• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.05a
• /
• pp.97-100
• /
• 2006

This paper report the result of the investigation on the properties of drying shrinkage for alkali-activated slag mortar in different relative humidity Commonly we know that drying shrinkage means lost more moisture but the mechanism of drying shrinkage of alkali activated slag mortar is not entirely due to the quantity of weight loss of water from mortar. pore size distribution and the calcium silicate hydrate gel characteristics have a critical influence on the magnitude of drying shringkage to alkali activated slag mortar. For this investigation, Ca(OH)2, Na2SiO4 were as alkali activator with 5 dosages(6%, 9%, 12%, 15%, 20%) and curing condition were three different relative humidity(35%, 65%, 95%) at $20{\pm}3^{\circ}C$

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.221-224
• /
• 2005

In order to traffic safety during winter season, snowfall and cold area has been spread the deicing chemicals, and the spraying amount is increasing every year. Use of deicing chemicals has been and will continue to be a major part of highway snow and ice control methods. Chloride-containing chemicals such as calcium chloride or rock salt are main deicers for the road. Extensive use of chloride deicers is, however, the source of substantial cost penalties due to their corrosive action and acceleration to deterioration concrete structures. Deterioration due to de-icer salt occurs in practice in concrete pavement, dike, barrier and similar structure. This paper reports the results of effect of de-icer salt on durability of concrete structure in winter. To protect concrete structure from damage by de-icer salt in winter, the exposure test was performed using three methods such as increase in design strength upto 35MPa application of granulated blast furnace slag powder, and concrete sealer. Of these, the method of increase in design strength upto 35MPa showed better durability for deterioration by de-icer salt.

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.651-656
• /
• 1993

Granulated Y-TZP powders were coated by using Sol-Gel method and the coating effect of Al2O3 on the isothermal phase transformation in Al2O3 coated Y-TZP powders was investigated. During aging, tetragonal phase in Y-TZP powder were isothermally transformed to monoclinic, but the tetragonal phase in Al2O3 coated Y-TZP powders was continuously retained in spite of long aging. It can be considered that the improvement of thermal stability of tetragonal phase in Al2O3 coated Y-TZP powders may be due to the increase of constraint effect near tetragonal phase, and the suppression of surface transformation by obstructing the reaction between the surface of Y-TZP and H2O.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.489-492
• /
• 2004

Compressive strength of self-compacting concrete with waste concrete powder(SCCWCP) linearly decreased as the containing ratio of WCP increas. When granulated blast furnace slag(SG) was contained for improving the rheological properties of SCCWCP, compressive strength of concrete with $15\%$ SG and $15\%$ WCP was increased in comparison with that of concrete with $30\%$ WCP. Splitting tensile strength of SCCWCP higher increased than that of CEB-FIP at same compressive strength. Relationship between compressive strength and elastic modulus of SCCWCP indicated a similar function with CEB-FIP fuction.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.11a
• /
• pp.186-187
• /
• 2013

Recently, high fluidity concrete is becoming more prevalent. High fluidity concrete uses admixture or thickener in order to prevent separation of materials due to increased fluidity, and, especially, BS is becoming more use for reduced heat of hydration and improved long-term strength. This study examined the effect of BS on fluidity of cement paste from a rheological viewpoint. As for BS types, materials equivalent to 1 types of KS F 2563 and the cement mass was substituted by 20, 40, 60, 80%.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.127-136
• /
• 2015

To evaluate the effects of limestone powder and silica fume on the properties of high-strength high-volume ground granulated blast-furnace slag (GGBFS) blended cement concrete, this study investigated the rheology, strength development, hydration and pozzolanic reaction characteristics, porosity and pore size distribution of high-strength mortars with the water-to-binder ratio of 20, 50 to 80% GGBFS, up to 20% limestone powder, and up to 10% silica fume. According to test results, compared with the Portland cement mixture, the high-volume GGBFS mixture had much higher flow due to the low surface friction of GGBFS particles and higher strength in the early age due to the accelerated cement hydration by increase of free water; however, because of too low water-to-binder ratio and cement content, and lack of calcium hydroxide content, the pozzolanic reactio cannot be activated and the long-term strength development was limited. Limestone powder did not affect the flowability, and also accelerate the early cement hydration. However, because its effect on the acceleration of cement hydration is not greater than that of GGBFS, and it does not have hydraulic reactivity unlikely to GGBFS, compressive strength was reduced proportional to the replacement ratio of limestone powder. Also, silica fume and very fine GGBFS lowered flow and strength by absorbing more free water required for cement hydration. Capillary porosities of GGBFS blended mortars were smaller than that of OPC mortar, but the effect of limestone powder on porosity was not noticeable, and silica fume increased porosity due to low degree of hydration. Nevertheless, it is confirmed that the addition of GGBFS and silica fume increases fine pores.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.1
• /
• pp.57-62
• /
• 2008

