteristics of how water boiler. In tap water and 0.001mol/$\ell$ NaCl solution the characteristics of anodic polarization of Mg-base alloys galvanic anode and tube material is investigated the measurement of cathodic protection potential according to the time elaspsed is carried out.

• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.210-216
• /
• 2012

For the recycling of rapid-cooled steel slag, various specimens were prepared with the various replacement ratios of the rapid-cooled steel slag and the addition ratios of polymer binders. The physical properties of these specimens were then investigated by absorption test, compressive strength test, flexural strength test and hot water resistance test, and the pore and the micro-structure analysis was performed using scanning electron microscope. Results showed that the flexural strength increased with the increase of rapid-cooled steel slag and polymer binder, but the compressive strength showed a maximum strength at a certain proportion. By the hot water resistance test, compressive strength and flexural strength decreased remarkably and the total pore volume increased but the pore diameter decreased. SEM observation of the structure before the hot water resistance test revealed a very compact infusion of structure but the decomposition or thermal degradation appeared in polymer binders when observed after the hot water resistance test.

• Applied Chemistry for Engineering
• /
• v.29 no.2
• /
• pp.201-208
• /
• 2018

The ortho- and iso- type unsaturated polyester resins were synthesized and used as a polymer binder of the polymer mortar composite. Styrene monomer and acrylonitrile were used as a diluent for the unsaturated polyester resin. Methyl ethyl ketone peroxide (MEKPO) and cobalt octoate (CoOc) were used as a curing agent and an accelerator, respectively. Four kinds of unsaturated polyester resins were prepared according to types of the resin and diluent, and used as a polymer binder in the preparation of the specimen. A total of 16 polymer mortar specimens were prepared according to the added amount of the polymer binder and subjected to a hot water resistance test, followed by compressive and flexural strength tests, and pore and SEM analyses. As a result, it was found that the strength of the specimen using the iso-type unsaturated polyester resin as the polymer binder was better than that of using the ortho-type unsaturated polyester resin. The total pore volume and diameter measured after the hot water resistance test were reduced compared to the values before the test. In the micrographs observed before the hot water resistance test, the polymer binder, filler and fine aggregate were firmly combined to the co-matrix, but the polymer binder was mostly decomposed in the micrographs observed after the test.

• Applied Chemistry for Engineering
• /
• v.28 no.3
• /
• pp.360-368
• /
• 2017

In order to investigate the durability of high performance polymer concrete composites, polymer concrete specimens were prepared using the ortho-type unsaturated polyester resin (UPR) and iso-type UPR as a polymer binder and the calcium carbonate and silica fine powder as a filler. The durability of polymer concrete specimens was measured by hot water resistance, chemical resistance, pore analysis and SEM observation. The compressive strength of the specimen using the iso-type UPR was higher than that of using the ortho-type UPR, and the compressive strength of the specimen using the silica fine powder was higher than that of using the calcium carbonate filler. From hot water resistance results, it was found that the specimen using the iso-type UPR was superior to that of using the ortho-type UPR and the specimen using the calcium carbonate filler was superior to that of using the silica fine powder. The compressive strength reduction rate was measured after the chemical resistance test and the sodium hydroxide solution showed the highest reduction rate, followed by sulfuric acid, hydrochloric acid and calcium chloride solutions. When using the alkaline solution of sodium hydroxide, the weight reduction rate of the specimen using calcium carbonate was lower than that of using silica fine powder, while for the acidic solutions of sulfuric acid and hydrochloric acid, the weight reduction rate of the specimen using the silica fine powder was lower than that of using calcium carbonate.

• Applied Chemistry for Engineering
• /
• v.19 no.6
• /
• pp.652-660
• /
• 2008

For the recycling of rapid-chilled steel slag, the mechanical strengths and physical properties of EVA-polymer modified mortars with the various replacement ratios of rapid-chilled steel slag were investigated. Twenty five specimens of polymer modified mortars were prepared with the five different amounts of EVA-polymer modifier (0, 5, 10, 15, 20 wt%) and rapid-chilled steel slag (0, 25, 50, 75, 100 wt%). For the investigation of the characteristics of polymer modified mortars, the measurements such as water-cement ratio, unit volume weight, air content for fresh mortar and compressive strength, flexural strength, water absorption, hot water resistance, porosity and SEM investigation for curing specimens were conducted. As a results, with an increase in the replacement ratio of rapid-chilled steel slag, water-cement ratios decreased but unit volume weight increased remarkably. With increasing EVA-polymer modifier and the replacement ratio of rapid-chilled steel slag, percent of water absorption decreased but compressive and flexural strengths increased remarkably. By the hot water resistance test, mechanical strengths decreased but total pore volume and porosity increased remarkably. In the SEM observation, the components of specimen were shown to stick to each other in the form of co-matrix phase before hot water resistance test, but polymer modifier of co-matrix phase was decomposed or deteriorated after hot water resistance test.

• Journal of Adhesion and Interface
• /
• v.19 no.3
• /
• pp.118-122
• /
• 2018

In this study, polyurethane hot melt adhesive containing ester groups was synthesized. Three kinds of chain extenders were used to find out the best chain extender. Results showed that adhesive containing 1,4-butanediol as a chain extender exhibited the highest peel strength among them. Also, it was found that there existed the optimum molecular weight of 1,4-butanediol containing adhesive for make the highest peel strength.. Moreover, hot melt adhesive containing 1,4-butanediol chain extender was applied to various kinds of textiles substrate such as cotton, polyester, and urethane coated polyester textiles to study the effects of different substrates on the peel strength and water resistance at $60^{\circ}C$. It was found that cotton substrate showed the highest peel strength and urethane coated polyester substrate showed the highest resistance on $60^{\circ}C$ water.