• Journal of Welding and Joining
• /
• v.8 no.4
• /
• pp.20-26
• /
• 1990

In this study, to make research on its optimum condition in friction weld when the heating pressure is change during 1.6 to 3.0 $kgf/mm^2$, the experiment was performed with metal bearing under various condition; 1600 r.p.m spindile speed, 0.6 $kgf/mm^2$ preheating pressure, upset pressure 2.6 $kgf/mm^2$, 0.5 seconds preheating time, 1.7 seconds heating time, water and air was ejected 6 $kgf/mm^2$ into the bushing. On the basis of the experimental results, the following conclusion are drawn; 1) At the area of weld interface, the heardness is shown the maximum value and heat-affected zone about 0.5mm both sides. 2) Bending strength is shown the optimum heating pressure 2.4 kgf/mm. 3) With the approach of the flash, Sn is increased only 2 mm in A-alloy structure.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.1
• /
• pp.63-69
• /
• 2006

This study deals with the friction welding of A2024- T6 to A6061- T6; The friction time was variable conditions under the conditions of spindle revolution of 2000rpm, friction pressure of 50MPa, upset pressure of 100MPa, and upset time of 5.0seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied, of friction weld, and so the results were as follows. 1. When the friction time was 1.5seconds under the conditions, the maximum tensile strength of the friction weld happened to be 292MPa, which is $94.2\%$ of the base material's tensile strength(310MPa). At the same condition, the maximum shear strength was 2l2MPa, which is equivalent to $103\%$ of the base material's shear strength (205MPa). 2. At the same condition, the maximum vickers hardness was Hv 146 at A2024- T6 nearby weld interface, which is higher Hv3 than condition of the friction time 0.5seconds, and the maximum vickers hardness was Hvl20 from weld interface of A6061-T6, which is higher Hv28 then base material's. 3. The results of microstructure analysis show that the structures of two base materials have fractionized and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.6
• /
• pp.29-36
• /
• 2007

The present study examined the mechanical properties of the friction welding of Ni-Cr-Mo to SM45C. Friction welding was conducted at welding conditions of 2,000 rpm, friction pressure of 100MPa, friction time of 0.8, 1.0, 1.2, 1.4, 1.6, 1.8, 2.0 seconds, upset pressure of 150MPa, and upset time of 3.0 seconds. When the friction time was 1.6 seconds, the maximum tensile strength of the friction weld happened to be 1,020MPa, which is 120% of the base material's tensile strength(850MPa). At the same condition, the maximum shear strength was 438MPa, which is equivalent to 103% of the base material's shear strength(425MPa). At the same condition, the maximum vickers hardness was Hv490 at Ni-Cr-Mo nearby weld interface, which is higher Hv40 than condition of the friction time 0.8 seconds, and the maximum vickers hardness was Hv305 from weld interface of SM45C, which is higher Hv12 than condition of the friction time 0.8 seconds. The results of microstructure analysis show that the structures of two base materials have fined and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.1
• /
• pp.138-143
• /
• 1987

Friction welding has emerged as a reliable process for high-production commercial applications with significant economic and technical advantages. But nondestructive test in friction weld was not clearly developed. Therefore the experimental verification is necessary in order to understand the characteristcs of the pulse echo effects according to various change in welding conditions. This paper presents an attempt to determine the relationship between the varios welding conditions and the coefficients of reflection using the ultrasonic pulse echo method in dissibilar metals friction weld. The new approach of calculating the coefficients of reflection based on measured amplitudes of the echoes is applied in this paper. These coefficients provides a single quantitative measurement which involves both acoustic energy reflected at the welded interface as well as transmitted across the interface. As a result, it was known that the quantitave relationship between welding conditions and the coefficients of reflection using the ultrasonic pulse echo exists in dissimilar metals friction weld.

• Journal of Ocean Engineering and Technology
• /
• v.2 no.2
• /
• pp.112-121
• /
• 1988

