• 대한치과보철학회지
• /
• 제36권1호
• /
• pp.26-49
• /
• 1998

The purpose of this study was to confirm the formation of hybrid layer and resin tags in dentin tissue and the possibility of bonding between luting cements used for the prosthesis and the resinous surface coated with resin bonding agents to prevent the dentin hypersensitivity after abutment preparation. Some resin bonding agents, which may have the possibility of bonding with polyacrylic acid as a liquid ingredient of polycarboxylate and glass ionomer cements, were selected. All-Blond desensitizer containing NTG-GMA and BPDM, Scotch-Bond Multipurpose plus containing HEMA, and XR-bond containing organophosphate were selected as a coating agent. Dental cements were zinc phosphate, polycarboxylate, and glass ionomer cement. After the exposed dentin surface of premolars was ethced with 10% phosphoric acid and coated with resin bonding agents, the morphology of treated surfaces and the resin tags and hybrid layers on sectioned surfaces were observed by SEM. Shear bond strength between the resin bonding agents and 3 kinds of cements was measured 24 hours after bonding. On the debonded surfaces of the shear bond strength tested specimens, the cement tags and the bonding sites between the resin materials and cements were examined by SEM. Following conclusions were drawn : 1. Coating of dentin with resin bonding agents had no effect on the shear bond strength of zinc phosphate cement. 2. Both of polycarboxylate and glass ionomer cements showed the increased shear bond strength by the dentinal coating with Scotch-Bond Multipurpose plus containing HEMA. However, in the case of dentinal coating with some agents containing NTG-GMA and BPDM or organophosphate, polycarboxylate cement exhibited the lowered shear bond strength, and glass ionomer cement showed the unchanged shear bond strength. 3. Complete obstructions of dentinal tubules were observed on the dentin coated with All-Bond desensitizer or XR-bond, but distinct shape of the orifices of dentinal tubules was observed consistently on the dentin coated with Scotch-Bond Multipurpose plus. 4. The hybrid layer was thickest on the dentin coated with All-Bond desensitizer, and the length of resin tags was longest on the dentin coated with Scotch-Bond Multipurpose plus. 3. On the debonded specimens which had been bonded with polycarboxylate cement or glass ionomer cement after coating with Scotch-Bond Multipurpose plus, the cement tags and the bonding sites between the resinous surface and the cements could be examined.

• Restorative Dentistry and Endodontics
• /
• 제18권1호
• /
• pp.197-204
• /
• 1993

This study was conducted to evaluate and compare the apical leakage in the following retrofilling techniques after apical resection; No apical cavity preparation and no retrofilling(control group), Amalgam(group I) or silver glass ionomer cement(group II) retrofilling after apical cavity preparation with mini contra-angle and bur, Amalgam(group III) or silver glass ionomer cement(group N) retrofilling after apical cavity preparation with ultrasonic micro endo tip. Extracted ninety upper anterior and lower canine teeth were fixed in skull simulators and root canals were prepared with step-back method and obturated with gutta-percha and zinc oxide eugenol sealer. Obturated roots were resected 2mm from apical ends and apical cavities of 1mm width and 2mm depth were prepared and retrofilled by above mentioned methods. After application of nail varnish on all surface except resected surface, apical 1/3 of the roots were placed in 1% methylene blue solution for 3 days. After longutudinal sectioning to expose central parts of filled materials, depths of penetrated dye were measured by measuring microscope and were analyzed statistically. The results were as follows. 1. Having no relation with instruments used in apical cavity preparation, amalgam retrofilling groups(group I and II) showed less apical leakage which was not significant statistically than no retrofilling group(control group) (P<0.05), but silver glass ionomer cement retrofilling gruoups(group II and IV) showed significantly less apical leakage than no retrofilling group(control group) (P<0.01). 2. In the groups retrofilled with the same material, the apical leakage in cavities prepared with ultrasonic micro endo tip (group III and IV) was less than that in cavities prepared with mini contra-angle and bur(group I and II), but not significant statistically(P>0.05). 3. When apical cavities were prepared with same instrument. the egroups retrofilled with silver glass ionomer cement(group II and IV) showed significantly less apical leakage than the groups retrofilled with amalgam(group I and III)(<0.01).