Twelve mortars were mixed and tested to explore the effect of gypsum on the compressive strength development and shrinkage strain of alkali-activated mortars. Powder typed sodium silicate and ground granulated blast-furnace slag were employed as alkaline activator and source material, respectively, to produce cementless mortar. The main variables investigated were alkali quality coefficient combining the concentration of activator and main compositions in source material, and the adding amount of gypsum ranged between 1 and 5% with respect to the weight of binder. Initial flow, compressive strength development, modulus of rupture, and shrinkage strain behavior of mortar specimens were measured. In addition, the hydration production of alkali-activated pastes with gypsum was traced using X-ray diffraction and energy-dispersive X-ray analysis combined with scanning electron microscope image. Test results showed that the initial flow of slag-based alkali-activated mortar was little influenced by the adding amount of gypsum. On the other hand, the effect of gypsum on the compressive strength of mortar specimens was dependent on the alkali quality coefficient, indicating that the compressive strength increased with the increase of the adding amount of gypsum until a certain limit, beyond which the strength decreased slowly. Shrinkage strain of mortar tested was little influenced by the adding amount of gypsum because no ettringite as hydration product was generated. However, the adding of gypsum had a beneficial effect on reducing the microcrack in the alkali-activated mortar.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.6
• /
• pp.527-532
• /
• 2018

The objective of the present study is to evaluate a practical approach for enhancing the compressive strength and minimizing deforming of aerated concrete. Test results measured in the aerated concrete mixes that were produced using 40% ground granulated blast-furnace slag (GGBS) as a replacement of cement and cured under different conditions (i.e., high temperatures of $40^{\circ}C$ and $60^{\circ}C$ for 10 hrs or 15 hrs) were compared with those obtained from the specimens cured under room temperature. No deforming was observed in the mixes with 40% GGBS. The compressive strength of the prepared aerated concrete cured under high temperature was higher than that of the concrete cured at room temperature, even at the lower ranges of the apparent dry density. However, the curing time is needed to be controlled as not exceeding 10 hrs at the temperature of $60^{\circ}C$ to prevent the decrease in the compressive strength due to foam mergences.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.6
• /
• pp.85-91
• /
• 2020

The necessity for ground reinforcement of structures has been increasing in South Korea because buildings have encountered constructional problems such as inclined structures and collapses caused by earthquakes or differential settlement of the foundations. With regard to a ground reinforcement method, an increasing number of high-strength concrete piles have been used based on their advantages, including a wide range of penetration depth and a high load-bearing capacity. However, problems such as the destruction of a pile head during on-site placement work can occur when the pile has insufficient strength. For this reason, the strength of such piles should be managed more thoroughly. Thus, this study analyzed the strength properties of high-strength concrete piles using blast furnace slag (BFS) powder as a cement replacement, which was generated as an industrial byproduct. The analysis results indicated that the compression strength of the concrete piles increased when 10% to 20% of the cement was replaced with ground granulated blast-furnace slag (GGBS). In addition, the compression strength of the concrete piles was calculated to be 80.6 MPa when 20% of the cement was replaced with GGBS, which was greater by 5% than that of an ordinary Portland cement (OPC) specimen.

• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.225-230
• /
• 1988

The strength and thermal shock resistance of $Al_2O_3-ZrO_2$ composites have been studied. The tetragonal $ZrO_2$ powder containing 1 mol.% $Y_2O_3$ and monoclinic $ZrO_2$ powder were prepared by coprecipitation method and subsequently mixed with $Al_2O_3$ powder and granulated by sieving. Duplex composites were prepared by dry mixing matrix agglomerate with 15 to 30 vol.% of dispersion agglomerate, followed by pressing and sintering at 1$600^{\circ}C$ for1 hr. These $Al_2O_3-ZrO_2$ 2 composites having heterogeneous structure showed improved thermal shock behaviors because of the microcracking and pores in dispersed granules, and compressive stresses around dispersed granules resulting from $ZrO_2$ transformation.