• Korean Journal of Agricultural Science
• /
• v.12 no.2
• /
• pp.292-308
• /
• 1985

This study was performed to obtain the basic data which can be applied to the use of foamed mortars using foaming agent of prefoamed type. The data was based on the properties of foamed mortars depending upon various mixing ratios of cement to fine aggregates, flow values and foam-cement ratio to compare those of cement mortar. The results obtained were summarized as follow; 1. At the mixing ratio of 1:0 and the foam-cement ratio of 6.00%, the increasing rate of water-cement ratio was 25% by flow $200{\pm}5mm$, 28% by flow $240{\pm}5mm$ and 32% by flow $280{\pm}5mm$. But it decreased as the mixing ratio gets poorer. The result showed that water amount increased because of the high viscosity caused by the increase of foam-cement ratio. The decrease of water-cement ratio was the greatest when the foam-cement ratio was 1.50%. 2. Absolute aridity bulk density of foamed mortars decreased with the increase of foam-cement ratio and the decrease of flow values. 3. Generally, compressive, tensile and bending strenghs of foamed mortars decreased with the decrease of flow values and the increase of foam-cement ratio. 4. The compressive strength was in proportion to tensile strength. It was estimated that the compressive strength was 8.8 times of tensile strength. The compressive strength was in proportion to bending strength. It was estimated that the compressive strength was 4.0 times of bending strength. The bending strength was in proportion to tensile strength. It was estimated that the bending strength was 2.1 times of tensile strength. 5. At the mixing ratio of 1:1 the lowest absorption rates were showed by foamed mortars, respectively. It was significantly higher at the early stage of immersed water.