• 대한치과보철학회지
• /
• 제39권5호
• /
• pp.502-513
• /
• 2001

The purpose of this study was to evaluate the effect of dentin pretreatment with Dentin Conditioner, Ultra-Etch, conditioner of Fuji Plus cement on the shear bond strength of resin-reinforced glass ionomer cements to dentin and analyze the fractured surfaces. To evaluate the bond strength, the extracted human teeth which had uniform area of exposed dentin were cemented with conventional glass ionomer cement, 3M $RelyX^{TM}$ Luting (Vitremer luting cement), Fuji Plus cement after dentin pretreatment. The shear bond strength was measured using the Universal testing machine (Instron Co., USA) with a crosshead speed of 1mm/m. The effect of dentin pretreatment was evaluated by observing pretreated dentin surfaces under the scanning electron microscope, measuring the shear bond strength and observing the fractured surfaces under the scanning electron microscope. The results were as follows : On the SEM observation of surface morphology, the specimens treated with Dentin Conditioner. Ultra-Etch and conditioner of Fuji Plus cement were removed the smear layer and funneled dentinal tubules in dentin surfaces. In $RelyX^{TM}$ Luting cement group, shear bond strength of pretreated group was significantly higher than control group. In Fuji Plus cement group and Fuji I group, regardless of the type of pretreatment agents, there was tendency of increase in the shear bond strength. On the SEM observation of fractured surfaces, as the shear bond strength increase, it were shown thicker cement layers and were not shown dentinal tubules According to these results. it were shown that dentin pretreatment have much effect on bonding states.

• 대한치과보철학회지
• /
• 제38권5호
• /
• pp.618-630
• /
• 2000

As Fiber-reinforced composite restorations cannot be made without leaving a marginal gap, luting cements play a pivotal role in sealing the margins as a prevention against margnal leakage. A recently introduced adhesive resin cement system is claimed to adhere chemically, as well as mechanically, to tooth substances, dental alloys and porcelain. But when considering the clinical variation conventional cementation using Zinc Phosphate and Glass-Ionomer can be requested. A vitro study was undertaken to compare microleakage and marginal fitness of Fiber-reinforced composite crowns(Targis/Vectris) depending upon luting cements. Fifty non-carious human premolar teeth were randomly divided into five experimental groups of 10 teeth each and luted with five luting cements. ($Bistite\;II^(R),\;Super-bond^(R),\;Variolink\;II^(R)$), Zinc phosphate and Glass-Ionomer cement) After 24 hours of being luted, all specimens were thermocycled 300 times through water bath of $5^{\circ}C\;and\;55^{\circ}C$ in each bath, then the quality of the marginal fitness was measured by the Digital Microscope and marginal leakage was characterized using Dye Penetration technique and the Digital Microscope The results were as follows : 1. The mean values of marginal fit were Bistite II($46.78{\mu}m$), Variolink II($56.25{\mu}m$), Super-Bond($56.78{\mu}m$), Glass-Ionomer($99.21{\mu}m$), Zinc Phosphate($109.49{\mu}m$) indicated a statistically significant difference at p<0.001. 2. The mean microleakage values of tooth-cement interface, restoration-cement interface were increased in the order of Variolink II, Bistite II, Super-Bond, Glass-Ionomer, Zinc Phosphate 3. Crowns luted with resin cement (Bistite II, Super-Bond, Variolink II, etc) exhibited less marginal gap and marginal leakage than those luted with conventional Glass-Ionomer and Zinc Phosphate cement. 4. The results indicated that all five luting systems yielded comparable and acceptable marginal fit.

