• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.213-213
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7NO1 spot-welded by pulse Nd: YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed: center line crack($C_{C}$), diagonal crack($C_{D}$), and U shape crack($C_{U}$). Also, HAZ crack($C_{H}$), was observed in the HAZ region, furthermore, mixing crack($C_{M}$), consisting of diagonal crack and HAZ crack was observed.White film was formed at the hot crack region in the fractured surface after it was immersed to 10%NaOH water. In the case of A5083 alloy, white films in C crack and $C_D crack region were composed of low melting phases, Fe₂Si$Al_8$ and eutectic phases, Mg₂Al₃ and Mg₂Si. Such films observed near HAZ crack were also consist of eutectic Mg₂Al₃. In the case of A7N01 alloy, eutectic phases of CuAl₂, $Mg_{32}$ (Al,Zn) ₃, MgZn₂, Al₂CuMg and Mg₂Si were observed in the whitely etched films near $C_{C}$ crack and $C_{D}$ crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Si in the case of A7N01 aooly, respectively.The $C_{D}$ and $C_{C}$ cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of $C_{M}$ crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The $C_{U}$ crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification. (Received October 7, 1999)

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.34 no.7
• /
• pp.721-727
• /
• 2010

The spontaneous ignition of coal stockpile causes serious safety and economic problems. Such spontaneous ignition occurs in coal stockpile when the rate of heat released by the oxidation of coal is greater than the rate of heat lost to the surroundings. In this study, a two-dimensional unsteady model is adopted for studying spontaneous ignition and the numerical results are compared with experimental results. The numerical results are in a good agreement with the experimental ones. Depending on the porosity, the internal maximum temperature, pressure, and oxygen mass fraction during spontaneous ignition are investigated. On the basis of the numerical results, the transient temperature variations for several shapes of coal stockpiles are analyzed. Further, the physical mechanisms of hot-spot formation and spontaneous ignition are analyzed.

• Asian Pacific Journal of Cancer Prevention
• /
• v.16 no.5
• /
• pp.1677-1682
• /
• 2015

Cancer progression is attained by uncontrolled cell division and metastasis. Increase in tumor size triggers different vascular channel formation to address cell nutritional demands. These channels are responsible for transferring of nutrients and gaseous to the cancer cells. Cancer vascularization is regulated by numerous factors including vascular endothelial growth factors (VEGFs). These factors play an important role during embryonic development. Members included in this group are VEGFA, VEGFB, VEGFC, PIGF and VEGFD which markedly influence cellular growth and apoptosis. Being freely diffusible these proteins act in both autocrine and paracrine fashions. In this review, genetic characterization these molecules and their putative role in cancer staging has been elaborated. Prognostic significance of these molecules along with different stages of cancer has also been summarized. Brief outline of ongoing efforts to target hot spot target sites against these VEGFs and their cognate limitations for therapeutic implications are also highlighted.

• Tribology and Lubricants
• /
• v.12 no.3
• /
• pp.79-84
• /
• 1996

One of the greatest dangers in mechanical face seals is the formation of heat checking and thermal stress cracks on the sliding surfaces. These thermal distortions due to non-uniform heating lead to increase the leakage of the sealed fluids and wear, and with balance of the seal can cause the seal faces to part. In this study heat checking and thermal stress cracks are investigated experimentally. These thermal distortions are explained using the thermal models of the conatct geometries between the seal ring and the seal seat. To overcome these thermal problems, the thermohydrodynamic seal is presented. The newly developed mechanical seal may substantially reduce the friction torque, frictional heating which causes heat checking and thermal stress cracks, and wear.

• Journal of the Korean Society of Industry Convergence
• /
• v.2 no.1
• /
• pp.69-75
• /
• 1999

Intending to develop a new rubber curing process using only microwave, the both the characteristics of cure and the mechanical properties of rubbers for the tire tread, for which a green styrene-butadiene compounds had been cured with 2.45 GHz microwave, have been compared with those of the custom thermal cured rubber. The unintentional hot spot formation in the compound during the microwave curing has not found where the compound has a microwave absorbing ceramic powders in 4.18 weight percents and the supplying voltage has been adjusted to 90 volts. The new microwave process accomplished preheating to 418K in a quarter of the thermal cure time. The average tensile strength of the microwave-cured rubber indicating $190kg/cm^3$ was compatible to that of the thermal cure. In conclusion, the new microwave cure had approved to be applicable in a commercial plant.

