• 한국재료학회지
• /
• 제34권2호
• /
• pp.79-84
• /
• 2024

Thin films of yttria-stabilized zirconia (YSZ) nanoparticles were prepared using a low-temperature deposition and crystallization process involving successive ionic layer adsorption and reaction (SILAR) or SILAR-Air spray Plus (SILAR-A+) methods, coupled with hydrothermal (175 ℃) and furnace (500 ℃) post-annealing. The annealed YSZ films resulted in crystalline products, and their phases of monoclinic, tetragonal, and cubic were categorized through X-ray diffraction analysis. The morphologies of the as-prepared films, fabricated by SILAR and SILAR-A+ processes, including hydrothermal dehydration and annealing, were characterized by the degree of surface cracking using scanning electron microscopy images. Additionally, the thicknesses of the YSZ thin films were compared by removing diffusion layers such as spectator anions and water accumulated during the air spray plus process. Crack-free YSZ thin films were successfully fabricated on glass substrates using the SILAR-A+ method, followed by hydrothermal and furnace annealing, making them suitable for application in solid oxide fuel cells.

• 한국결정성장학회지
• /
• 제16권5호
• /
• pp.227-234
• /
• 2006

제강분진(EAF dust, 이하 더스트)이 첨가된 규산염계 유리 프리트를 용융하여 유리 시편을 제조하고, 이를 열처리하여 결정화 시킨 후 표면 및 내부의 미세구조를 관찰하였다. 제조된 유리의 DTA 분석결과 결정화온도($T_c$)는 $850^{\circ}C$ 부근이었으며 이로부터 열처리 온도를 $950^{\circ}C$로 정하였다. XRD 분석결과 더스트가 50wt% 들어간 유리시편은 비정질 상태였으나 70wt% 들어간 유리시편은 spinel 결정상이 나타났다. 결정화유리시편은 spinel 및 willemite 결정상이 함께 나타나며 더스트의 첨가량이 증가할수록 willemite 결정상이 증가하였다. 더스트의 함유량이 50wt%인 유리시편의 경우 연마된 절단면이 거울 표면같이 매끄러운 상태였으나 70wt% 첨가된 경우에는 유리질의 모상(glass matrix)내에 최대 10mm 크기의 spinel 결정상이 존재하였다. 결정화유리시편의 경우에는 자유표면에 $2{\sim}5{\mu}m$ 크기의 ZnO 결정입자들이 생성되었고, 내부에는 유리상, spinel 그리고 willemite 결정상이 혼재하였다. 더스트가 50wt% 첨가된 유리는 결정입자가 존재하지 않았으나 70wt% 첨가된 유리시편에는 14%의 결정이 존재하였다. 더스트가 50 및 70wt% 첨가된 결정화유리시편의 결정화도는 각각 19 및 43% 이었다. 결정화 전후 시편들을 TCLP 용액에 18시간 담근 후 SEM을 통하여 미세구조를 관찰했을 때 유리시편에는 균열이 발생하였으나, 결정화유리시편의 경우 침식흔적은 나타났으나 균열은 존재하지 않았다.

• 한국건설순환자원학회논문집
• /
• 제4권2호
• /
• pp.136-142
• /
• 2016

전 세계적으로 급격한 산업화 및 현대화가 진행됨에 따라 환경오염 또한 급격히 진행되어가고 있다. 그리고 천연골재의 무분별한 채취로 환경오염 및 분진발생 등은 심각한 문제가 되고 있다. 이에 본 연구는 시멘트 생산 시 $CO_2$ 배출량을 줄이고자 시멘트 대체재로서 산업부산물인 고로슬래그와 유동층 연소 플라이애시를 사용하고자 하였으며, 천연골재의 무분별한 채취 문제를 해결하고자 골재로서 폐자기 및 폐유리를 활용하는 인조석재에 적용하는 산업부산물 및 폐자원을 활용한 내 외장재 인조석재의 특성에 대한 기초자료를 제시하고자 하였다. 그 결과, 고로슬래그를 주 결합재로 하여 유동층 연소 플라이애시를 40% 첨가하였을 때 가장 강도가 높았으며 또한, 선행실험을 토대로 폐자기 및 폐유리의 혼입율에 따른 실험을 진행 한 결과, 폐자기 및 폐유리의 적정 혼입율은 출석률이 45% 이상 보이는 혼입율 60, 70(%)의 혼입율이 가장 적정 혼입율이라고 판단된다.

