• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.6
• /
• pp.468-472
• /
• 2005

In order to prevent adhering of molten glass on a mold wall, the wall is swabbed with lubricant oil before forming. However, the swabbing process can be removed from the entire processes of the glass forming if the mold wall is made of a porous sintered material. The purpose of the present study is to manufacture a sintered material(having a sintered density of $85{\~}90\%$)which is the most appropriate into. plane material for a glass mold. For the research, SUS310L-based coarse powder (${\~}150{\mu}m$) and SUS420J2-based fine powder ($40{\~}50{\mu}m$) were used for the compact materials, and effects of compaction pressure and sintering condition(atmosphere, temperature) were investigated. The results obtained were as fellows. (1) By means of solid phase sintering, a desired sintering density could not be achieved in any case when using a 310L-based powder having a large particle size. (2) When sintering green compacts(compaction pressure of $2ton/cm^2$) in a commercial vacuum furnace(at $1300^{\circ}C$ for 2 hours), the sintered compacts had densities of $6.2g/cm^3(79\%)$ for 310L + 0.03$\%$B, $6.6g/cm^3 (86\%)$ for 420J2, $7.3g/cm^3(95\%)$ for 420J2+(0.03)$\%$B, and $7.6g/cm^3(99\%)$ for 420j2+(0.06)$\%$B, respectively. As a result, it is regarded that sintered compacts having a desired porosity may be achieved by vacuum sintering the 420J2-based powder (low pressure compaction) and the 310L+0.03$\%$B-based powder (high pressure compaction).