• Journal of Magnetics
• /
• v.3 no.1
• /
• pp.15-20
• /
• 1998

A newly designed magnetic annealing apparatus was used for the treatment of Fe-3%Si steels. With the help of this device, the effect of magnetic annealing on magnetostriction was studied in a wide spectrum of external elastic stresses. It was shown that magnetostriction properties of Fe-Si steels were improved in the compressed state through magnetic annealing, while those in the unstressed state or under tensiion were found to be practically unchanged.

• Journal of Magnetics
• /
• v.11 no.3
• /
• pp.111-114
• /
• 2006

We electroplated copper-cobalt thin films on a silicon substrate, which had 150 nm thick copper seed layer. The adhesion between the two metallic layers could be increased by utilizing a proper organic additive, pulse plating technique, and high temperature annealing. The thin films exhibited columnar growth of the deposits and enhanced adhesion. This is attributed to the grain growth mechanism introduced by the additive and annealing.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.625-626
• /
• 2008

The magnetic domain-refining techniques such as ball scratching, laser irradiation and plasma have been developed to reduce the domain wall spacing and thus iron losses in Fe-3%Si grain-oriented silicon steels. In view point of magnetic properties, it was supposed that the locally residual stresses change the magnetoelastic energy of the material and thus the spacing between $180^{\circ}$ domain walls decreases in order to reduce the magnetostatic energy. The effect of laser irradiation on iron loss and magnetostriction reduction for Fe-3%Si grain-oriented steel were investigated. Since the local tensile stresses were induced at the surface of Fe-3%Si steel by the laser irradiation, the minimum iron loss caused by reducing eddy current loss was obtained in spiete of the decrease of permeability by hindering eddy current loss was obtained in spite of the decrease of permeability by hindering the domain wall movement around the induced stress field. Furthermore, the laser treated 3%Si steel has lower magnetostriction as compared to non laser-treated steel and is less sensitive to applying pre-stresses due to the volume reduction of $90^{\circ}$ domain in materials.

• Proceedings of the KIPE Conference
• /
• 2001.10a
• /
• pp.93-97
• /
• 2001

A new compact, low-energy electron beam irradiator has been developed. The core-loss of silicon steels can be reduced by magnetic-domain refinement method. The irradiator was developed for the application of core-loss reduction using the method. The beam energy of the irradiator can be varied from 35 to 80 keV and the maximum current is 3mA. The irradiation area is designed to be $30\times30mm2$ now and will be upgraded to $30\times150mm2$ using a scanning magnet and scanning cone. The electron beam generated from 3 mm diameter LaB6 is extracted to the air for the irradiation of the silicon steels in the air. A special irradiation port was developed for this low-energy irradiator. A havar foil with $4.08{\mu}m$ thickness were used for the window and a cold air-cooling system keeps the foil structure by removing heat at the window. The irradiator system and its operation characteristics will be discussed.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.20 no.7
• /
• pp.639-647
• /
• 2009

In this work, wrapping conductors with thin magnetic materials is proposed as a magnetic shielding method. The 0.1 mm thick metal sheets of mu-metal, grain-oriented electrical steel, and non-oriented electrical steel were produced from commercial alloy sheets through cold rolling and followed high temperature annealing. In case of 3-phase electric currents, mu-metal was the best in shielding performance at a B-field magnitude of about 100 ${\mu}T$, whereas silicon steels were better than mu-metal at a B-magnitude over 500 ${\mu}T$. In addition, wrapping with silicon steel(inner) together with mu-metal(outer) resulted in a shielding factor less than 0.1 even at 500 ${\mu}T$. These results are due to changes in hierarchy of magnetic permeabilities of the materials with increasing magnetic field strength. In case of single-phase electric current, B-magnitude outside the magnetic shell was rather increased compared to the unshielded case. This result is explained by vector composition of B-fields near magnetic shielding materials.