• Restorative Dentistry and Endodontics
• /
• 제17권2호
• /
• pp.307-330
• /
• 1992

The aim of this study was to investigate the physical properties of visible light curing Glass Ionomer cement for restorative esthetic filling. The control group was the autopolymerizing GC Fuji II Glass Ionomer cement (2.2: 1 P/L ratio) and the experimental groups were made by following procedure. To induce the polymerization by visible light, the powder of GC Fuji II GI cement and the liquid of Vitrabond for base & liner were mixed in an amalgam capsule with 2.5:1, 3.0:1, 3.5:1 P/L ratio (% wt/wt). After fabrication of specimens, compressive strength, fracture toughness ($K_{IC}$) Scanning Electron Microscope and X-ray Diffraction, water-leachable content, marginal leakage and surface roughness were studied. The results were as follows: 1. Only experimental No. 1 group (visible light curing) showed less compressive strength than control group 1 hour after curing. Strength was increased with aging in all groups, so the compressive strength of light curing groups was no less than that of autopolymerizing group after 3 weeks. 2. Experimental No.3 group (visible light curing) was inferior to No.2 group (visible light curing) in fracture resistance but light curing groups were more resistant to fracture than autopolymerizing group and showed ductile fracture pattern as compared with the brittle fracture pattern of autopolymerizing group. 3. From scanning electron microscopic image, various sized unreacted powder particles, surrounded by silica gel, were embedded in polysalt matrix. Light curing groups showed little crack and more dense unreacted particles than autopolymerizing group. 4. From X-ray diffraction analysis, GC Fuji II Glass Ionomer cement powder and all groups showed glassy appearance but light curing groups seemed to be more intensive in crystaline than autopolymerizing group. S. The most significant dissolution was shown in early setting period in all group. Light curing groups were dissolved less than autopolymerizing group. 6. Marginal leakage was not different significantly in case of cavity margin composed of same tooth structure (ex. only enamel margin, only dentin margin) but much more leakage was shown in dentin/cementum margin than enamel margin. In only case of only enamel margin, light curing groups were superior to autopolymerizing group. 7. All groups showed relatively smooth surface, which irregularity was less than $1{\mu}m$. Light curing groups were smoother than autopolymerizing group.

• Restorative Dentistry and Endodontics
• /
• 제13권1호
• /
• pp.69-78
• /
• 1988

The study was designed to establish a more nearly quantitative method for assessing the marginal leakage of dental restorations. 27 Class V cavities with $45^{\circ}$ bevel joint were prepared and classified into 2 groups. One group was filled with Scotchbond and silux. The other group was filled with glass ionomer cement, Scotchbond and silux. After finishing, all specimens were subjected manually to 100 thermal cycles at $0^{\circ}C$ and $100^{\circ}C$ water-bath. They were soaked in a samarium nitrate solution for 3 hours, irradiated with flux of $6{\times}10^{12}$ neutrons/$cm^2$/sec for 11 hours, cooled for 200 hours, counted with the HPGE detector and the tracer uptake was determined by comparison with a standard of samarium (10 ${\mu}g$). The following results were obtained. 1. Both of the two groups showed a considerable amounts of marginal leakage. 2. The group filled without glass ionomer cement base showed more marginal leakage than the group filled with glass ionomer cement base. 3. Neutron Activation Analysis produced a good quantitative method to measure the marginal leakage and samarium was appropriate to measure the marginal leakage of resin restorations using neutron activation analysis.

• Restorative Dentistry and Endodontics
• /
• 제10권1호
• /
• pp.103-114
• /
• 1984

The purpose of this study was to compare the polished surfaces of two composite resins (Clearfil F and Durafill) with those of glass ionomer cement (Fuji ionomer cement) and to observe what types of polishing devices are valuable, and then to establish a clinically satisfactory procedures. Studies have been undertaken to determine the effects of glass plate matrix and finishing instruments (Carborundum point, White point and Sof-Lex medium) on the surface finish of three restorative materials. The results were examined with profilometer (Kosaka laboratory LTD. Tokyo, Japan) and scanning electron microscopy (JSM-T20: JEOL). The results were as follows: 1. The most satisfactory surface finishes were produced against glass matrix. 2. Coarser finishes were obtained with use of carborundum point. 3. Generally Fuji ionomer cement were left surfaces with higher roughness values. 4. The smoothest finishes were obtained with Sof-lex medium. 5. Clearfil-F was showed more smoother than the other restorative materials.