• 한국결정성장학회지
• /
• 제8권1호
• /
• pp.169-178
• /
• 1998

CaO-$SiO_2-P_2O_5$ 3성분계 유리화 영역(glass forning region)내의 여러조성(A:$SiO_2$- rich조성, B:CaO-rich조성, C:$P_2O_5$-rich조성, D, E:A, B, C의 중간조성)을 가지는 유리분말을 결정화시켰을 때 유리중에 석출되는 결정상(crystal phase)을 분말 XRD로 확인하였다. 여러조성중 apatite(($Ca_{10}(PO_4)_6O$)와 $\beta$-wollastonite($CaSiO_3$)결정이 석출되고, 굽힘강도가 우수한 E조성(CaO 49.4, $SiO_2\;36.8,\;P_2O_5$8.8wt%)을 선택하여 이 조성의 유리분말을 일방향으로 결정화 소결하였다. 제조된 결정화 소결체에 대하여 charaterization을 하고 굽힘강도를 측정하였다. 또한 결정화 소결체와 생체뼈와의 결합성을 조사하기 위하여 유사체액(simulated body fluid)내에서 침적실험을 하였으며, 결정화 소결체의 표면을 thin-film XRD, FT-IR로 분석하였다. 실험결과, apatite와 wollastonite 결정이 석출된 치밀한 결정화 소결체가 얻어졌으며, 이들 결정은 wollastonite 결정의 (202)면이 인상방향에 수직으로 성장하는 경향을 보였다. 또한 제조된 결정화 소결체는 평균 186.9MPa의 굽힘강도를 나타내어 일반적 방법으로 제조되는 결정화 소결체보다 높은 역학적 성질을 보였다. 유사체액내의 침적실험결과, 시료표면위에 apatite 결정층이 3일후부터 형성되어 생체뼈와 화학결합을 이룰 가능성이 있음을 알았다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 봄 학술발표회 논문집
• /
• pp.391-396
• /
• 2001

Exposed concrete execution is utilized insufficiently due to surface honecomb and undesirable appearance by entrapped air when existing placing method is applied. Therefore, surface glossing and impact properties of cement mortar incorporating fiber glass net blast furnace slag, expansive admixture and Polypropylene fiber are investigated in order to develop precast exposed concrete pannel by dry construction method. The kinds of the forms, placing method and admixture contents are varied. According to test results, surface glossing decrease with elapse of age. Considering the form kinds, surface glossing with acryle + astage shows the best performance. Placing horizontally shows positive results in reducing surface defects such as honecomb. Impacting resistance shows the best performance when glass fiber net applied, due to the enhance in toughness and absorption of impact.

• 한국세라믹학회지
• /
• 제34권9호
• /
• pp.935-940
• /
• 1997

This study investigated the crystallization behavior in PbO-ZnO-B2O3-TiO2 system sealing glass, inorganic polymer heat-treated by conventional heat and microwave energy. After determining heat-treated temperature for crystallization and characteristic points by DTA analysis, samples were heat-treated in a classical electric furnace and a home-style microwave oven (LG Electronic Co., 2.45 GHz, 700 W). A microwave heat-treated sample had the growth of PbTiO3 crystal at 45$0^{\circ}C$, 2$0^{\circ}C$ lower than that of a conventionally heat-treated sample. Also, it had crystallinity about 20% higher than the conventionally heat-treated sample. At 49$0^{\circ}C$, the size of PbTiO3 crystal in the conventionally heat-treated sample was larger than that in the microwave heat-treated sample due to longer heat-treated time.

• 마이크로전자및패키징학회지
• /
• 제6권4호
• /
• pp.35-39
• /
• 1999

The $Li_2O-MgO-MgF_2-SiO_2$glasses with addition of $B_2O_3$ were investigated in order to make glass-ceramics for low temperature firing substrate. Glasses were made by melting at $1450^{\circ}C$ in the electronic furnace and crystallized at $750^{\circ}C$. The crystal phases were polycrystalline of lithium boron fluorphlogopite and lithium fluorhectorite. The crystal shape was chanced to granule type from needle type with increasing $B_2O_3$ content. Average particle size of the glass-ceramics after water swelling was 3.77$\mu\textrm{m}$. The optimum sintering temperature and sintering shrinkage of the substrate were $900^{\circ}C$ and 13.4%, respectively.

• 한국산학기술학회:학술대회논문집
• /
• 한국산학기술학회 2002년도 춘계학술발표논문집
• /
• pp.70-73
• /
• 2002

도가니로를 사용하여 유리제품을 생산하고있는 중소 유리제조업체인 D.H사의 제품내 발생한 결함을 분석하였다. 제품내 결함으로는 기포, 코드(cord), 석물(stone)이 발생하고 있었으며, 광학현미경, EDS 등의 분석장비를 통해 제품내 결함을 분석한 결과 코드는 석물에 의해 발생하고 있음을 확인하였다. 석물의 EDS 분석결과 주요성분은 Si로 나타났으며, 이는 도가니의 장기간 사용시 도가니 내벽과 유리물의 반응에 의한 도가니의 용융침식에 의해 발생한 한가지 결점원에 의한 한가지 결정상으로 SiO₂의 고온결정상인 cristobalite임을 확인할 수 있었다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2006년도 6th International Meeting on Information Display
• /
• pp.946-948
• /
• 2006

It is important to keep a constant transmittance of dielectric during firing. To control the shrinkage and fusion stage of frits in firing, we used a hot stage microscope (HSM) to analyze the thermal properties of the lead and bismate glass frits by the in-situ method. This research would be useful for improving the reliability of transmittance of dielectric during firing in industry using a large furnace with temperature deviation.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2002년도 하계학술대회 논문집 D
• /
• pp.2507-2509
• /
• 2002

본 논문에서는 유리 용해로의 온도 제어를 위한 동역학 행렬 제어 (Dynamic Matrix Control, DMC) 기법의 적용 사례를 소개한다. 다양한 제약조건들과 긴 시간지연 응답을 갖는 유리 용해로는 DMC외 좋은 적용 분야가 될 수 있다. 먼저 용해로 테스트를 통하여 입출력 데이터를 생성하고 이를 바탕으로 용해로의 동역학 행렬 모델을 결정한다. 그 후, 모의 실험을 통하여 제어기의 설계변수들을 결정한다. 마지막으로, 제시된 제어기를 실제 용해로 생산 공정에 적용된 결과를 제시한다.