A study on friction welding of carbon steel bar (SM45C) to chrome molybedenum steel bar(SCM4) is examined experimentally through tensile test, hardness test, microstructure test and fatigue test. so, this paper deals with optimizing the welding concitions and analyzing various mechanical properties about friction welds of SM45C to SCM4 steel bars. The results obtained are summarized as follows; 1) For friction welded joints of SM45C to SCM4 steel bars, the total upset(U)increases linearly with an increase of heating time ($t_{1}$) till 6s. 2) The determined optimum welding conditions are heating time ($t_{1}$)2s, upsetting time($t_{2}$), 3s, heating pressure($p_{1}$), 4kgf/$mm^{2}$(39.2MPa), upsetting pressure($p_{2}$, 8kgf/mm$^{2}$(78.4MPa) and rotating speed(N), 2, 000rpm when the total upset(U) is 3.4mm, resulting in a computed relationship between the joint tensile strength .sigma.$_{t}$ (kgf/mm$^{2}$and the total upset U(mm); .sigma.$_{t}$ =$0.21U^{3}$ - $3.38U^{2}$ +17.03U + 66.00 3) As the elongation is increased more and more, the fracture position becomes away from weld interface and the fractures are similar to those of SM45C. Fracture is taken place on SM45C side. 4) The weld interface of two dissimilar materials is mixed strongly, and the heat affected zone is about 2.0mm at SM45C while about 2.7 mm at SCM4 side. Therefore, the welded zone and heat affected zone are very narrow, comparing with those of the joints welded by the other welding methods. 5) The fatigue strengths at N=10$^{6}$ cycles of SM45C, SCM4 and friction welded joints are 23kgf/$mm^{2}$, 33kgf/$mm^{2}$(220.5 MPa), and 22.5kgf/$mm^{2}$(220.5MPa) respectively, and fracture at friction welded joint takes place at the side of SM45C. 6) The hardness of the friction weld interface is 3 times higher than that of base metal. 7) Fatigue strength of friction welded joint is higher than that of base metal. 8) Notch sensitivity factor of friction welded joint is lower than that of base metal.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.6
• /
• pp.75-81
• /
• 2012

Dissimilar material friction welding such as STD11 and SCM440, we are considering of such things as strength and tenacity of welding interface, which consist of friction welding rotation frequency, friction heating pressure, upset forging-pressure, friction heating time, and upset forging-pressure time. From the study, obtaining the interrelationship between welding condition and quality(toughness, tenacity), we can set the best range of welding condition. while performing acoustic emission examination for the nondestructive evaluation, we can deduce the interrelationship among total acoustic emission counts, friction welding variable, and quality during friction welding, which can solve the manufacturing difficulty and enhance the economic value.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.4
• /
• pp.49-55
• /
• 2006

This study deals with the friction welding of SM25C and SCNCrM-2B; The friction time was variable conditions under the conditions of spindle revolution 2,000rpm, friction pressure of 100MPa, upset pressure of l50MPa, and upset time of 4.0 seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied, and so the results were as follows. 1. When the friction time is 2.0 seconds, the tensile strength of friction welds was 874MPa, which is around as much as 117% of the tensile strength of base metal(SM25C), the bending strength of friction welds was 1,354MPa, which is around as much as 108.9% of the bending strength of base metal(SM25C). 2. At the same condition, the maximum vickers hardness was Hv443 at SCNCrM-2B nearby weld interface, which is higher Hv20 than condition of the friction time 0.5 seconds. 3. The results of microstructure analysis show that the structures of two base materials have fractionated and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Journal of Welding and Joining
• /
• v.8 no.1
• /
• pp.43-53
• /
• 1990

The transient temperature distribution in the continuous friction welding 304 stainless steel bars is investigated by experimental and analytical methods. It is calculated by F.D.M. (finite difference method). The heating pressure, the rotational speed and friction coefficient obtained from experiment are used to determine the heat input at the contacting surface. Thermal properties of the workpiece are the function of temperature. The calculated temperature is well coincided with the measured value. The grain size at weld interface is extremely small due to the severe plastic deformation at high temperature, and result of this refined zone reveals higher hardness value. Because the HAZ is very narror about 2-3 mm, welding defects do not occure.

• Journal of Welding and Joining
• /
• v.26 no.5
• /
• pp.79-89
• /
• 2008

With the increased use of surface textured steel sheet in body-in-white assembly, resistance spot weldability of these steels is considered to be an important subject. This study evaluated nugget formation and weldability by measuring dynamic resistance with various weld pressure, current, and weld time for steel sheet with two different surface roughnesses. The surface roughness for T-H steel ($R_{a}=1.70\;{\mu}m$) was higher than that for T-L steel ($R_{a}=1.33\;{\mu}m$), and resulted in increased contact resistance and heating for T-H steel spot welding. Therefore, at low weld current and weld cycle ranges, the T-H steel showed better weldability over the T-L steel. The evaluations of weld interface showed that the fusion zone in the T-H steel sheet was continuous in contrast to discontinuous fusion zone for T-L steel sheet at the same welding conditions. A comparison of dynamic resistance and tensile-shear strength (TSS) between T-H and T-L steel sheet suggested that high surface roughness provided larger heating at early cycle of welding and larger TSS.

• Journal of the Korean Society of Safety
• /
• v.16 no.3
• /
• pp.19-25
• /
• 2001

The friction-welding SM25C is a substitute for the suing steel that is utilized in the machinery, airplane, and automobile, ok. This substitution would provide reduction of material and weight of welding parts. From the result we found that the strength of the friction welded joint was 529-617MPa and the toughness 1.2 times higher than that of the base metal. The optimal condition of friction welding was found as follows : n=2000rpm, $P_1$=68㎫, $P_2$=137MPa, $t_2$=2sec, $t_1$=2-4sec, Considering the strength, the hardness, and the reduction of area in the friction welding, the fiction welding using SUP9A and SM25C was found to cause no problem in on-the-job application.