• Korean Chemical Engineering Research
• /
• v.58 no.4
• /
• pp.642-650
• /
• 2020

In general, the circulation path of the fluidized particles in a CFB (Circulating Fluidized Bed) boiler is such that the particles entrained from a combustor are collected by a cyclone and recirculated to the combustor via a sealpot which is one of non-mechanical valves. However, when a fluidized bed heat exchanger (FBHE) is installed to additionally absorb heat from the fluidized particles, some particles in the sealpot pass through the FBHE and then flow into the combustor. At this time, in the FBHE operated in the bubbling fluidization regime, if the heat flow is not evenly distributed by poor mixing of the hot particles (800~950 ℃) flowing in from the sealpot, the heat exchanger tubes would be locally heated and then damaged, and the agglomeration of particles could also occur by formation of hot spot. This may affect the stable operation of the circulating fluidized bed. In this study, the unevenness of heat flow arising from structural problems of the FBHE of the domestic D-CFB boiler was found through the operating data analysis and the CPFD (Computational Particle Fluid Dynamics) simulation using Barracuda VR. Actually, the temperature of the heat exchanger tubes in the FBHE showed the closest correlation with the change in particle temperature of the sealpot. It was also found that the non-uniformity of the heat flow was caused by channeling of hot particles flowing in from the sealpot. However, it was difficult to eliminate the non-uniformity even though the fluidizing velocity of the FBHE was increased enough to fluidize hot particles vigorously. When the premixing zone for hot particles flowing in from the sealpot is installed and when the structure is changed through the symmetrization of the FBHE discharge line for particles reflowing into the combustor, the particle mixing and the uniformity of heat flow were found to be increased considerably. Therefore, it could be suggested that the structural modification of the FBHE, related to premixing and symmetric flow of hot particles, is an alternative to reduce the non-uniformity of the heat flow and to minimize the poor particle mixing.

• Journal of the Korean Institute of Landscape Architecture
• /
• v.46 no.3
• /
• pp.36-45
• /
• 2018

Cemeteries in the United States are frequently observed near residential areas in cities even though they are spaces for the dead. However, it has not been fully studied when and how cemeteries were formed in the process of urbanization. Thus, this research aimed to investigate the spatial structure and historical change of cemeteries in Seattle due to urbanization, focusing on the contextual relationship between cemeteries and the surroundings according to two time periods: the early formation period of cemeteries in Seattle and the current period. For this, a mixed method was taken in this paper that combined historical analysis based on old references and historic maps with cluster analysis using GIS. In conclusion, the research found that early cemeteries of Seattle in downtown areas were introduced as by-products of urban formation, but the cemeteries in the suburbs were established ahead of urban growth and neighborhood development. In addition, Seattle's cemeteries not only showed a similar locational pattern to Seattle's shopping centers, but also were positively associated with population distribution given the Hot Spot Analysis. In other words, Seattle's cemeteries were originally located in rural areas, but later came to be located in urban areas, sustaining the landscape of American rural cemeteries.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.4
• /
• pp.421-439
• /
• 2003

Statement of problem : It is difficult to obtain a good titanium casting body using the traditional sprue design because of high melting point of Ti, and the low fluidity and high reactivity of molten Ti. Purpose : A new sprue design for titanium casting bodies needs more trial and error. In order to decrease the number of trial and error, computer simulation(MAGMASOFT, Magmasoft Giessereitechnologie GmbH, Achen, Germany) was used to optimize sprue design in U-shaped implant superstructures. Material and method : Five kinds of sprue were examined for the design of the sprue former for titanium casting: Sprue design A(sprue length 4 mm, rectangular shape, 4 sprues), Sprue design B(sprue length 4 mm. round shape. radius 2 mm, 7 sprues), Sprue design C (sprue length 2 mm, round shape, radius 2 mm, 7 sprues). Sprue design D (sprue length 2 mm, cone shape, large radius 3mm. small radius 2mm, 7 sprues), and Sprue design E( sprue length 2 mm. one unit channel shape). Sprue design F(sprue length 2mm, one unit channel shape) was also examined for the design of the customized sprue former in the Biotan system(Schutz Dental Gmbh, Germany). The casting bodies were taken in Sprue design A, Sprue design D, Sprue design E, and Sprue design F in the Biotan casting system. The numerically predicted defects were compared with the experimental dental castings by the radiographic and sectional view observations. Results : 1. According to the result of computer simulation, turbulence during mold filling was decreased in the sequence of Sprue design F, Sprue design E, Sprue design D, Sprue design C, Sprue design B, and Sprue design A. 2. The calculated solidification time contours indicate that hot spot was moved from the casting body to the sprue button in the sequence of Sprue design A, Sprue design B, Sprue design C, Sprue design D, and Sprue design E. The filling pattern of Sprue design F was similar to that of Sprue design E. 3 The predicted filling pattern shows that less turbulence was found in the customized sprue former than in the standard sprue former. 4. According to the results of the radiographic and cross sectional observations, casting defects less than 1mm were found at the center of a casting body with Sprue design E and Sprue design F. However, larger casting defects of 4mm were found in a casting with Sprue design A. 5. The predicted casting porosity was similar to that of the real casting. Conclusion : One unit channel-type and customized sprue former can be recommended. Further research and developement of various sprue designs using computer simulation in necessary to optimize casting design, in order to reduce the formation of casting defects in implant titanuim super-structures.