• Restorative Dentistry and Endodontics
• /
• 제22권1호
• /
• pp.156-169
• /
• 1997

This study was designed to evaluate the influences of evaporation of liquid of dental cements by drying during long term using. Zinc phosphate cement, polycarboxylate cement, and glass ionomer cement were used, and evaluated the properties as follows; consistency, setting time, film thickness, solubility, and compressive strength according to the ADA specification. The specimens of control group were made by mixing the newly opened liquid using the powder-liquid ratio recommended by the manufacturer, and the specimens of ES groups were made by mixing the 10% evaporated liquid by drying with the powder-liquid ratio recommeded by the manufacturer, and the specimens of EM group were made by mixing the 10% evaporated liquid with the powder-liquid ratio modified for standard consistency. The following conclusions were drawn ; 1. The viscosity of mixture of all kinds of cements were increased by the evaporation of liquid, especially the viscosity of glass ionomer cement were influenced significantly. 2. The amount of liquid should be increased to get a standard consistency at the using of evaporated liquid of cement, the most significant increase of liquid amount was required on Ketac-Cem. 3. The setting times were increased at both cases of mixing of evaporated liquid with powder - liquid ratio recommended by manufacturer or modifided through consistency test. 4. At an experimental group of mixing of the evaporated liquid with powder-liquid ratio recommended by manufacturer, solubility was decreased and film thickness was increased. 5. By the result of evaporation of cement liquid, the compressive strength of polycarboxylate cement was increased slightly and it of glass ionomer cement was increased, however, by the increase of amount of liquid to be possible to manipulate the compressive strength were decreased.

• The Journal of Advanced Prosthodontics
• /
• 제7권6호
• /
• pp.475-483
• /
• 2015

PURPOSE. The objective of this study was to evaluate the influence of various cement types on the stress distribution in monolithic zirconia crowns under maximum bite force using the finite element analysis. MATERIALS AND METHODS. The models of the prepared #46 crown (deep chamfer margin) were scanned and solid models composed of the monolithic zirconia crown, cement layer, and prepared tooth were produced using the computer-aided design technology and were subsequently translated into 3-dimensional finite element models. Four models were prepared according to different cement types (zinc phosphate, polycarboxylate, glass ionomer, and resin). A load of 700 N was applied vertically on the crowns (8 loading points). Maximum principal stress was determined. RESULTS. Zinc phosphate cement had a greater stress concentration in the cement layer, while polycarboxylate cement had a greater stress concentration on the distal surface of the monolithic zirconia crown and abutment tooth. Resin cement and glass ionomer cement showed similar patterns, but resin cement showed a lower stress distribution on the lingual and mesial surface of the cement layer. CONCLUSION. The test results indicate that the use of different luting agents that have various elastic moduli has an impact on the stress distribution of the monolithic zirconia crowns, cement layers, and abutment tooth. Resin cement is recommended for the luting agent of the monolithic zirconia crowns.

• Restorative Dentistry and Endodontics
• /
• 제22권2호
• /
• pp.596-608
• /
• 1997

The purpose of this study was to compare the apical leakage and adaptation to the dentinal wall of a glass ionomer root canal cement(Ketac-Endo) with those of AH-26 and Tubli-Seal. 102 single-rooted teeth were insrumented with step-back technique and randomly divided into four groups according to kinds of root canal cements: Ketac-Endo, AH-26, Tubli-Seal, and no root canal cement. Four experimental groups were as follows; Group 1 : Filling with gutta-percha and Ketac-Endo Group 2 : Filling with gutta-percha and AH-26 Group 3 : Filling with gutta-percha and Tubli-Seal Group 4 : Filling with gutta-percha without root canal cement All the specimens were obturated with lateral condensation technique, and stored in 100% humidity for 4 days. 20 teeth in each group were placed in centrifuge tube filled with India ink, and then centrifuged for 20 minutes at 3,000 rpm. And they were evaluated for linear dye leakage using a stereoscope and analyzed by one-way ANOVA. 22 teeth were split longitudinally and evaluated the adaptation to the dentinal wall using scanning electron microscope(4 teeth in each group) and stereoscope(2 teeth in 1, 2, 3 group). The obtained results were as follows ; 1. In case of not used root canal cement(Group 4), there was showed much degree of dye penetration comparerd with used root canal cements (Group 1, 2, 3)(P<0.01). 2. In the case of used root canal cements(Group 1, 2, 3), there was no significant difference in linear leakage in groups(P>0.01). 3. In the case of used root canal cements(Group 1, 2, 3), there was showed intimate adaptation to the dentinal wall independent on kinds of root canal cements. 4. Fractured surfaces indicated failure of cohesion in Ketac-Endo, and failure of adhesion to dentine in AH-26 and Tubli-Seal. 5. According to similar apical leakage and adaptability to the dentinal wall to another root canal cements, it is possible to be used glass-ionomer cement as root canal cement.