• Advances in concrete construction
• /
• 제10권2호
• /
• pp.127-140
• /
• 2020

This study explores the feasibility of granite waste aggregate (GWA) as a partial replacement of natural fine aggregate (NFA) in binary blend self-compacting concrete (SCC) prepared with fly ash. Total of nine SCC mixtures were prepared wherein one was Ordinary Portland cement (OPC) based control SCC mixture and remaining were fly ash based binary blend SCC mixtures which included the various percentages of GWA. Fresh properties tests such as slump flow, T₅₀₀, V-funnel, J-ring, L-box, U-box, segregation resistance, bleeding, fresh density, and loss of slump flow (with time) were conducted. Compressive strength and percentage of permeable voids were evaluated in the hardened state. All the SCC mixtures exhibited sufficient flowability, passing ability, and resistance to segregation. Besides, all the binary blend SCC mixtures exhibited lower fresh density and bleeding, and better residual slump (up to 50% of GWA) compared to the OPC based control SCC mixture. Binary blend SCC mixture incorporating up to 40% GWA provided higher compressive strength than binary blend control SCC mixture. The findings of this study encourage the utilization of GWA in the development of binary blend SCC mixtures with satisfactory workability characteristics as a replacement of NFA.

• 산업기술연구
• /
• 제31권A호
• /
• pp.53-57
• /
• 2011

Recently due to dramatically increasing demand of liquid crystal display (LCD) panel in IT industry, the used LCD panel glass has been wasted from electronic items, and also panel glass of poor quality during manufacturing process. The wasted LCD panel glass was crushed in the range of 0.42 to 2mm and evaluated for its usefulness as a aggregate in production of cement concrete brick. Cement concrete specimens with various mixing ratios of weathered granite soil, LCD panel glass and cement were cured in wetness for 7 days at $40^{\circ}C$ and then tested for uniaxial comprehensive strength (UCS)(KS F 4004 method). Specimen with a mixing ratio, 1:6:3, of weathered granite, LCD panel glass and cement, respectively, showed the highest average in the UCS test($26.51N/mm^2$). It is much higher than that of commercial brick without glass($17.00N/mm^2$). Conclusively waste LCD panel glass can be reutilized economically as a raw building material of good quality.

• 한국건축시공학회지
• /
• 제15권6호
• /
• pp.545-551
• /
• 2015

본 연구에서는 국내의 석회암 광산에서 시멘트 제조를 위해 채굴되는 석회석을 시멘트 제조용으로 사용하지 못하는 저품위 석회암 폐석을 분쇄 및 체가름 등의 골재 생산설비를 통하여 제조한 석회암 굵은 골재를 고강도 콘크리트용 골재로의 활용성을 검토한 것이다. 즉, 석회암 굵은 골재를 사용한 고강도 콘크리트의 유동성, 공기량, 압축강도 등의 시공 특성을 화강암 굵은 골재에 대한 치환율로 변화시켜 그 성능을 검토하였다. 실험결과 굳지 않은 콘크리트 및 경화 콘크리트에서의 시공특성은 화강암 골재를 사용한 고강도 콘크리트와 동등 이상의 양호한 시공품질이 확보되는 것을 확인할 수 있었다.

• Nuclear Engineering and Technology
• /
• 제54권12호
• /
• pp.4449-4459
• /
• 2022

In this study, an NF₃ plasma etching reaction with a cobalt oxide (Co₃O₄) films grown on the surface of inorganic compounds using granite was investigated. Experimental results showed that the etching rate can be up to 1.604 mm/min at 380 ℃ under 150 W of RF power. EDS and XPS analysis showed that main reaction product is CoF₂, which is generated by fluorination in NF₃ plasma. The etching rate of cobalt oxide films grown on inorganic compounds in this study was affected by surface roughness and etch selectivity. This study demonstrates that the plasma surface decontamination can effectively and efficiently remove contaminated nuclides such as cobalt attached to aggregate in concrete generated when decommissioning of nuclear power plants.

• 터널과지하공간
• /
• 제21권4호
• /
• pp.320-327
• /
• 2011

본 연구는 ○○ 석회석 광산의 화강암 폐석을 이용한 부순 모래를 전색재로 이용하기 위하여 그 현장의 주변에서 쉽게 구할 수 있는 바다 모래, 강 모래, 점토와 물의 전색재와 동일한 조건으로 모르타르 블록의 시험발파를 통해 전색효과에 대한 비교가 이루어졌다. 이때 모르타르 블록은 폭 50 cm, 길이 50 cm와 높이 70 cm로 제작하였다. 전색재료들에 대한 물리.역학적 특성을 알아보기 위하여 체가름 시험, 직접전단시험과 압출시험이 수행되었다. 모르타르 발파시험에서 전색길이 10 cm 및 20 cm에 대하여 폭발 충격압에 따른 강봉의 축방향 변형율과 전색재의 분출속도가 동적 변형율 측정기에 의해 측정되었다. 강봉의 축방향 변형율은 화강암 부순 모래가 가장 크게 나타났으며, 전색재의 분출속도는 물을 전색재로 사용하였을 때 가장 작은 값을 보이고 있다. 이 결과는 사용된 전색재의 발파 공내 다짐단위중량, 입도분포, 전단저항 및 압출시험결과와 상호 연관성을 보이고 있다. 전색재의 분출속도와 축방향 변형률은 서로 지수적으로 반비례하는 경향을 나타낸다.